Abstract: A method for manufacturing rolled steel products, especially of threaded tension steels or the like, is described, in accordance with which the steel with a C-content of 0.50 to 0.80 W %, a Si-content of 0.20 to 0.60 W %, and a Mn-content of 0.30 to 0.80 W %, after hot rolling is surface quenched by means of cooling from the rolling heat at the output side of the finishing equipment so that the material in a peripheral zone is immediately and entirely converted to martensite, while the heat which remains in the core zone during the subsequent cooling effects an annealing the martensitic peripheral zone not beyond the range of the intermediate stage, and which in accordance with the invention is characterized in that after the cooling a cold working follows, and then an annealing. The total reduction amounts preferably to 0.5 to 1.5%; the annealing is preferably carried out at a temperature in the range of 350.degree. C. to 380.degree. C. and during a period of maximum temperature of 5 to 60 seconds.