Abstract: A method is provided for manufacturing spherical corundum grains having a bulk density between 1.5 kg/L and 2.5 kg/L, with aluminum oxide being melted in an electric arc furnace with the addition of 0.1 to 1% quartz sand, the melt being poured in a pouring quantity of less than 100 kg/min, and the pouring stream being blown using compressed air at a pressure between 3 to 10 bar.

Abstract: The present invention relates to sintered abrasive grit agglomerates based on aluminum oxide, having homogeneously distributed nanoscale pores in the range of 100-300 nm, with a pore volume of at least 15%. The average diameter of primary particles of the aluminum oxide primary particles is less than 5 ?m, wherein said primary particles are connected to each other without additional adhesive agent.

Abstract: The invention relates to a wear protection layer comprising a mixture of non-uniform transparent hard material particles, which are stored in a matrix material and which comprise a Mohs hardness of at least 6 and transparent solid material particles, wherein the transparent solid material particles encompass a bi-modal grain size distribution. The invention also relates to a method for producing a wear protection layer as well as the use thereof for producing wear protection surfaces, in particular surfaces on wood fiber boards, which are provided with a décor.

Abstract: The invention relates to an anti-abrasion layer, comprising a mixture of irregular particles of hard material and round particles essentially free of cutting edges embedded in a matrix material and the use thereof for the production of anti-abrasion surfaces on wood materials, decorative paper, or wood fibre sheets printed with patterns for the production of parquet floors, floor laminates, furniture surfaces or work boards and for the production of wear-resistant surface layers on support materials made from metal, glass, ceramics, plastic concrete or other materials.

Abstract: A method is provided for manufacturing spherical corundum grains having a bulk density between 1.5 kg/L and 2.5 kg/L, with aluminum oxide being melted in an electric arc furnace with the addition of 0.1 to 1% quartz sand, the melt being poured in a pouring quantity of less than 100 kg/min, and the pouring stream being blown using compressed air at a pressure between 3 to 10 bar.