Abstract: The present invention provides a composition for use in forming an abrasion-resistant easy-to-clean coating on a substrate. The composition according to the invention includes a mixture of a fluorocarbon polymer component and an enamel-forming component. The enamel-forming component includes at least a first lead-free and cadmium-free glass frit. The first lead-free and cadmium-free glass frit includes from about 30% to about 50% P2O5, from about 15% to about 30% Al2O3, and from about 2% to about 40% X2O where X=Na and/or K. The present invention also provides a method of forming an abrasion-resistant easy-to-clean coating on a substrate. The method includes applying the composition according to the invention to a substrate and sintering the applied composition to fuse an abrasion-resistant easy-to-clean coating to the substrate.

Abstract: The present invention provides a composition for use in forming an enamel cover coat from which baked-on foods can be removed without the need for pyrolysis or highly alkaline cleaners. The enamel cover coat preferably exhibits no chipping or other surface defects subsequent to a 2.0 mm Plum Jam Test and an acid resistance of A or better according to ISO 2722. The composition according to the invention includes a glass component including at least a first glass frit comprising a low SiO2 glass frit. Preferably, the glass component includes a blend of the first glass frit and at least a second glass frit. Preferably, the first glass frit includes by weight from about 30% to about 45% P2O5, from about 20% to about 40% Al2O3, from about 15% to about 35% Li2O+Na2O+K2O, up to about 15% B2O3, up to about 15% MgO+CaO+SrO+BaO+ZnO, up to about 10% TiO2+ZrO2, and up to about 10% SiO2.

Abstract: The present invention provides a composition for use in forming an abrasion-resistant easy-to-clean coating on a substrate. The composition according to the invention includes a mixture of a fluorocarbon polymer component and an enamel-forming component. The enamel-forming component includes at least a first lead-free and cadmium-free glass frit. The first lead-free and cadmium-free glass frit includes from about 30% to about 50% P2O5, from about 15% to about 30% Al2O3, and from about 2% to about 40% X2O where X=Na and/or K. The present invention also provides a method of forming an abrasion-resistant easy-to-clean coating on a substrate. The method includes applying the composition according to the invention to a substrate and sintering the applied composition to fuse an abrasion-resistant easy-to-clean coating to the substrate.

Abstract: The present invention provides a composition for use in forming an abrasion-resistant easy-to-clean coating on a substrate. The composition according to the invention includes a mixture of a fluorocarbon polymer component and an enamel-forming component. The enamel-forming component includes at least a first lead-free and cadmium-free glass frit. The first lead-free and cadmium-free glass frit includes from about 30% to about 50% P2O5, from about 15% to about 30% Al2O3, and from about 2% to about 40% X2O where X=Na and/or K. The present invention also provides a method of forming an abrasion-resistant easy-to-clean coating on a substrate. The method includes applying the composition according to the invention to a substrate and sintering the applied composition to fuse an abrasion-resistant easy-to-clean coating to the substrate.

Abstract: The present invention provides a composition for use in forming a white porcelain enamel coating on aluminized or galvanized steel. The composition according to the present invention includes a solids portion including a glass component and a white pigment. The glass component includes one or more glass frits including by weight from about 30% to 50% P2O5, from about 15% to about 30% Al2O3, from about 8% to about 40% X2O where X=Na and/or K, up to about 30% TiO2, up to about 12% B2O3, up to about 10% K2O, up to about 10% ZnO, up to about 8% SiO2, up to about 7% La2O3, up to about 5% Li2O, and up to about 15% F. The white pigment include TiO2.

Abstract: The present invention provides a composition for use in forming an opaque porcelain enamel coating on a metal substrate. A porcelain enamel coating formed using a composition according to the invention readily adheres to metal substrates such as, for example, steel, that are degreased-only. Furthermore, such a porcelain enamel coating displays an acid resistance of A according to ISO 2722 and good easy-to-clean properties. The composition according to the invention includes a glass component including by weight from about 45% to about 55% SiO2, from about 8% to about 17% B2O3, from about 1.8% to about 17.7% SrO+BaO, from about 1.9% to about 10% Li2O, up to about 6% ZrO2, from about 2% to about 11% TiO2, from about 1.5% to about 6% K2O, from about 1% to about 4% MoO3, from about 0.3% to about 13% Na2O, up to about 2% NiO, up to about 3% Al2O3, up to about 2.9% MnO, up to about 0.8% CoO, up to about 3% MgO, up to about 5% CaO, and up to about 2% Sb2O3.

Abstract: The present invention provides a composition for use in forming an adherent, brilliant white, chemically and mechanically resistant porcelain enamel coating on aluminized steel. The composition includes a self-opacifying glass frit component which includes high levels of titanium dioxide, lithium oxide, sodium oxide, and potassium oxide. The composition is able to produce a brilliant white finish on aluminized steel in one coat without the addition of titanium oxide during milling.

Abstract: The present invention provides a new and improved porcelain enamel coating composition for use in forming a self-cleanable coating upon aluminized steel. The coating composition comprises a glass component having a composition comprising from about 30% to about 55% SiO2, from about 11% to about 20% TiO2, from about 0% to about 10% B2O3, from about 20% to about 40% alkali metal oxides, less than about 5% rare earth metal oxides, from about 0% to about 10% CaO, from about 0% to about 10% BaO, from about 0% to about 10% MnO, from about 2% to about 12% CuO, from about 0% to about 10% Sb2O3, from about 1.5% to about 10% Fe2O3, from about 0% to about 10% SnO2, from about 0% to about 10% P2O5, less than about 2% MoO3, and less than about 5% V2O5.

Abstract: The present invention provides a composition for use in forming a white porcelain enamel coating on aluminized or galvanized steel. The composition according to the present invention includes a solids portion including a glass component and a white pigment. The glass component includes one or more glass frits including by weight from about 30% to 50% P2O5, from about 15% to about 30% Al2O3, from about 8% to about 40% X2O where X=Na and/or K, up to about 30% TiO2, up to about 12% B2O3, up to about 10% K2O, up to about 10% ZnO, up to about 8% SiO2, up to about 7% La2O3, up to about 5% Li2O, and up to about 15% F. The white pigment include TiO2.