Abstract: The invention relates to a method for the economic production of a blank for a component made from laser-active quartz glass in any form or dimension. The method comprises the following method steps: a) preparation of a dispersion with a solids content of at least 40 wt. %, comprising SiO2 nanopowder and doping agents, including a cation of the rare earth metals and transition metals in a fluid, b) granulation by agitation of the dispersion, with removal of moisture to form a doped SiO2 granulate of spherical porous granular particles with a moisture content of less than 35 wt. % and a density of at least 0.95 g/cm3, c) drying and purification of the SiO2 granulate, by heating to a temperature of at least 1000° C. to form doped porous SiO2 grains with an OH content of less than 10 ppm and d) sintering or fusing the doped SiO2 grains in a reducing atmosphere to give the blank made from doped quartz glass.

Abstract: A device is provided for measuring the cooling curve of melts and/or the heating curve of melt samples with an optical fiber, wherein an immersion end of the optical fiber having an at least partially free surface is surrounded with a spacing by a temperature-resistant sample-receiving chamber. The optical fiber is immersed with its immersion end in the melt, and a sample is thereby formed in the sample-receiving chamber. The sample-receiving chamber with the sample and the optical fiber are thereafter pulled out of the molten metal. The cooling curve of the sample and/or, after previous solidification of the sample, the temperature profile during heating is measured with reference to a signal obtained by the optical fiber and forwarded to a measurement device.

Abstract: A stimulation electrode is produced having a porous film layer and being partially coated with an insulating parylene (polyparaxylylene) film, whose insulating film has a dielectric breakdown voltage of greater than 100 V. Parylene is deposited on the entire surface of a porous film coating and then partially removed again by plasma. After the partial removal of the parylene, this porous film still has a capacitance of greater than 15 mF/cm2 in a physiological NaCl solution at a frequency of 0.1 Hz. For the stimulation electrode, the transition from the insulating film to the porous film is formed so that the film thickness of the parylene film decreases continuously. In this way, a stimulation electrode having a porous film layer and being partially coated with an insulating parylene film is provided, whose electrode on the non-insulating parylene film-coated surface has a capacitance of greater than 15 mF/cm2 in a physiological NaCl solution at a frequency of 0.

Abstract: A process by means of which the colonisation by plaque on dental materials can be permanently prevented or delayed without the product properties of the dental material being negatively influenced. The process involves equipping the dental material with anti-plaque substance, namely at least one molecularly dispersely distributed octenidine salt or dequalinium salt. Also disclosed is a dental material so equipped.

Abstract: Process for removing the noble metal from noble metal-containing moulded catalyst bodies, comprising these steps of A leaching the noble metal from loosely heaped moulded catalyst bodies, B removing the mother liquor, C automated conveying of the moulded bodies into a centrifuge, D renewed leaching, E separating off of the residual mother liquor by centrifuging.

Abstract: An immersion probe has a probe body having a longitudinal axis and an outer surface surrounding the longitudinal axis, wherein a portion of the outer surface has sampling elements, which extend around the longitudinal axis in the peripheral direction and which have a radial dimension. A protective layer, which can be dissolved or combusted in molten steel or slag, is arranged around the sampling elements.

Abstract: A measurement device, in particular anemometric measurement device of a flow sensor, contains film resistors in one or more opening(s) of a cover or a hollow body. The film resistors are fastened according to the invention in the opening(s). Two film resistors differ with respect to their resistance by one to three orders of magnitude. In an anemometric measurement device of a flow sensor according to the invention, a temperature sensor and a heating capacity sensor are placed in a carrier element. The temperature sensor has a temperature-measuring resistor and a heat conductor as platinum thin-film or thick-film resistors on a ceramic substrate. For self-cleaning of an anemometric measurement device of a flow sensor, in which a temperature-measuring element and a heating element are placed in a carrier element, the temperature-measuring element has a platinum thin-film resistor on a ceramic substrate for temperature measurement and is heated with an additional platinum thin-film resistor.

Abstract: A method known in prior art for determining the occupation of the surface of a silica glass component with impurities comprises taking a sample, a process in which at least some of the surface of the silica glass component is brought in contact with an acidic desorption solution, and surface impurities that are to be analyzed are accumulated therein and are subjected to an element-specific analysis. The aim of the invention is to create a method which is based on said method, allows the occupation of the surface of silica glass components to be determined accurately and reproducibly, and is suited for determining small amounts of impurities within the order of magnitude of 1010 atoms/cm2 also directly in situ. Said aim is achieved by the fact that taking the sample encompasses contacting the component surface with an acidic desorption solution containing water, nitric acid, and hydrofluoric acid, the nitric acid concentration in the desorption solution amounting to 1.

Abstract: A sputter target includes a sputter material made of an alloy or a material mixture composed of at least two components which are in a state of thermodynamic disequilibrium. The components are compacted by an isostatic or uniaxial cold-pressing process.

Abstract: A local system for the liberation of an active principle is described which consists of spherical bodies which are composed of polymethyl methacrylate or polymethyl methacrylate co-methyl acrylate and, if necessary, zirconium dioxide and/or barium sulphate and a pharmaceutical active principle, which contains at least one hemostyptically effective compound stable at least up to 120° C., preferably a calcium salt. The local system for the liberation of an active principle is provided as medical product or drug.

Abstract: A known SiO2 slurry for the production of quartz glass contains a dispersion liquid and amorphous SiO2 particles with particle sizes to a maximum of 500 ?m, wherein the largest volume fraction is composed of SiO2 particles with particle sizes in the range 1 ?m-60 ?m, as well as SiO2 nanoparticles with particle sizes less than 100 nm in the range 0.2-15% volume by weight (of the entire solids content). In order to prepare such a slurry for use, and to optimize the flow behavior of such a slurry with regard to later processing by dressing or pouring the slurry mass, and with regard to later drying and sintering without cracks, the invention suggests a slurry with SiO2 particles with a multimodal distribution of particle sizes, with a first maximum of the sizes distribution in the range 1 ?m-3 ?m and a second maximum in the range 5 ?m-50 ?m, and a solids content (percentage by weight of the SiO2 particles and the SiO2 nanoparticles together) in the range 83%-90%.

Abstract: To improve a generally known method for producing a tubular semifinished product from fluorine-doped quartz glass such that it is possible to produce a tubular semifinished product of fluorine-doped quartz glass with an inner bore of high quality while the efforts for making or treating the same are as small as possible, the present invention suggests a method comprising the following steps: (a) providing a substrate tube consisting of fluorine-doped quartz glass; (b) forming, in a deposition process, SiO2 particles by means of plasma burners and in the presence of fluorine, and depositing said particles in layers on the cylindrical outer surface of the substrate tube rotating about its longitudinal axis with formation of a mother tube consisting of fluorine-doped quartz glass; and (c) elongating the mother tube in an elongation process to obtain the tubular semifinished product.

Abstract: A self-curing or dual-curing, low viscosity composite is used for the fabrication of a dental liner capable of polymerization in 2 stages with 2 curing times and delayed polymerization characteristics that is designed for use at the cavity wall in the form of a thin layer.

Abstract: A method of forming a layer of an electrically conductive metal-silicide material, comprises steps of: providing a Si-containing workpiece; forming a Ni-doped Co layer on a surface of the workpiece, as by sputter deposition utilizing a Ni-doped Co sputtering target; and reacting the Ni-doped Co layer and workpiece. Embodiments include performing a salicide process to form electrically conductive Ni-doped Co silicide functioning as electrically conductive contacts to the gate electrode and source and drain regions of a MOS transistor. Also disclosed are PVD sources, e.g., sputtering targets, comprising Ni-doped Co and utilized for forming the Ni-doped Co layer.

Abstract: An electrode system with a current feedthrough through a ceramic discharge vessel is provided which, on one hand, increases the visible output of lamps and, on the other hand, allows smaller dimensions. For this purpose, the current feedthrough is made of rhenium or a platinum-group metal. In this way, improved color reproduction is also achievable. In preferred embodiments: (a) the current feedthrough is made of rhenium or a rhenium alloy or a platinum-group metal or a platinum-group metal alloy and the current feedthrough is brazed flush in the discharge vessel, (b) the discharge vessel has no shaft, and/or (3) the current feedthrough is in the form of one or more joined spheres.

Abstract: For composite materials having a total filler content of 80 to 95% by weight, containing A) 0.5 to 10% by weight of non-agglomerated nanofillers having particle sizes of 1 to 50 nm in the filler component, B) at least 60% by weight of a filler mixture of 50 to 90% coarse-particle and 10 to 50% fine-particle dental glass in the filler component, having a size ratio, relative to the average particle size (d50 value), of coarse to fine particles of >1:4 to 1:30, C) as monomer component, a monomer mixture of i. 60 to 80% bis-GMA or TCD-di-HEMA or TCD-di-HEA, ii. 10 to 18% UDMA, iii. Residual TEDMA and/or multifunctional crosslinkers, D) up to 1% photoinitiator(s); and E) optionally, at least one additional dental glass in the filler component having a different particle size than the coarse- and fine-particle dental glass, the polymerization shrinkage may be reduced to <1.

Abstract: In a known method for producing a cylindrical glass body in a vertical drawing process, a glass blank is softened in a heating zone and drawn off as a glass strand by means of a draw-off device at a controlled drawing speed, the draw-off device comprising a first draw-off unit with rolling bodies rolling on the glass strand and being distributed around the circumference thereof, the rolling bodies being formed by a reference rolling body and at least one auxiliary rolling body, the drawing speed being controlled via the speed of the reference rolling body.

Abstract: An electrode for medical applications is provided with a PtIr coating which is at least partly porous. The coating contains more than 20% iridium by weight and at least 100 ppm Pt. The coated areas of the electrode exhibit an electrochemical capacitance of more than 5 mF/cm2 in physiological saline solution at 37° C. and a measurement frequency of 100 mHz. A sputter process is suitable for this purpose, in which a porous platinum-iridium layer is deposited on the electrode by simultaneously sputtering at least one iridium target and at least one platinum target.

Abstract: A tubular target is provided having a cylindrical carrier tube, at least one target tube arranged on its exterior surface, and a connecting layer arranged between the target tube and the carrier tube. The connecting layer is electrically conductive and has a wetting degree of >90%.

Abstract: Starting from an optical component of quartz glass for transmitting ultraviolet radiation of a wavelength between 190 nm and 250 nm, with a glass structure essentially without oxygen defects, a hydrogen content ranging from 0.1×1016 molecules/cm3 to 5.0×1016 molecules/cm3, and with a content of SiH groups of less than 5×1016 molecules/cm3, to provide such a component which is particularly well suited for use with linearly polarized UV laser radiation, the present invention suggests that the component should have a content of hydroxyl groups ranging from 10 to 250 wt ppm and a fictive temperature above 1000° C.