Abstract: A woven article for a carbon fiber reinforced plastic according to the present invention is a woven article of a spun yarn containing: about 10 wt % to about 60 wt % of a carbon fiber staple in which the content of carbon components is equal to or greater than about 97 wt %; and about 40 wt % to about 90 wt % of a thermoplastic resin fiber, wherein the carbon fiber staple is obtained by carbonizing carbon fiber reinforced plastic scrap at a temperature of about 900 to about 1400° C. The woven article for a carbon fiber reinforced plastic includes a carbon fiber staple manufactured from scrap generated during manufacture of the carbon fiber reinforced plastic, and allows economic recycling of the carbon fiber reinforced plastic scrap without a reduction in mechanical properties. When molded, productivity is high due to a short cycle time, there is almost no orientation, and an excellent flexural modulus is exhibited.

Abstract: A polyamide resin composition and a molded article including the same are disclosed. The polyamide resin composition includes: (A) an aromatic polyamide resin; (B) an aliphatic polyamide resin; (C) a modified polyolefin resin; and (D) calcium carbonate. The polyamide resin composition can have good properties in terms of heat resistance, impact resistance, plating adhesion, and the like.

Abstract: An aerator device and a filter system including the same are provided. The aerator device includes: a housing having an inner cavity defined therein, the housing including at least one sidewall and an upper surface connected to the at least one sidewall; a first partition formed within the inner cavity and extending from an upper end to a lower end to define a first cavity and a second cavity; and a second partition formed within the inner cavity between the first partition and a first sidewall of the at least one sidewall and extending from an upper end to a lower end to define a first chamber and a second chamber of the second cavity, and the housing includes an inlet opening communicating with the first cavity and an outlet opening communicating with the second chamber, and the second chamber gradually narrows towards the upper surface of the housing.

Abstract: A thermoplastic resin composition of the present invention is characterized by comprising: a thermoplastic resin containing a rubber-modified vinyl-based graft copolymer and an aromatic vinyl-based copolymer resin; zinc oxide; zinc phosphate; a surface-coated zinc oxide, of which a portion or the entirety of a surface is coated with zinc phosphate. The thermoplastic resin composition has excellent acid resistance and antibacterial properties.

Abstract: A thermoplastic resin composition and a molded article formed of the same. The thermoplastic resin composition includes: about 100 parts by weight of a polycarbonate resin; about 5 to about 20 parts by weight of a rubber modified aromatic vinyl copolymer resin; about 0.5 to about 3 parts by weight of a maleic anhydride-grafted rubber polymer; about 50 to about 100 parts by weight of glass fibers; about 10 to about 30 parts by weight of barium sulfate; and about 5 to about 20 parts by weight of a phosphorus flame retardant. The thermoplastic resin composition can have high specific gravity and good properties in terms of impact resistance, weather resistance, flame retardancy, fluidity, and the like.

Abstract: Disclosed are a polyester resin composition including (A) about 100 parts by weight of a polybutylene terephthalate (PBT) resin; (B) greater than or equal to about 0.01 parts by weight and less than about 0.1 parts by weight of a phenol-based antioxidant; (C) greater than or equal to about 0.01 parts by weight and less than about 0.1 parts by weight of a thioester-based antioxidant; (D) greater than or equal to about 0.01 parts by weight and less than 0.2 parts by weight of an ethylene acrylic acid-based copolymer; and (E) greater than or equal to about 0.01 parts by weight and less than 0.2 parts by weight of montan wax, and an article made using the same.

Abstract: A thermoplastic resin composition and a molded article including the same. The thermoplastic resin composition includes: about 100 parts by weight of a thermoplastic resin; about 1 to about 30 parts by weight of an additive for laser direct structuring (LDS additive); about 0.01 to about 5 parts by weight of a hindered phenol-based compound; about 0.01 to about 10 parts by weight of a sodium phosphate salt; about 0.01 to about 5 parts by weight of a phosphite compound; about 0.01 to about 5 parts by weight of a sulfonate compound; and about 0.01 to about 10 parts by weight of a metal oxide, wherein a weight ratio of the hindered phenol-based compound, the sodium phosphate salt, the phosphite compound and the sulfonate compound to the metal oxide may range from about 2:1 to about 10:1.

Abstract: A thermoplastic resin composition of the present invention comprises a rubber-modified vinyl-based graft copolymer, a first aromatic vinyl-based copolymer, a second aromatic vinyl-based copolymer, and a polyalkylene glycol, wherein the first aromatic vinyl-based copolymer is a copolymer of methyl methacrylate, methyl acrylate, an aromatic vinyl-based monomer, and a monomer copolymerizable with the aromatic vinyl-based monomer, the second aromatic vinyl-based copolymer is a copolymer of an aromatic vinyl-based monomer and a monomer copolymerizable with the aromatic vinyl-based monomer, and the weight ratio of methyl methacrylate to methyl acrylate, in the first aromatic vinyl-based copolymer, is approximately 1:0.01 to approximately 1:0.2. The thermoplastic resin composition has excellent discoloration resistance, color, transparency, and the like even after irradiation with ionizing radiation.

Abstract: A polyamide resin composition includes an aromatic polyamide resin, an aliphatic polyamide resin, a polyacrylic acid, and glass fibers. The polyamide resin composition can have good properties in terms of heat resistance, long-term heat resistance stability, and/or appearance characteristics.

Abstract: A thermoplastic resin composition includes: a polyester resin including a repeat unit represented by Formula 1 as described in the specification; glass fibers; a white pigment; an aromatic vinyl-olefin copolymer; and talc. The thermoplastic resin composition can have good properties in terms of reflectance, reflectance retention, impact resistance, and/or moldability.

Abstract: The present invention relates to a thermoplastic resin composition for a laser direct structuring process and a molded article produced therefrom. In one embodiment, the thermoplastic resin composition comprises: a polyamide resin; a polyester resin; a rubber-modified aromatic vinyl-based graft copolymer; an inorganic filler; and an additive for laser direct structuring.

Abstract: Provided is a thermoplastic resin composition having excellent electrical properties, and the thermoplastic resin composition comprises: (A) 100 parts by weight of polycarbonate; (B) 2 parts by weight to 6 parts by weight of a cyclic phosphazene compound flame retardant; (C) 0.1 parts by weight to 5 parts by weight of an impact-reinforcing agent; and (D) 1 part by weight to 3 parts by weight of a fluorinated polyolefin.

Abstract: A thermally-conductive resin composition according to the present invention comprises: approximately 10-50 wt % polycarbonate resin; approximately 1-10 wt % glycol-modified polyester resin; approximately 1-15 wt % glass transition temperature depressing agent; approximately 5-20 wt % additive for laser direct structuring; approximately 10-35 wt % boron nitride having average particle size (D50) of approximately 10 ?m or greater; and approximately 10-30 wt % glass fiber having a non-circular cross-sectional surface.

Abstract: A thermoplastic resin composition of the present invention comprises: a base resin comprising a rubber modified vinyl-based graft copolymer, a large-diameter rubbery polymer having an average particle size of approximately 3,000-8,000 nm, and an aromatic vinyl-based copolymer resin; and zinc oxide having an average particle size of approximately 0.5-3 ?m and a specific surface area BET of approximately 1-10 m2/g. The thermoplastic resin composition has an excellent low gloss property, antibacterial property and the like.

Abstract: A thermoplastic resin composition and a molded article formed of the same includes: about 100 parts by weight of a polycarbonate resin; about 1 to about 20 parts by weight of a rubber modified aromatic vinyl copolymer resin; about 0.1 to about 2 parts by weight of a maleic anhydride modified olefin copolymer; and about 0.1 to about 2 parts by weight of a phosphite compound represented by Formula 1 as described in the present specification. The thermoplastic resin composition can have good properties in terms of chemical resistance, impact resistance, and balance therebetween.

Abstract: Provided are resin composition and a molded product manufactured therefrom. The resin composition includes (A) a polycarbonate resin; (B) a rubber-modified vinyl-based graft copolymer; (C) a rubber-modified vinyl-based copolymer; (D) a vinyl-based copolymer including an epoxy group; and (E) a compound represented by Chemical Formula 1. (R1)a(R2)b(R3)c—Si—(OR4)4-a-b-c??[Chemical Formula 1] In Chemical Formula 1, each substituent is the same as that defined in the specification.

Abstract: A thermoplastic resin composition of the present invention comprises: (A) 100 parts by weight of a thermoplastic resin comprising (A1) a rubber-modified aromatic vinyl-based graft copolymer, (A2) an aromatic vinyl-based copolymer resin having a flow index of about 5 g/10 min to about 8 g/10 min as measured by the ASTM D 1238 standard, and (A3) an ?-methylstyrene copolymer; and (B) about 0.1 to about 10 parts by weight of zinc oxide, wherein the zinc oxide has a size ratio (B/A) of peak A in the region of 370 nm to 390 nm to peak B in the region of 450 nm to 600 nm of about 0.01 to about 1 in photoluminescence measurement, and has a BET surface area of about 10 m2/g or less as measured by a BET analyzer.

Abstract: A thermoplastic resin composition and a molded article formed of the same. The thermoplastic resin composition includes: a polycarbonate resin; an aromatic vinyl copolymer resin; mica having an average particle diameter of about 200 ?m to about 400 ?m; a modified polyolefin; and a phosphorus flame retardant, wherein the modified polyolefin includes a first modified polyolefin including a repeat unit represented by Formula 1 and a repeat unit represented by Formula 2 as defined in the specification and a second modified polyolefin including the repeat unit represented by Formula 1 and a repeat unit represented by Formula 3 as also defined in the specification. The thermoplastic resin composition can have good properties in terms of rigidity, impact resistance, heat resistance, flame resistance, and balance therebetween.

Abstract: Provided are a thermoplastic resin composition including 100 parts by weight of a base resin including (A-1) a polycarbonate resin, (A-2-1) a first acrylonitrile-butadiene-styrene graft copolymer including a rubber polymer having an average particle diameter of 200 nm to 400 nm and an acrylonitrile-butadiene-styrene copolymer comprising (A-2-2) a second acrylonitrile-butadiene-styrene graft copolymer including a rubber polymer having an average particle diameter of 400 nm to 600 nm, and (A-3) an aromatic vinyl compound-vinyl cyanide compound copolymer; (B) 1 to 10 parts by weight of a crosslinked styrene-acrylonitrile copolymer; and (C) 5 to 15 parts by weight of a flame retardant, and a molded article using the same.

Abstract: A thermoplastic resin composition includes: about 100 parts by weight of a thermoplastic resin including about 35 wt % to about 55 wt % of a polycarbonate resin, about 3 wt % to about 9 wt % of a first rubber-modified aromatic vinyl graft copolymer, about 7 wt % to about 13 wt % of a second rubber-modified aromatic vinyl graft copolymer, and about 30 wt % to about 50 wt % of an aromatic vinyl copolymer resin; about 6 to about 13 parts by weight of a halogen compound; and about 8 to about 17 parts by weight of a phosphoric ester compound. The first rubber-modified aromatic vinyl graft copolymer is obtained by graft copolymerization of an alkyl(meth)acrylate, an aromatic vinyl monomer and a copolymerizable monomer to a rubber polymer, and the second rubber-modified aromatic vinyl graft copolymer is obtained by graft copolymerization of an aromatic vinyl monomer and a copolymerizable monomer to a rubber polymer.