Abstract: The invention relates to a method for incinerating carbon-containing dry metallic ash and a pertinent device. The method comprises the steps of p) adding the metallic ash into a trough; q) aerating with ambient air from above, and concurrently, at least for part of the time, r) injecting air and/or oxygen through the trough hearth; s) establishing the ignition temperature; t) stirring of the metallic ash by means of a suitable tool; u) whereby the carbon content is reduced to less than 3%; and whereby steps b), c), and d) can proceed concurrently or in alternating order or pairs or all of these steps can proceed concurrently; step d) can just as well proceed selectively in partial quantities of the metallic ash; and whereby the reverse transport of ash through the trough hearth is prevented, whereas the supply of air and/or oxygen is maintained.

Abstract: A method recovers noble metals from noble metal-containing compositions and includes steps of (i) providing a noble metal-containing composition containing an adsorption agent that is based on an inorganic material and is functionalized by organic groups and has at least one noble metal adsorbed to it, and (ii) ashing of the noble metal-containing composition provided in step (i) in order to adjust a residual carbon content of at most 10% by weight, relative to the total weight of the noble metal-containing composition after ashing, to obtain an ashed composition.

Abstract: This invention provides a thick-film composition for printing the front-side of a solar cell device having one or more insulating layers. The composition comprises a bismuth oxide comprising glass frit and antimony oxide as part of the glass frit or an additive. The invention further refers to a process for preparing a semiconductor device by use of the thick-film composition and an article, especially a solar cell comprising the semiconductor device. The solar cells show improved efficiency.

Abstract: Described are processes for the production of silver nanowires comprising forming a reaction mixture including a polyol, an organic chemical adsorbed to a silver surface, a chemical to form a halide and/or pseudohalide and a chemical which forms a redox pair. A silver salt is added to the reaction mixture and temperature is maintained to form the silver nanowires.

Abstract: The invention relates to a process for producing electrolytic capacitors with low equivalent series resistance, to electrolytic capacitors produced by this process and to the use of such electrolytic capacitors.

Abstract: The invention relates to a thick film conductive composition comprising metal particles wherein the specific surface area of the silver particles measured by BET according to ISO 9277 is equal to or more than 1.8 m2/g; manganese oxide; glass particles; and an organic vehicle.

Abstract: The invention relates to a process for the production of electrolyte capacitors having a low equivalent series resistance and low residual current for high nominal voltages, electrolyte capacitors produced by this process and the use of such electrolyte capacitors.

Abstract: The disclosure describes a monomer having the general formula (I): in which R1 and R2 stand, independently of one another, for hydrogen, for an optionally substituted C1-C20-alkyl group or C1-C20-oxyalkyl group, optionally interrupted by 1 to 5 oxygen atoms and/or sulfur atoms, or jointly for an optionally substituted C1-C20-dioxyalkylene group or C6-C20-dioxyarylene group. The monomer has a color in a range of a Hazen color number determined according to test method described herein of at least 20 to a Gardner color number determined according to test method described herein of not more than 5. The present invention also relates to a method for the manufacture of a capacitor, a capacitor obtained by this method and to the use of a monomer.

Abstract: A recycling furnace is provided for processing potentially explosive precious metal-containing materials having organic fractions that combust with great energy. The furnace includes a switching facility for alternating operation of two burning-off chambers of the furnace between: (A) pyrolysis or carbonization under protective furnace gas in an atmosphere comprising maximally 6 wt-% oxygen, and (B) oxidative combustion of the organic fractions including carbon. The furnace has indirect heating and a control that determines the end of the pyrolysis or carbonization by a sensor and controls the switching facility to supply air or oxygen to the interior of the furnace. A continuous conveyor for dosing of liquids or liquefied substances during the pyrolysis is controlled by at least one parameter of post-combustion, preferably a temperature sensor. A single waste gas treatment facility is used for thermal post-combustion for the two furnace chambers.

Abstract: A stimulation electrode is produced having a porous film layer and being partially coated with an insulating parylene (polyparaxylylene) film, whose insulating film has a dielectric breakdown voltage of greater than 100 V. Parylene is deposited on the entire surface of a porous film coating and then partially removed again by plasma. After the partial removal of the parylene, this porous film still has a capacitance of greater than 15 mF/cm2 in a physiological NaCl solution at a frequency of 0.1 Hz. For the stimulation electrode, the transition from the insulating film to the porous film is formed so that the film thickness of the parylene film decreases continuously. In this way, a stimulation electrode having a porous film layer and being partially coated with an insulating parylene film is provided, whose electrode on the non-insulating parylene film-coated surface has a capacitance of greater than 15 mF/cm2 in a physiological NaCl solution at a frequency of 0.

Abstract: The present invention relates to a medical device or implant made at least in part of a high strength, low modulus metal alloy comprising Niobium, Tantalum, and at least one element selected from the group consisting of Zirconium, Tungsten and Molybdenum. The medical devices according to the present invention provide superior characteristics with regard to biocompatibility, radio-opacity and MRI compatibility.

Abstract: A metallic material is made from at least one refractory metal or an alloy based on at least one refractory metal. The metallic material has an oxygen content of about 1,000 to about 30,000 ?g/g and the oxygen is interstitial.

Abstract: The present invention relates to a medical device or implant made at least in part of a high-strength, low-modulus metal alloy comprising niobium, tantalum, and at least one element selected from the group consisting of zirconium, tungsten, and molybdenum. The medical devices according to the present invention provide superior characteristics with regard to biocompatibility, radio-opacity and MRI compatibility.

Abstract: The invention relates to compositions which include: (a) a polythiophene containing repeating units represented by the following general formula (I), wherein X represents, for example, —CH2—CH(CH2—O—(CH2)4SO3?H+)—; and (b) further polymers, that are different than polythiophene (a), and which contain SO3? M+ or COO?M+ groups. Also disclosed are electroluminescing (EL) arrangements that contain hole-injecting layers which include such compositions.

Abstract: A crystalline epirubicin hydrochloride and a method for its production are provided. The method for producing the crystalline epirubicin hydrochloride includes the steps: (a) providing epirubicin hydrochloride, (b) producing a mixture containing the provided epirubicin hydrochloride and at least one alcohol selected from the group 1-butanol, 2-butanol, and 1-pentanol, and (c) crystallizing epirubicin hydrochloride from this mixture.

Abstract: The invention relates to a process for the production of electrolyte capacitors having a low equivalent series resistance and low residual current for high nominal voltages, electrolyte capacitors produced by this process and the use of such electrolyte capacitors.

Abstract: A bright noble metal preparation for firing on ceramic/porcelain surfaces at a minimum temperature of 900° C. The preparation has at least one organic noble metal compound including at least one of an organic gold, platinum, silver, and palladium compound, at least one flux that consists of organometallic compounds including Cr in the form of at least one organic compound, such that a Cr content is 0.01 to 1.0 mole per mole of noble metal, and at least one vehicle. The bright noble metal preparation is rhodium-free and has a noble metal content of 6 to 20 wt. %, based on the preparation.

Abstract: A stimulation electrode is provided having an electrically conducting electrode base member which is partially covered with an electrically insulating ceramic layer. The ceramic layer is formed of an oxide and/or an oxynitride of at least one metal of the group of titanium, niobium, tantalum, zirconium, aluminum and silicon. Various methods are provided for production of the stimulation electrode, including methods in which the ceramic layer is formed in situ by a thermal, chemical or electrochemical oxidation or oxynitridation process. The stimulation electrode may be used as a cardiac pacemaker electrode, a neuro-stimulation electrode, or another human implant.

Abstract: A bright noble metal preparation for firing on ceramic/porcelain surfaces at a minimum temperature of 900° C. The preparation has at least one organic noble metal compound including at least one of an organic gold, platinum, silver and palladium compound, at least one flux that consists of organometallic compounds including Cr in the form of at least one organic compound, such that a Cr content is 0.01 to 1.0 mole per mole of noble metal, and at least one vehicle. The bright noble metal preparation is rhodium-free and has a noble metal content of 6 to 20 wt. %, based on the preparation.

Abstract: A method recovers noble metals from noble metal-containing compositions and includes steps of (i) providing a noble metal-containing composition containing an adsorption agent that is based on an inorganic material and is functionalized by organic groups and has at least one noble metal adsorbed to it, and (ii) ashing of the noble metal-containing composition provided in step (i) in order to adjust a residual carbon content of at most 10% by weight, relative to the total weight of the noble metal-containing composition after ashing, to obtain an ashed composition.