Abstract: A method for directly preparing a foamed polylactic acid (PLA) product from a PLA melt includes PLA melt preparation, feeding, and two-stage extrusion. In the two-stage extrusion, a pressure at an outlet of a first-stage twin-screw extruder is 15 MPa to 17 MPa, a PLA melt is fed at a rate of 250 kg/h, a foaming additive is fed at a rate of 7.5 kg/h to 10 kg/h, and a foaming gas is fed at a rate of 2.8 L/h to 7.5 L/h. The method can ensure both foamability and quality of a material and reduce more than ? of energy consumption; and an obtained product has an adjustable foaming rate of 3 to 25, a crystallinity of 40.3% to 48.5%, a tensile strength of 8.7 MPa to 19.6 MPa, and an apparent density of 0.05 g/cm3 to 0.4 g/cm3.

Abstract: A preparation method of a high-rate foamed polylactic acid (PLA) sheet includes first-stage extrusion, second-stage extrusion, and foamed sheet extrusion. The method requires the following raw materials in parts by mass: 88 to 94 parts of PLA, 1 to 2 parts of a nucleating agent, 2 to 5 parts of a foaming agent, and 2 to 5 parts of an additive. The new method effectively solves the problems of low foaming rate, low strength, and the like in the industrial production using carbon dioxide, and a prepared PLA sheet with high foaming rate and excellent surface performance can be used in the fields of food packaging, disposable fully-degradable lunch boxes, and the like.