Abstract: A fire-proof insulation material, in particular a fire-proof insulation material, which is composed of a harden-able compound which contains 19 to 40 wt % of porous glass balls, 60 to 81 wt % of an aqueous solution of sodium silicate having a density in the range of 1370 to 1400 kg/m3 and a molar ratio of SiO2 to Na2O in the range of 3.2 to 3.4, and 0.1 to 1 wt % water glass binder stabiliser, while further containing 2 to 10 wt % of chopped basalt fibre, and the surface of the porous glass balls having a diameter of 0.3 to 1 mm is provided with carbon black, the carbon black constituting 0.1 to 0.9 wt % of total weight.

Abstract: A surface protection compound, in particular a compound for the non-flammable water-resistant non-hazardous biocidal surface protection of wood, or paper, or textile, or plastic, which contains an aqueous silicate solution which contains 93 to 98 wt % of an aqueous solution of potassium silicate, 1 to 6 wt % of aluminium hydroxide and, 0.5 to 1.5 wt % of stabiliser of the aqueous solution of potassium silicate.

Abstract: A wood chip material, especially a fireproof water resistant wood chip material, especially a fireproof water resistant wood chip material to make oriented strand boards which consists of a mixture containing 30 to 43 weight percent of wood chips, 53 to 61.9 weight percent of an aqueous solution of silicate, 2 to 5 weight percent of aluminium hydroxide, 1 to 3 weight percent of water, 0.1 to 1 weight percent of a stabilizer of the aqueous solution of silicate, and a hardener of the aqueous solution of sodium silicate in the concentration of 0.5 to 5 weight percent to the pure aqueous solution of sodium silicate providing always that the density of the aqueous solution of sodium silicate ranges from 1370 to 1400 kg/m3 and the SiO2 to NA2O molar ratio in the aqueous solution of sodium silicate ranges from 3.2 to 3.4.

Abstract: A fire-proof material, in particular a fire-proof thermal insulation material containing water glass, which is composed of a compound which contains 34 to 49.9 wt % of inorganic non-flammable fibres, 50 to 65 wt % of an aqueous silicate solution, and 0.1 to 1 wt % of water glass stabiliser, while it further contains a water glass hardener and the aqueous silicate solution has a density in the range of 1370 to 1400 kg/m3 and a molar ratio of SiO2 to Na2O in the range of 3.2 to 3.4.

Abstract: A fire-proof material, in particular a fire-proof thermal insulation material containing water glass, which is composed of a compound which contains 34 to 49.9 wt % of inorganic non-flammable fibres, 50 to 65 wt % of an aqueous silicate solution, and 0.1 to 1 wt % of water glass stabiliser, while it further contains a water glass hardener and the aqueous silicate solution has a density in the range of 1370 to 1400 kg/m3 and a molar ratio of SiO2 to Na2O in the range of 3.2 to 3.4.

Abstract: An insulating material, in particular a permeable fire-proof insulating material comprising water glass and polystyrene, consisting of a hardening mixture which contains 1 to 32.4 wt % of expanded polystyrene, 57.5 to 96.0 wt % of aqueous sodium silicate solution, 2 to 6 wt % of aluminium hydroxide, 0.8 to 2.6 wt % water glass hardener and 0.1 to 0.5 wt % of water glass stabilizer, while the surface of the expanded polystyrene is provided with carbon black, the carbon black making up 0.1 to 1 wt % of total weight.

Abstract: A wood chip material, especially a fireproof water resistant wood chip material, especially a fireproof water resistant wood chip material to make oriented strand boards which consists of a mixture containing 30 to 43 weight percent of wood chips, 53 to 61.9 weight percent of an aqueous solution of silicate, 2 to 5 weight percent of aluminium hydroxide, 1 to 3 weight percent of water, 0.1 to 1 weight percent of a stabilizer of the aqueous solution of silicate, and a hardener of the aqueous solution of sodium silicate in the concentration of 0.5 to 5 weight percent to the pure aqueous solution of sodium silicate providing always that the density of the aqueous solution of sodium silicate ranges from 1370 to 1400 kg/m3 and the SiO2 to NA2O molar ratio in the aqueous solution of sodium silicate ranges from 3.2 to 3.4.

Abstract: A mixture for a thermal insulating plaster, especially a mixture for a thermal insulating plaster that contains aqueous solution of silicate, which contains 78 to 90 volume percent of hollow glass microspheres, 5 to 17 volume percent of aqueous solution of potassium silicate, 0.1 volume percent of water-glass-binder stabilizer, 1.5 to 5 volume percent of styrene-acrylate dispersion, 0.4 to 3 volume percent of aqueous colloidal solution of silver, 0.2 to 2.4 volume percent of tensides as an aerating agent, and 0.5 to 7 volume percent of water.

Abstract: An insulating material, especially a non-flammable thermally insulating material containing water glass and a plastic component consisting of a mixture containing 43 to 57.5 weight percent of a plastic component, 30 to 47 weight percent of an aqueous solution of silicate, 9 to 11.5 weight percent of hollow glass microspheres, and 0.1 to 1 weight percent of a water glass stabilizer. Method of production of the insulating material, especially method of production of the non-flammable thermally insulating material lying in the fact that, as the first step, a water glass stabilizer is added into the aqueous solution of silicate and, at the same time, a mixture of phenyl methyl diisocyanate and branched polyol is prepared and then the aqueous solution of silicate is intermixed with the mixture of phenyl methyl diisocyanate and branched polyol and thereafter hollow glass spheres are added into the resulting mixture and everything is then thoroughly mixed again.

Abstract: A compound for reinforcing surface treatment, in particular a compound for waterproof reinforcing surface treatment of concrete containing water glass, which contains 1 to 10 wt % of bis (?-triethoxysilylpropyl) tetrasulphide, 89.9 to 98 wt % of an aqueous solution of lithium silicate, and 0.1 to 1 wt % water glass stabiliser. The full text of the replacement paragraph without any underlining or strikethrough is provided below: A compound for reinforcing surface treatment, in particular a compound for waterproof reinforcing surface treatment of concrete containing water glass, which contains 1 to 10 wt % of bis (?-triethoxysilylpropyl) tetrasulphide, 89.9 to 98 wt % of an aqueous solution of lithium silicate, and 0.1 to 1 wt % water glass stabiliser.

Abstract: An insulating material, in particular a permeable fire-proof sound insulating material comprising water glass and rubber, in particular recycled rubber, consisting of a harden-able mixture which contains 47 to 61 wt % of rubber granulate, 30 to 50 wt % of aqueous sodium silicate, 0.1 to 0.5 wt % water glass stabiliser, 0.4 to 1.5 wt % water glass hardener, and 2 to 6 wt % of aluminium hydroxide, the surface of the rubber granulate being provided with carbon black, the carbon black constituting 0.1 to 1 wt % of total weight.

Abstract: A surface protection compound, in particular a compound for the non-flammable water-resistant non-hazardous biocidal surface protection of wood, or paper, or textile, or plastic, which contains an aqueous silicate solution which contains 93 to 98 wt % of an aqueous solution of potassium silicate, 1 to 6 wt % of aluminium hydroxide and, 0.5 to 1.5 wt % of stabiliser of the aqueous solution of potassium silicate.

Abstract: A plaster treatment compound, in particular a compound for reinforcing waterproof plaster treatments containing water glass, which contains 20 to 69 wt % of an aqueous solution of potassium silicate, 20 to 59.9 wt % of aqueous lithium silicate solution, 10 to 20 wt % of octyltriethoxysilane, and 0.1 to 1 wt % water glass stabilizer.

Abstract: A fire-proof insulation material, in particular a fire-proof insulation material, which is composed of a harden-able compound which contains 19 to 40 wt % of porous glass balls, 60 to 81 wt % of an aqueous solution of sodium silicate having a density in the range of 1370 to 1400 kg/m3 and a molar ratio of SiO2 to Na2O in the range of 3.2 to 3.4, and 0.1 to 1 wt % water glass binder stabiliser, while further containing 2 to 10 wt % of chopped basalt fibre, and the surface of the porous glass balls having a diameter of 0.3 to 1 mm is provided with carbon black, the carbon black constituting 0.1 to 0.9 wt % of total weight.

Abstract: The invention relates to a coating composition, especially to a coating composition intended for thermal insulation of hot metals, which contains an aqueous solution of silicate and which consists of the first layer containing 35 to 71 volume percent of hollow glass spheres, 26 to 62 volume percent of an aqueous solution of potassium silicate, 1 to 3 volume percent of an adhesive additive, and 0.1 volume percent of a water glass stabilizer, and of at least one second layer containing 71 to 84.6 volume percent of hollow glass spheres, 9 to 22.6 volume percent of an aqueous solution of potassium silicate, 0.2 to 0.3 volume percent of an adhesive additive, 0.1 volume percent of a water glass stabilizer, 2 to 3 volume percent of cut glass fibres, and 1.7 to 3 volume percent of a styrene-acrylate dispersion.

Abstract: An insulating material, in particular a permeable fire-proof insulating material comprising water glass and which is composed of a air harden-able compound which contains 2 to 40 wt % of plastic balls, 55 to 95.0 wt % of aqueous sodium silicate solution, 2 to 6 wt % of aluminium hydroxide, and 0.1 to 0.5 wt % water glass stabiliser.