Abstract: Purposes of the present invention are to provide a dry coated sand having a high degree of fluidity at the room temperature, a method of advantageously producing the coated sand, and a method of producing a casting mold having excellent properties, by using the coated sand. The dry coated sand is obtained by mixing an aqueous solution of a water glass used as a binder, with a heated refractory aggregate, whereby water in the aqueous solution is evaporated, and a coating layer of the binder is formed on surfaces of the refractory aggregate. A moisture percentage in the thus obtained dry coated sand is controlled so as to be not more than 0.5% by mass. The intended casting mold is obtained by filling a molding cavity of a forming mold, with the dry coated sand, and passing a steam through the coated sand, to solidify or cure the coated sand.

Abstract: Provided are an organic binder for a mold, which can advantageously extend the pot life without causing uneven curing, reduction in mold strength and an increase in the amount of use of a catalyst; a molding sand composition which is obtained by using the organic binder for a mold, and which exhibits an extended pot life; and a mold produced by curing such a molding sand composition through gas hardening. The urethane-curable type organic binder for a mold, which is used for production of a urethane-based mold, is constituted by comprising a specific alkoxysilyl group-containing ketimine compound, together with a polyol compound and a polyisocyanate compound.