Abstract: A damper spring having an excellent fatigue limit is provided. A damper spring according to the present embodiment includes a nitrided layer formed in an outer layer, and a core portion that is further inward than the nitrided layer. The chemical composition of the core portion consists of, in mass %, C: 0.53 to 0.59%, Si: 2.51 to 2.90%, Mn: 0.70 to 0.85%, P: 0.020% or less, S: 0.020% or less, Cr: 1.40 to 1.70%, Mo: 0.17 to 0.53%, V: 0.23 to 0.33%, Cu: 0.050% or less, Ni: 0.050% or less, Al: 0.0050% or less, Ti: 0.050% or less, N: 0.0070% or less, and Nb: 0 to 0.020%, with the balance being Fe and impurities. In the core portion, a number density of V-based precipitates having a maximum diameter ranging from 2 to 10 nm is 500 to 8000 pieces/?m2.

Abstract: A valve spring includes a nitrided layer, and a core portion that is further inward than the nitrided layer. A chemical composition of the core portion consists of, in mass %, C: 0.53 to 0.59%, Si: 2.51 to 2.90%, Mn: 0.70 to 0.85%, P: 0.020% or less, S: 0.020% or less, Cr: 1.40 to 1.70%, Mo: 0.17 to 0.53%, V: 0.23 to 0.33%, Ca: 0.0001 to 0.0050%, Cu: 0.050% or less, Ni: 0.050% or less, Al: 0.0050% or less, Ti: 0.050% or less, and N: 0.0070% or less, with the balance being Fe and impurities. In the core portion, a number density of V-based precipitates having a maximum diameter ranging from 2 to 10 nm is 500 to 8000 per ?m2, and in the core portion, a numerical proportion of Ca sulfides with respect to a total number of oxide-based inclusions and sulfide-based inclusions is 0.20% or less.

Abstract: A steel wire which has an excellent fatigue limit when made into a spring is provided. A chemical composition of the steel wire according to the present embodiment consists of, in mass %, C: 0.53 to 0.59%, Si: 2.51 to 2.90%, Mn: 0.70 to 0.85%, P: 0.020% or less, S: 0.020% or less, Cr 1.40 to 1.70%, Mo: 0.17 to 0.53%, V: 0.23 to 0.33%, Cu: 0.050% or less, Ni: 0.050% or less, Al: 0.0050% or less, Ti: 0.050% or less, N: 0.0070% or less, Ca: 0 to 0.0050%, and Nb: 0 to 0.020%, with the balance being Fe and impurities. In the steel wire, a number density of V-based precipitates having a maximum diameter ranging from 2 to 10 nm is 500 to 8000 pieces/?m2.