Abstract: A polyamide comprising a unit containing at least one (a) alicyclic dicarboxylic acid and a unit containing a (b) diamine having 8 or more carbon atoms, wherein the polyamide satisfies the following conditions (1) and (2): (1) a sulfuric acid relative viscosity ?r at 25° C. is 2.3 or more; and (2) Mw (weight average molecular weight)/Mn (number average molecular weight) is 4.0 or less.
Abstract: The present invention provides a production process of a heat shrinkable film which is transparent, excellent in the balance of physical properties such as rigidity, elongation and shrink properties in both MD and TD, especially has a uniform film thickness and good stability in extrusion molding film while utilizing an inflation method; a block copolymer or hydrogenated product thereof, or a composition composed thereof excellent in tensile properties, optical properties, hardness, stretch properties, molding processability, shrink properties and solvent resistance and therefore suited for extrusion, injection molding and foams. The production process of a heat shrinkable film has a first inflation step of forming a tube having a thickness of from 0.05 to 0.5 mm by using a block copolymer having a vinyl aromatic hydrocarbon content of from 65 to 95 wt. % and a conjugated diene content of from 5 to 35 wt.
Abstract: It is an object to provide a block copolymer composition for a viscous adhesive, which will be a viscous adhesive composition excellent in balance of the adhesive properties such as tack strength and tackiness, having a low melt viscosity, and excellent solubility, coating properties, ejection stability, and surface skin quality. The block copolymer composition for a viscous adhesive having: a component (a) in an amount of 50 mass % or more and 90 mass % or less; and a component (b) in an amount of 10 mass % or more and 50 mass % or less; a content of the vinyl aromatic monomer unit being 25 to 50 mass %; a viscosity of the 15 mass % toluene solution being 10 to 40 mPa·s; and a number average molecular weight ratio of the component (b) to the component (a) being 2.0 to 4.0.
Type:
Application
Filed:
July 18, 2013
Publication date:
June 25, 2015
Applicants:
Asahi Kasei Chemicals Corporation, Japan Elastomer Co., Ltd.
Abstract: Provided are composite particles which exhibit excellent fluidity and high liquid retentivity and which exhibit high fluidity even in a liquid-holding sate. Also provided are composite particles which permit direct compressing in an open feed manner and which suffer from little compressing trouble and exhibit high shapability. When shaped together with an active ingredient, the composite particles provide shaped bodies which have uniform weight, uniform active ingredient content, and high hardness and which suffer from less galling.
Abstract: An object of the present invention is to provide an isocyanate production process, which is free of the various problems found in the prior art, and which uses a composition containing a carbamic acid ester and an aromatic hydroxy compound when producing isocyanate without using phosgene, as well as a carbamic acid ester composition for transferring or storing carbamic acid ester. The present invention discloses an isocyanate production process including specific steps and using a composition containing a carbamic acid ester and an aromatic hydroxy compound, as well as a composition for transfer or storage of carbamic acid ester comprising the carbamic acid ester and the specific aromatic hydroxy compound.
Abstract: A method for preparing a ruthenium catalyst, including a step of reducing a ruthenium catalyst precursor by holding the ruthenium catalyst precursor in an aqueous solution containing a metal salt at a temperature within the range of more than 180° C. and 220° C. or less and a hydrogen partial pressure within the range of 0.6 MPa or more and 5 MPa or less. A method for producing a cycloolefin, including a step of preparing a ruthenium catalyst by the method including a step of reducing a ruthenium catalyst precursor in an aqueous solution containing a metal salt by holding the ruthenium catalyst precursor at a temperature within the range of more than 180° C. and 220° C. or less and a hydrogen partial pressure within the range of 0.6 MPa or more and 5 MPa or less, and a step of partially hydrogenating a monocyclic aromatic hydrocarbon by use of the ruthenium catalyst obtained.
Abstract: Provided is a method for producing an episulfide compound, the method including a step of thiating epoxy groups of (B) an epoxy compound by a reaction with (C) a thiating agent in the presence of (A) a polyhydric hydroxyl compound having two or more hydroxyl groups.
Abstract: A method for converting an olefin or an alcohol has a pretreatment step of obtaining a conductive catalyst by a pretreatment for suppressing electrostatic charging of a non-conductive catalyst and a step of converting an olefin or an alcohol by a fluidized bed reaction using the conductive catalyst.
Abstract: This cellulose powder has: an average degree of polymerization of 100 to 350; a weight average particle size of over 30 ?m, but less than 250 gm; an apparent specific volume of 2 to less than 15 cm3/g; and a particle size distribution sharpness of 1.5 to 2.9.
Abstract: Disclosed is a solid preparation which comprises at least one active ingredient and at least one dissolution-controlling base substance and can be formed by compression molding, wherein the dissolution-controlling base substance contains 5.0 to 99.9% by weight (inclusive) of a modified starch having a moisture retaining capacity of 400% or more and a gel indentation load of 200 g or more, containing a water-soluble ingredient in an amount of 40 to 95% by weight, having particles passing through a 75 ?m-mesh sieve in the proportion of 90% by weight or more and particles passing through a 32 ?m-mesh sieve in the proportion of 20% by weight or more, and having an average particle diameter of not smaller than 20 ?m and smaller than 50 ?m.
Abstract: An object of the present invention is to provide a method for production of a high purity conjugated diolefin. The method for production of a conjugated diolefin of the present invention comprises steps of supplying a source gas containing a C4 or higher monoolefin and an oxygen-containing gas into a reactor, bringing a catalyst into contact with the gas mixture, compressing a gas containing a conjugated diolefin produced by an oxidative dehydrogenation reaction to obtain a liquefied gas and rinsing the liquefied gas with water.
Abstract: [Problem to be Solved] To provide a polyamide having a high melting point, which has excellent strength, toughness, and stability under heating. [Solution] This polyamide is obtained by polymerizing an (a) dicarboxylic acid comprising at least 50 mol % of an alicyclic dicarboxylic acid and a (b) diamine comprising at least 50 mol % of a diamine having a pentamethylenediamine skeleton, wherein the polyamide has a cyclic amino end amount of 30 to 60? equivalents/g.
Abstract: An object of the present invention is to provide a metal pigment composition having the characteristics that aging stability is excellent, reductions of brightness, masking and flip flop appearance are little, and storage stability is excellent. The present invention is directed to a metal pigment composition containing a metal pigment treated with at least one of organic molybdenum compounds, or a metal pigment composition containing a metal pigment treated with at least one of organic molybdenum compounds, and at least one agent selected from the groups consisting of an anti-oxidizing agent, an anti-reducing agent and a photostabilizer.
Abstract: This cellulose powder has: an average degree of polymerization of 100 to 350; a weight average particle size of over 30 gm, but less than 250 ?m; an apparent specific volume of 2 to less than 15 cm3/g; and an organic carbon content from residual impurities, which is defined by the total organic carbon content (%) during 1% NaOH extraction to the total organic carbon content (%) during pure water extraction, of over 0.07 to 0.3%.
Abstract: The present invention is related to a method for producing a polymer to efficiently remove metal residues of at least lithium and/or titanium from a polymer solution comprising the at least lithium and/or titanium to thereby obtain a refined polymer solution having little metal residue.
Abstract: A coating film comprising ethyl cellulose as a component A and an (ethyl acrylate)-(methyl methacrylate) copolymer or a plasticized vinyl acetate polymer as a component B, and having a tensile elongation of 150% or more and a tensile strength of 9 N or more.
Abstract: A method for producing a silica-supported catalyst comprising Mo, V. Nb, and a component X (Sb and/or Te) to be used in a vapor phase catalytic oxidation or ammoxidation of proprane, comprising the steps of: (I) preparing a raw material mixture solution by mixing Mo, V, Nb, component X, a silica sol, and water; (II) obtaining a dry powder by drying the raw material mixture solution; and (III) obtaining a silica-supported catalyst by calcining the dry powder, wherein the silica sol contains 10 to 270 wt ppm of nitrate ions based on SiO2.
Abstract: A cover tape having a temperature at which a heat shrinkage rate in at least one of a machine direction and a transverse direction perpendicular to the machine direction is 5% or more between 80° C. to 200° C.
Abstract: The present invention provides a zeolite-containing catalyst having excellent shape, fluidity and mechanical strength as a catalyst for a fluidized bed reaction. The present invention provides a zeolite-containing catalyst which is a particulate catalyst containing zeolite and silica, wherein the catalyst has an average particle diameter of 20 to 300 ?m and the ratio of the void area in the cross-section of the particle is 30% or less relative to the cross-section area of the particle.
Abstract: The present invention provides a glass fiber-reinforced thermoplastic resin composition in which a particular relationship is satisfied between the glass fiber content (W (parts by weight)) and the melt viscosity (?) of the thermoplastic resin composition at molding temperature as determined at a shear rate of 1,000 sec?1. According to the present invention, there can be obtained a glass fiber-reinforced thermoplastic resin having increased strength and rigidity and excellent in practical characteristics such as impact resistance and antifreeze liquid resistance. In addition, molded articles obtained by injection-molding the composition are available as components having reduced anisotropies of mechanical characteristics and mold shrinkage factor.