Abstract: This invention relates to an aqueous solution and a method for preparing an organic protective coating on a Cr(lll) conversion layer which is localized on (anodized) aluminium (alloy) to enhance corrosion protection. The composition is an aqueous solution which contains water, an organic film forming agent and a corrosion inhibitor, wherein the corrosion inhibitor comprises or consists of at least one 2-arylriazole. According to the method of the present invention, the composition is used for post-treating of a Cr(lll) conversion layer on (anodized) aluminium (alloy). The invention further provides a modified Cr(III) conversion coating on (anodized) aluminium (alloy), which is producible or produced with the inventive method. The modified Cr(III) conversion coating according to the invention shows excellent corrosion protection, paint adhesion and electrical resistivity.
Abstract: The present invention provides a suspension and method for improving the corrosion protection of substrates which comprise or consist of steel. It has been discovered that if an organic derivative of a bentonite clay and a modified urea are added to a dispersion of flakes of Zn, Al and/or Mg, or alloys thereof, the resulting suspension demonstrates a rheological profile which is ideally suited for coating steel substrates. In fact, the inventive suspension enables coating with a high consistency of performance. The performance of the suspension is already reached after one coating process i.e. even after a dip/spin coating process is conducted only one once. In conclusion, steel substrates can be provided with a high-quality corrosion resistant coating in a more economical way compared to the prior art.
Type:
Application
Filed:
April 16, 2014
Publication date:
February 25, 2016
Applicants:
EWH INDUSTRIEANLAGEN GMBH & CO. KG, COVENTYA SAS
Abstract: The present invention relates to an electroplating bath for zinc-iron alloys as an anti-corrosive layer and to a method for depositing zinc-iron alloy on a device. The invention also relates to a device which comprises an anti-corrosive layer of a zinc-iron alloy and the use of mentioned electroplating bath.
Abstract: This invention relates to a composition and a method for preparing an organic protective coating on a Cr(lll) conversion layer which is localized on aluminium or an aluminium alloy to enhance corrosion protection. The composition is an alkaline aqueous solution which contains at least one corrosion inhibitor, a buffering agent and at least one organic film former. According to the method of the present invention, the composition is used for post-treating of a Cr(lll) conversion layer on aluminium or an aluminium alloy and on anodized aluminium or an anodized aluminium alloy.