Abstract: The coating agent composition comprises an emulsion containing (A) polydiorganosiloxane having a viscosity of 50 to 10,000,000 mPa·s at 25° C. and having both terminal ends blocked by hydroxyl groups, (B) polyorganohydrogensiloxane having at least three hydrogen atoms bonded to silicon atoms in one molecule, (C) a curing catalyst, and (D) chlorinated polyolefine and/or acryl-modified polyolefine, with which (E) fine spherical particles comprised of a rubber-like elastomer having hardness of less than 90 are mixed to disperse into it. The coating agent composition having good uniform applying property, non tackness, water repellency and lubricating properties and outstanding adhesiveness to a rubber or plastic substrate can be obtained.
Abstract: The coating agent composition comprises an emulsion containing (A) polydiorganosiloxane having a viscosity of 50 to 10,000,000 mPa·s at 25° C. and having both terminal ends blocked by hydroxyl groups, (B) polyorganohydrogensiloxane having at least three hydrogen atoms bonded to silicon atoms in one molecule, (C) a curing catalyst, and (D) chlorinated polyolefine and/or acryl-modified polyolefine, with which (E) fine spherical particles comprised of a rubber-like elastomer having hardness of less than 90 are mixed to disperse into it. The coating agent composition having good uniform applying property, non tackness, water repellency and lubricating properties and outstanding adhesiveness to a rubber or plastic substrate can be obtained.
Abstract: A wiper blade rubber is provided, which has low sliding resistance against a glass surface, hardly generates creak and chatter, has good flexibility and bending property at low temperatures, has excellent durability, and has good design property. The wiper blade rubber has a main body, at least an outer surface of which is coated with a silicone rubber, and a wiping layer comprising a high-hardness organic rubber provided by on a tip portion of the main body at a contact side to a glass surface.
Abstract: Spherical silicone fine particles having an average particle diameter of 0.1 to 5 &mgr;m, which can be produced without decreasing a yield and also without conducting a dilution step, and a process for effectively producing the same. Spherical silicone particles are obtained by reacting an organotrialkoxysilane with a tetraalkoxysilane. Water in an amount of 20 to 150 moles is added to 1 mole of the silane mixture, which is subjected to hydrolysis under an acidic condition to obtain an aqueous or alcohol solution of an organosilanol and/or the partial hydrolyzed product thereof, and an aqueous alkaline solution is added thereto, mixed and allowed to stand to conduct polycondensation.