Abstract: The present invention discloses a low density basic refractory lining material with improved resistance to corrosion by molten slag and metal that is especially adapted for use as a disposable liner in molten metal containing vessels. This material incorporates hollow ceramic microspheres of alumina, silica or mixtures thereof, having diameters of between about 5 and 500 microns as a density reducing material. This material may also include a stiffening agent, a set retarding agent, a foaming agent to further reduce the density, a plasticizer, and a low temperature binder. The addition of the ceramic microspheres has been found to provide reduced open porosity, improving resistance to corrosion. Also, the invention relates to methods for applying the disposable lining and vessels which include the lining applied thereon.

Abstract: A dry vibratable substantially alkali free refractory composition is disclosed for use as a disposable liner wherein the combination of a powdered metal utilized as a high temperature binder and an organic material utilized as a low temperature binder obviates the use of alkali oxides which previously caused degradation of the permanent refractory liner materials upon which the disposable lining was placed. Low density materials such as expanded inorganic materials can be added to the disclosed compositions to decrease the density. The invention also relates to a method of providing a disposable lining in a vessel having a permanent refractory lining, and to the resulting vessel thereof.

Abstract: A refractory composition, particularly for application as a dry vibratable refractory for forming the wearable, disposable monolithic lining coating the permanent lining of a tundish or ladle used in molten metal casting processes is disclosed. The composition contains a refractory aggregate, a first bonding agent actuatable at temperatures in the range of from about 300.degree. F. to about 1000.degree. F. to cause the formation of interparticle bonds between aggregate particles, at least one second bonding agent actuatable at temperatures in the range of from about 1000.degree. F. to about 2500.degree. F. to cause further formation of interparticle bonds between aggregate particles, and, optionally, clay. The use of both first and second bonding agents enables installation of the refractory in hot practice, in which vessel preheat temperatures of up to about 2500.degree. F. are utilized.