Abstract: A lead-free composition capable of being applied as a film and hardening to form a protective layer on the back of a mirror comprises a fluid organic resin and a corrosion inhibitor selected from the group consisting of dicyanadiamide, metal or acid salts of dicyandiamide, hydrogen cyanamide, and 2-cyanoacetamide. The organic resin may be any thermoplastic or thermosetting resin suitable for coating the reflective and other metallic layers of the mirror. Exemplary resins include alkyd resins, acrylic resins, modified alkyd resins, polyesters, urethane oils, vinyl halide polymers or copolymers, oleoresinous varnishes, nitrocellulose compositions, phenol-formaldehyde resin varnishes, and epoxy resins. Preferably, the resin is an alkyd or modified alkyd resin. The aforementioned corrosion inhibitor may be present in an amount from about 0.1 to 20 weight percent, preferably 0.5 to 10 weight percent, of the organic resin coating system. The resin system should be essentially free of lead and lead salts.

Abstract: Environmentally preferred water-based coatings can be substituted for solvent-based coatings in commercial wood finishing processes without sacrifice of coating quality. Art-recognized discoloration of water-based coatings due to uneven leaching of chromophoric substances, such as natural tannins, is eliminated by contacting the surface with a water soluble anti-leachate compound selected from the group consisting of carboxylic acid salts, mono/polyfunctional amines and amine derivatives and their acid addition salts. The process allows for marked reduction of VOC emissions from commerical wood finishing operations.

Abstract: A lead-free composition capable of being applied as a film and hardening to form a protective layer on the back of a mirror comprises a fluid organic resin and a corrosion inhibitor selected from the group consisting of dicyandiamide, metal or acid salts of dicyandiamide, hydrogen cyanamide, and 2-cyanoacetamide. The organic resin may be any thermoplastic or thermosetting resin suitable for coating the reflective and other metallic layers of the mirror. Exemplary resins include alkyd resins, acrylic resin, modified alkyd resins, polyesters, urethane oils, vinyl halide polymers or copolymers, oleoresinous varnishes, nitrocellulose compositions, phenol-formaldehyde resin varnishes, and epoxy resins. Preferably, the resin is an alkyd or modified alkyd resin. The aforementioned corrosion inhibitor may be present in an amount from about 0.1 to 20 weight percent, preferably 0.5 to 10 weight percent, of the organic resin coating system. The resin system should be essentially free of lead and lead salts.

Abstract: A composition capable of being applied as a film and hardening to form a protective layer on the back of a mirror comprises a fluid organic resin and a corrosion inhibitor selected from the group consisting of dicyandiamide and metal or acid salt thereof. The organic resin may be any thermoplastic or thermosetting resin suitable for coating the reflective and other metallic layers of the mirror. Exemplary resins include alkyd resins, acrylic resins, modified alkyd resins, polyesters, urethane oils, vinyl halide polymers or copolymers, oleoresinous varnishes, nitrocellulose compositions, phenol-formaldehyde resin varnishes, and epoxy resins. Preferably, the resin is an alkyd or modified alkyd resin. The dicyandiamide or metal or acid salt of dicyandiamide may be present in an amount from about 0.1 to 20 weight percent, preferably 0.5 to 10 weight percent, of the organic resin coating system. The resin system should be essentially free of lead and lead salts.

Abstract: Discoloration of water-based coatings due to uneven leaching of chromophoric substances, such as natural tannins and applied stains, is eliminated by contacting the surface with a water soluble anti-leachate compound selected from the group consisting of carboxylic acid salts, mono/polyfunctional amines and amine derivatives and their acid addition salts.