Abstract: A method of treatment using a beam of singly- and multiply-charged gas ions produced by an electron cyclotron resonance (ECR) source of a glass material in which the ion acceleration voltage of between 5 kV and 1000 kV is chosen to create an implanted layer of a thickness equal to a multiple of 100 nm; and the ion dose per surface unit in a range of between 1012 ions/cm2 and 1018 ions/cm2 is chosen so as to create an atomic concentration of ions equal to 10% with a level of uncertainty of (+/?)5%. Advantageously this makes it possible to obtain materials made from glass that are non-reflective in the visible range.

Abstract: A treatment method of a sapphire material, said method comprising bombardment of a surface of the sapphire material, said surface facing a medium different from the sapphire material, by a single- and/or multi-charged gas ion beam so as to produce an ion implanted layer in the sapphire material, wherein the ions are selected from ions of the elements from the list consisting of helium (He), neon (Ne), argon (Ar), krypton (Kr), xenon (Xe), boron (B), carbon (C), nitrogen (N), oxygen (O), fluorine (F), silicon (Si), phosphorus (P) and sulphur (S). Use of said method to obtain a capacitive touch panel having a high transmission in the visible range.

Abstract: Process for treatment of a sapphire part with a beam of a mixture of mono- and multicharged ions of a gas which are produced by an electron cyclotron resonance (ECR) source, where: the voltage for acceleration of the ions is between 10 kV and 100 kV; the implanted dose, expressed in ions/cm2, is between (5×1016)×(M/14)?1/2 and 1017×(M/14)?1/2, where M is the atomic mass of the ion; the rate of displacement VD, expressed in cm/s, is between 0.025×(P/D) and 0.1×(P/D), where P is the power of the beam, expressed in W (watts), and D is the diameter of the beam, expressed in cm (centimetres). A part made of sapphire having a high transmittance and which is resistant to scratching is thus advantageously obtained.

Abstract: A method of treating a powder (P) made from cerium oxide using an ion beam (F) in which: —the powder is stirred once or a plurality of times; —the ions of the ion beam are selected from the ions of the elements of the list consisting of helium (He), boron (B), carbon (C), nitrogen (N), oxygen (O), neon (Ne), argon (Ar), krypton (Kr), xenon (Xe)—the acceleration voltage of the ions of the beam is between 10 kV and 1000 kV; —the treatment temperature of the powder (P) is less than or equal to Tf/3; —the ion dose per mass unit of powder to be treated is chosen from a range of between 1016 ions/g and 1022 ions/cm2 so as to lower the reduction temperature of the powder made from cerium oxide (P).

Abstract: The disclosure relates to a treatment method for coloring a metal that includes a) bombardment of the metal with a beam of singly- or multiply-charged gas ions produced by an electron cyclotron resonance source; b) heat treatment in ambient air so as to color the implanted metal using a temperature between 100° C. and 400° C. and an exposure time of between 1 minute and 4 hours.

Abstract: Process for treatment by an ion beam of a glass material where: the acceleration voltage of the ions is between 5 kV and 1000 kV; the temperature of the glass material is less than or equal to the glass transition temperature; the dose of nitrogen (N) or oxygen (O) ions per unit of surface area is chosen within a range of between 1012 ions/cm2 and 1018 ions/cm2 so as to reduce the contact angle of a drop of water below 20°; a prior pretreatment is carried out with argon (Ar), krypton (Kr) or xenon (Xe) ions in order to strengthen the durability of the superhydrophilic treatment. Superhydrophilic glass materials of long duration are thus advantageously obtained.

Abstract: A treatment method for modifying the reflected color of a sapphire material surface comprising bombardment by a single- and/or multi-charged gas ion beam so as to modify the reflected color of the treated sapphire material surface, wherein the ions are selected from ions of the elements from the list consisting of helium (He), neon (Ne), argon (Ar), krypton (Kr), xenon (Xe), boron (B), carbon (C), nitrogen (N), oxygen (O), fluorine (F), silicon (Si), phosphorus (P) and sulphur (S).

Abstract: A method of treatment using a beam of singly- and multiply-charged gas ions produced by an electron cyclotron resonance (ECR) source of a glass material in which—the ion acceleration voltage of between 5 kV and 1000 kV is chosen to create an implanted layer of a thickness equal to a multiple of 100 nm; —the ion dose per surface unit in a range of between 1012 ions/cm2 and 1018 ions/cm2 is chosen so as to create an atomic concentration of ions equal to 10% with a level of uncertainty of (+/?)5%. Advantageously this makes it possible to obtain materials made from glass that is non-reflective in the visible range.

Abstract: A method of treating a powder (P) made from cerium oxide using an ion beam (F) in which: —the powder is stirred once or a plurality of times; —the ions of the ion beam are selected from the ions of the elements of the list consisting of helium (He), boron (B), carbon (C), nitrogen (N), oxygen (O), neon (Ne), argon (Ar), krypton (Kr), xenon (Xe)—the acceleration voltage of the ions of the beam is between 10 kV and 1000 kV; —the treatment temperature of the powder (P) is less than or equal to Tf/3; —the ion dose per mass unit of powder to be treated is chosen from a range of between 1016 ions/g and 1022 ions/cm2 so as to lower the reduction temperature of the powder made from cerium oxide (P).