Abstract: A method of manufacturing a vinyl chloride-coated steel sheet involving the steps of coating electron ray curable adhesives on the surface of the thin metal sheet, such as a zinc plated steel sheet or cold rolled steel sheet, laminating a vinyl choride film of decorative and corrosion resistant protecting property to the coated surface and irradiating electron rays the upper surface of the coated sheet with thereby bonding the film with the metal sheet as raw material, wherein the vinyl chloride film is formed by applying a calendering or extruding process to a blend including a vinyl chloride resin obtained by suspension polymerization and, from 20 to 40 parts by weight of a plasticizer, dialkyl tin mercaptide type stabilizer, an acryl oligomer type lubricant and, optionally, pigments and other ingredients.

Abstract: A method of treating waste produced during stainless steel making is disclosed. The method comprises the steps of kneading a sludge cake with a mixture of dust and scale to obtain a kneaded mass, adding an organic binder and eventually adding water with an inorganic binder to said kneaded mass, shaping said kneaded mass into a briquette, and heating said briquette at a low temperature. The briquette obtained can be used as a ferroalloy making raw material.Metal oxides contained in the briquette are reduced by a dry reduction refining added with a carbonaceous reducing agent and eventually with a flux to separate usable metals.