Abstract: A process for overcoating granules with overcoating material in a granulator by providing the inside surface of the granulator, before introduction of the granules, with a layer of the overcoating material in a thickness of 0.1 to 1 mm, maintaining a preset entrainment height of the granules during the granulation process, and adding the overcoating material in the flowing particle bed. The deposited layers are very uniform.

Abstract: Substantially isotropic spherical fuel and absorber elements for high temperature reactors are produced by molding corresponding fuel particles and graphite molding compositions. There is used as graphite molding powder a mixture of graphitized granules of coke and a hardenable resin binder. There are first produced in steel dies at 80.degree. to 120.degree. C. half shells and a nucleus with a pressed density of 1.0 to 1.4 g/cm.sup.3 followed by molding in a further steel die to the final format.

Abstract: To produce spherical fuel or absorber elements for high temperature reactors a mixture of coated nuclear fuel or absorber particles and graphite molding composition is molded into spheres, carbonized in a furnace having gas flushing and calcined in a vacuum. There are attained high throughputs without addition of transportation aides by employing as resin binders a thermosetting synthetic resin, hardening the resin at 110.degree. to 170.degree. C. and subsequently allowing the spheres to roll for 1 to 10 hours through an oven which is inclined around 2.degree. to 12.degree. to the horizontal. Thereby the oven must exhibit an increasing and decreasing temperature profile, the flushing gas introduced from both sides and be removed in a temperature zone of 400.degree. to 500.degree. C.