Abstract: Provided by the present invention is a method for simultaneously dyeing and flame-retardant finishing a polyester-based fiber product, which is excellent regarding dyeing reproducibility, the method including immersing and heating a polyester-based fiber product in a processing bath containing a specific yellow disperse dye and a phosphoramidate represented by Formula (V):
Abstract: The invention provides a flame retardant for a polyester based synthetic fiber structure comprising aminopentaphenoxycyclotriphosphazene, and a flame retardant treatment agent for a polyester based synthetic fiber structure comprising the flame retardant dispersed in a solvent in the presence of a surfactant.
Type:
Application
Filed:
June 16, 2018
Publication date:
April 16, 2020
Applicants:
DAIKYO CHEMICAL CO., LTD., FUSHIMI PHARMACEUTICAL CO., LTD.
Inventors:
Terufumu IWAKI, Shigeto KOYAMA, Yuji TADA
Abstract: A flame-retardant metal-coated cloth having a high degree of flame retardancy and a soft feeling without the use of any halogen compound or antimony compound is provided. In the flame-retardant metal-coated cloth, a flame-retardant film comprising a mixture (E) of a phosphorus compound (A), a metal hydroxide (B), a phosphoric ester (C), and a thermoplastic resin (D), is formed on at least one surface of a metal-coated cloth, and the ratio of (A):(B):(C):(D) is 20 to 200:100 to 950:10 to 250:100 in terms of a weight ratio.
Type:
Grant
Filed:
January 14, 2005
Date of Patent:
October 25, 2011
Assignees:
Daikyo Chemical Co., Ltd., Seiren Co., Ltd.
Abstract: It is intended to provide a novel artificial sueded leather having flame retardance, which is excellent inflame retardance, light resistance and abrasion resistance, suffers from no water spot and is free from any halogenated chemical (i.e., one having been treated with a so-called non-halogenated flame retardant), and a method of producing the same. The above artificial sueded leather comprises a thermoplastic synthetic fiber cloth made of a woven fabric, a knitted web or a nonwoven fabric, which has a raised-fiber or napped-fiber surface and has been impregnated with a polyurethane resin, and a flame retardant which contains at least a phosphate compound A having a solubility in water of 1% or less, a vinyl group-containing resin C capable of forming a carbonization skeleton in burning and a water-insoluble thickener D and is imparted to one face of the thermoplastic synthetic fiber cloth.
Type:
Application
Filed:
July 7, 2006
Publication date:
October 15, 2009
Applicants:
Daikyo Chemical Co., LTD.,, Toray Industries, Inc.,
Abstract: The invention provides a flame-retardant processing agent capable of imparting durable flame retardance to polyester-based fiber products without using halogen-based flame retardant. The flame-retardant processing agent is obtained by dispersing at least one phosphoric acid amide selected from the group consisting of 1,4-piperazinediyl bis(diarylphosphate), diaryl aminophosphate and aryl diaminophosphate as a flame retardant in a solvent in the presence of a nonionic surfactant or an anionic surfactant.
Abstract: The invention provides a flame-retardant processing agent capable of imparting durable flame retardance to polyester-based fiber products without using halogen-based flame retardant. The flame-retardant processing agent is obtained by dispersing at least one phosphoric acid amide selected from the group consisting of 1,4-piperazinediyl bis(diarylphosphate), diaryl aminophosphate and aryl diaminophosphate as a flame retardant in a solvent in the presence of a nonionic surfactant or an anionic surfactant.