Abstract: Disclosed is a bulk block for manufacturing a prosthesis having high aesthetics and processability required for one-day dental prosthetic materials, which is a dental composite bulk block comprising a glass ceramic matrix and a polymer, wherein the glass ceramic matrix consists of an amorphous glass matrix and a crystalline phase dispersed in the glass matrix, the crystalline phase comprises as a main crystalline phase at least one selected from a leucite crystalline phase and a lithium disilicate crystalline phase, and has an average particle diameter of 0.01-1.0 ?m, and the polymer is included in an amount of 20-40 wt % with respect to the weight of the total bulk block. The bulk block has the advantages of improved mechanical properties, being capable of preventing microleakage, exhibiting excellent aesthetics, and enabling machining.

Abstract: Provided is a silicate glass, a method for preparing a silicate glass-ceramics by using the silicate glass, and a method for preparing a lithium disilicate glass-ceramics by using the silicate glass, and more particularly, to a method for preparing a glass-ceramics that has a nanosize of 0.2 to 0.5 ?m and contains lithium disilicate and silicate crystalline phases. A nano lithium disilicate glass-ceramics containing a SiO2 crystalline phase includes: a glass composition including 70 to 85 wt % SiO2, 10 to 13 wt % Li2O, 3 to 7 wt % P2O5 working as a nuclei formation agent, 0 to 5 wt % Al2O3 for increasing a glass transition temperature and a softening point and enhancing chemical durability of glass, 0 to 2 wt % ZrO2, 0.5 to 3 wt % CaO for increasing a thermal expansion coefficient of the glass, 0.5 to 3 wt % Na2O, 0.5 to 3 wt % K2O, and 1 to 2 wt % colorants, and 0 to 2.0 wt % mixture of MgO, ZnO, F, and La2O3.

Abstract: Disclosed is a machinable dental bulk block that is a glass ceramic block including an amorphous glass matrix and crystalline phases introduced into the matrix. A major crystalline phase is lithium disilicate and minor crystalline phases are lithium phosphate and at least one of spodumene and virgilite. The dental block is made of a functionally gradient material in which the major crystalline phase exhibits a gradient of particle sizes in a depth direction of the dental block and which has no interface at a point where the gradient of particle sizes of the major crystalline phase changes. The dental bulk block is useful for production of a dental prosthesis (artificial tooth) similar to a natural tooth. The dental bulk block can reduce time and the number of processing steps to manufacture a dental prosthesis and provides improved structural stability through good force distribution obtained by functionally graded mechanical properties.

Abstract: Proposed is a hybrid ceramic prosthesis. Since the prosthesis is made of a novel hybrid ceramic material, the prothesis has a similar color and transmittance to natural teeth, minimizes tooth removal during preparation for placement of the prothesis, is securely attached to the target tooth by snap-fit fastening to prevent detachment of the prothesis and re-treatment caused by the prothesis detachment, and can be more conveniently applied to the patient than conventional prostheses, enabling an one-day-one-stop dental procedure, thereby reducing burden to patients. The prothesis is useful as a primary crown.

Abstract: Dental composite composition including a glass ceramic and a curable organic material is described in which the glass ceramic includes a crystal phase having an average grain size of 50 to 400 nm, and the dental composite composition is provided as a dental prosthetic material exhibiting superior transparency and mechanical properties comparing to conventional composite products containing micro-sized crystal grains and also has excellent aesthetics and processability required for prosthetic materials for same-day dental prosthetic service.

Abstract: Provided is a dental bulk block for grinding processing. The dental bulk block includes a crystalloid, which includes lithium disilicate as a main crystal phase and silicate as a sub-crystal phase, and hyaline as a remainder. The dental bulk block is a functionally gradient material having a crystalline size gradient with respect to a depth thereof and having no interface at a change point of a crystalline size gradient value. The dental bulk block is useful for manufacturing an artificial dental prosthesis that is similar to natural teeth. Accordingly, the time and process for manufacturing the artificial dental prosthesis are shortened, and structural stability is increased in terms of dispersion of force due to gradient functionalization of mechanical properties.

Abstract: Provided is a method for preparing a lithium disilicate glass-ceramics containing silicate as a main component, and more particularly, to a method for preparing a glass-ceramics, which is capable of adjusting machinability or translucency according to a crystalline size by using a first heat treatment or a second heat treatment. To this end, a method for preparing a glass-ceramics containing a silica crystalline phase includes: performing a first heat treatment on a glass composition at a temperature of 400 to 850° C., so that a lithium disilicate crystalline phase and a silica crystalline phase each having a size of 5 to 2,000 nm are formed through the first heat treatment. After the first heat treatment, the method further includes performing a second heat treatment at a temperature of 780 to 880° C., so that translucency is adjusted by a temperature of the second heat treatment.

Abstract: The present invention relates to a method for preparing a lithium disilicate glass-ceramics containing silicate as a main component, and more particularly, to a method for preparing a glass-ceramics, which is capable of adjusting machinability or translucency according to a crystalline size by using a first heat treatment or a second heat treatment. To this end, a method for preparing a glass-ceramics containing a silica crystalline phase includes: performing a first heat treatment on a glass composition at a temperature of 400 to 850° C., so that a lithium disilicate crystalline phase and a silica crystalline phase each having a size of 5 to 2,000 nm are formed through the first heat treatment. After the first heat treatment, the method further includes performing a second heat treatment at a temperature of 780 to 880° C., so that translucency is adjusted by a temperature of the second heat treatment.

Abstract: A method of bonding a high-strength zirconia post serving as a core in a glass-ceramic block, a method of bonding a metal link fastened with an implant fixture to the zirconia post, and glass-ceramic bondable to the zirconia post and a preparation method thereof, when preparing artificial teeth through a CAD/CAM processing method by using the glass-ceramic block as an artificial-teeth material. The lithium disilicate glass-ceramics containing cristobalite crystalline includes glass-ceramics composition including 10 to 15 wt % Li2O, 68 to 76 wt % SiO2, 2 to 5 wt % P2O5 working as a nuclei formation agent, 0 to 5 wt % Al2O3 to increase glass transition temperature and softening temperature and increase chemical durability of the glass, 2 to 3 wt % ZrO2, 0.5 to 3 wt % CaO for enhancing a thermal expansion coefficient of the glass, 0.5 to 5 wt % Na2O, 0.5 to 5 wt % K2O, and 1 to 2 wt % colorants, and 0 to 2.0 wt % mixture of MgO, ZnO, F, and La2O3.

Abstract: Exemplary embodiments of the present disclosure provide a lithium silicate crystalline or amorphous glass overlaying the top surfaces of zirconia and the manufacturing process thereof. More specifically, exemplary embodiments of the present disclosure provide a lithium silicate glass or lithium silicate crystalline glass with high light transmittance and good coloring characteristics and the manufacturing process thereof, which overlays the top surface of zirconia with high mechanical strength, frameworks, or copings. The lithium silicate crystalline or amorphous glass may include 10-15 wt % Li2O, 71.1-85.0 wt % SiO2, 2-5 wt % P2O5 working as nuclear formation agent, 1-5 wt % Al2O3 to increase glass transition temperature and softening temperature, as well as chemical durability of the glass, and 0.01-1.0 wt % ZrO2 which increases the binding strength of the zirconia substructure.

Abstract: Provided is lithium disilicate crystalline glass containing cristobalite crystal phase for high strength and aesthetic traits and its manufacturing process thereof. Exemplary embodiments of the present invention provide the high strength and aesthetic lithium disilicate crystalline glass, one kind of dental restoration materials, and its manufacturing method which induces the growth of the different crystal phase, cristobalite, from glass with lithium disilicate crystal.

Abstract: A method of manufacturing a ceramic primary crown including mixing a source material including zirconia or alumina that configures a frame of a primary crown, a polymer for reducing viscosity and applying ductility upon injection molding, and a toner for providing the same or similar color as baby teeth, heating the polymer contained in the mixed source material to have ductility, injection molding the heated source material, extracting the polymer to reduce brittleness and increase ductility with respect to the injection-molded matter, removing fat to completely eliminate the polymer element from the injection-molded matter, from which the polymer is partially extracted through the polymer extraction, sintering the fat-removed body, from which the polymer is removed, to improve mechanical properties, and polishing an outer surface of the sintered body to provide gloss, and performing barrel-finishing to remove a burr.

Abstract: Provided is lithium disilicate crystalline glass containing cristobalite crystal phase for high strength and aesthetic traits and its manufacturing process thereof. Exemplary embodiments of the present invention provide the high strength and aesthetic lithium disilicate crystalline glass, one kind of dental restoration materials, and its manufacturing method which induces the growth of the different crystal phase, cristobalite, from glass with lithium disilicate crystal.

Abstract: A method of manufacturing a ceramic primary crown including mixing a source material including zirconia or alumina that configures a frame of a primary crown, a polymer for reducing viscosity and applying ductility upon injection molding, and a toner for providing the same or similar color as baby teeth, heating the polymer contained in the mixed source material to have ductility, injection molding the heated source material, extracting the polymer to reduce brittleness and increase ductility with respect to the injection-molded matter, removing fat to completely eliminate the polymer element from the injection-molded matter, from which the polymer is partially extracted through the polymer extraction, sintering the fat-removed body, from which the polymer is removed, to improve mechanical properties, and polishing an outer surface of the sintered body to provide gloss, and performing barrel-finishing to remove a burr.