Abstract: The present invention relates to a hydraulic binder system based on calcined aluminum oxide for use in refractory materials. The invention further relates to a process for producing the hydraulic binder system and also to the use thereof.

Abstract: The invention relates to a process for the milling-drying of a raw mixture containing aluminum trihydroxide having an average particle size D50 in the range from 50 to 130 ?m and a specific BET surface area in the range from 0.01 to 0.5 m2/g and containing from 0.1 to 20% by weight of water, based on the raw mixture, which including the steps i) introduction of the raw mixture into a milling-drying apparatus, ii) introduction of a hot air stream having a temperature in the range from 20 to 100° C. into the milling-drying apparatus so as to flow through the milling-drying apparatus and iii) comminution of the aluminum trihydroxide present in the raw mixture in the milling-drying apparatus.

Abstract: The present invention relates to a stabilizer system for halogenated polymers comprising, as component (A), calcium monocarbonatohydroxodialuminate of the formula (A) CamAl2(OH)6+2(m-1)CO3*nH2O??(A), where m=from 3.8 to 4.2, and n=from 0 to 3, and, as component (B), a catena-2,2?,2?-nitrilotrisethanolperchloratolithium or -sodium coordination polymer (B1) with a monomer unit of the formula where Mt=Li or Na, An=OClO3 and q=1, and/or a quaternary or ternary ammonium or phosphonium perchlorate (B2). The present invention further relates to compositions and articles comprising these stabilizer systems, and to the use of the systems and compositions.

Abstract: Neutral calcium-aluminum double salts of the formula (A): Ca2m(Zn2n)Al2(OH)6+2(2m+2n?1)An*oH2O??(A), where the following apply for m and n:m=0.5 to 3 and 0.5m?n>0; An=CO3, where this may be replaced completely or partially by at least one of the following groups selected from OH, ClO4 and H3CS(?O)2O (triflate) and o=0 to 3. The present invention further relates to their preparation, use in compositions and stabilizer systems and uses thereof.

Abstract: Method for the production of a finely crystalline boehmite and application of said boehmite as flame retardant in plastics. The method involves mixing aluminum monohydrate with a boehmite crystal structure in water to form an aqueous dispersion of said aluminum monohydrate in said water, and then grinding the dispersion while maintaining the dispersion in a pH range of 2 to 4 and forming boehmite seed crystals. The boehmite seed crystals can then optionally be mixed with a hydrate and a basic aqueous solution to form a dispersion which may be heated to convert at least a substantial portion of the aluminum monohydrate to boehmite.

Abstract: A process is provided for preparing calcium carbonate hydroxodialuminates which have a hexagonal platelet-shaped crystal habit and are of the formula (A): CamAl2(OH)6+2(m?1)An*nH2O??(A) where m=3.5 to 4.5 and An=carbonate which may be partly replaced by perchlorate and/or trifluoromethanesulfonate (triflate) and n=0 to 6, comprising the steps of reacting calcium oxide or calcium hydroxide with optionally activated aluminum oxohydroxide or aluminum hydroxide and simultaneously or subsequently with a carbonate source consisting of carbon dioxide or alkali metal (bi)carbonate and optionally further reacting the product obtained in step (a) with perchloric acid and/or trifluoromethanesulfonic acid or optionally calcining the product obtained in step (a) at 200° C. to 900° C. and subsequently exchanging ions in the presence of a perchlorate and/or triflate salt, optionally in the presence of alkali metal (bi)carbonate, in water.