Abstract: The high strength 7xxx aluminum alloy products and methods of making such products are disclosed resulting in better fatigue crack deviation performance, and high anisotropic ductility. The 7xxx aluminum alloy product comprises 7.0 to 7.8 wt. % Zn, 1.1 to 2.2 wt. % Cu, and 1.1 to 2.1 wt. % Mg. This 7xxx aluminum alloy product can be fabricated to produce plate, extrusion or forging products, and is especially suitable for aerospace structural components, especially large commercial airplane wing structure applications. The minimum tensile yield strength (TYS) along rolling (LT) direction is higher than 65 ksi for 4 to 5 inch plate. The minimum Kmax at crack deviation point is higher than 31 ksi*in1/2 for 4 to 5 inch plate. The minimum elongation is 1.4% for all tensile orientations including lowest orientations of ST-22.5 to ST-45. The 7xxx aluminum alloy product provides high damage tolerance performance as well as better corrosion resistance performance suitable for aerospace application.