Abstract: Disclosed herein are a polyamide filament comprising a polyamide resin composition which comprises an aromatic polyamide resin (A) produced by polymerizing a monomer containing not less than 85 wt % of an aromatic polyamide component composed of terephthalic acid, isophthalic acid and aliphatic diamine, and an aliphatic polyamide resin (B), and having a heat-shrinkage in boiling water of not less than 20%, and a process for producing the same.

Abstract: A process for producing a sucrose fatty acid polyester comprises reacting sucrose with fatty acid lower alcohol ester(s) in a solvent in the presence of an alkaline catalyst, wherein said fatty acid lower alcohol ester(s) are employed in an amount at least 5 times by mol as much as said sucrose. The alkaline catalyst component is removed from the reaction product thus obtained and the obtained sucrose fatty acid polyester-containing solution is catalytically treated with activated clay. This process enables the production of a sucrose fatty acid polyester containing an extremely small amount of ash components and having an extremely low color value. The alkaline catalyst used in this process may be recovered and reused, which further makes the process of the present invention advantageous.

Abstract: A process for producing crosslinked polymer particles which comprises a first step of polymerizing a polymerizable monomer containing from 0.1 to 2.0% by weight, based on the entire polymerizable monomer, of a crosslinkable monomer in a medium in which the polymerizable monomer is soluble but the resulting polymer is insoluble, to obtain crosslinked polymer particles having a particle size of from 0.8 to 10 .mu.m, and a second step of letting the crosslinked polymer particles absorb from 1 to 50 times by weight of a polymerizable monomer containing from 2 to 100% by weight, based on the entire polymerizable monomer, of a crosslinkable monomer in an aqueous medium, followed by polymerization to obtain crosslinked polymer particles having a particle size of from 1 to 30 .mu.m and a crosslinking degree of from 1.