Abstract: A fluoroelastomer polymer foam having a compression set value in the range of from about 8.3% to about 43% and closed cell microvoids having diameters of from about 0.002 mm to about 0.048 mm or less, and a method for foaming a fluoroelastomer polymer comprising the steps of dispersing in a fluoroelastomer polymer to be foamed a phenol-based blowing agent to produce a foaming formulation and curing the formulation at a temperature of from about 250.degree. F. (121.degree. C.) to about 450.degree. F. (232.degree. C.) and a pressure of from about ambient to about 3.0 atm.