Abstract: The present disclosure relates to an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: Disclosed are a pressure vessel steel sheet and a method for manufacturing the same, the steel sheet comprising: by wt %, 0.10-0.20% of C, 0.15-0.40% of Si, 1.15-1.50% of Mn, 0.45-0.60% of Mo, 0.03-0.30% of Cu, 0.025% or less of P, 0.025% or less of S and 0.005-0.06% of sol. Al; two or more selected from the group consisting of 0.03-0.30% of Cr, 0.002-0.025% of Nb and 0.002-0.025% of Zr, and the balance of Fe and inevitable impurities, wherein the structure comprises a mixture structure of ferrite, perlite and tempered bainite after post weld heat treatment (PWHT) for 60 hours at 600-660° C., and the area fraction of the tempered bainite is at least 10% (excluding 100%).

Abstract: An annealing separator composition for a grain-oriented electrical steel sheet according to an embodiment of the present invention includes: 100 parts by weight of at least one of a magnesium oxide and a magnesium hydroxide; and 30 to 250 parts by weight of a metal hydroxide including at least one of a nickel hydroxide and a cobalt hydroxide, wherein an average particle diameter of the metal hydroxide is 0.01 to 80 ?m.

Abstract: A method for monitoring a state of wearing safety protective equipment according to an embodiment includes receiving an image from a site monitoring device installed at an operation site determining whether a work performed in a monitoring area corresponds to a dangerous work by analyzing the image; detecting a target worker and a body area of the target worker when it is determined that the work corresponds to the dangerous work as a result of determining whether the work performed in the monitoring area corresponds to the dangerous work; determining a type of safety protective equipment required for the target worker; and determining the state of the target worker wearing the safety protective equipment.

Abstract: Provided is a high strength steel sheet having an excellent high-temperature elongation characteristic. The sheet includes, by weight %, 0.4-0.9% of C, 0.01-1.5% of Cr, 0.03% or less (exclusive of 0%) of P, 0.01% or less (exclusive of 0%) of S, 0.01% or less (exclusive of 0%) of N, 0.01% or less (exclusive of 0%) of sol. Al, and a balance of Fe and inevitable impurities, and comprises at least one among 2.1% or less (exclusive of 0%) of Mn and 1.6% or less (exclusive of 0%) of Si; the sheet has a microcrystalline structure including pearlite having an area fraction of 80% or more and ferrite having an area fraction of 20% or less; and the pearlite includes cementite having a major axis length of 200 nm or shorter.

Abstract: The purpose of one aspect of the present disclosure is to provide: a cold rolled steel sheet for a flux-cored wire, having excellent low temperature toughness, welding workability and processability; and a manufacturing method thereof. One embodiment of the present disclosure provides: a cold rolled steel sheet for a flux-cored wire, comprising, by wt %, 0.005-0.10% of C, 0.05-0.25% of Mn, 0.05% or less of Si (excluding 0%), 0.0005-0.01% of P, 0.008% or less of S (excluding 0%), 0.005-0.06% of Al, 0.0005-0.003% of N, 0.8-1.7% of Ni, 0.1-0.5% of Cr, and a balance of Fe and inevitable impurities, and having 0.10-0.75 of WN defined by Relationship 1 below; and a manufacturing method therefor. WN=(31×C+0.5×Mn+20×Al)×(Ni)×(0.6×Cr).

Abstract: The present invention relates to a composition for forming an insulation coating film of an oriented electrical steel sheet, including a first component (A) including a composite metal phosphate, a derivative thereof, or a mixture thereof, and a second component (B) including at least two colloidal silicas having different average particle diameters, a method for forming an insulation coating film using the same, and an oriented electrical steel sheet having an insulation coating film formed thereon.

Abstract: A grain-oriented electrical steel sheet according to an embodiment of the present includes Si at 1.0 wt % to 7.0 wt %, C at 0.005 wt % or less (excluding 0 wt %), In at 0.001 wt % to 0.5 wt %, and the remainder including Fe and other impurities unavoidably added thereto.

Abstract: The hot-rolled coated steel sheet comprising: in wt %, C: 0.05-0.14%, Si: 0.1-1.0%, Mn: 1.0-2.0%, P: 0.001-0.05%, S: 0.001-0.01%, AI: 0.01-0.1%, Cr: 0.005-1.0%, Ti: 0.005-0.13%, Nb: 0.005-0.03%, N: 0.001-0.01%, Fe residues, and other inevitable impurities; a mixed structure of ferrite and bainite as a main phase; and as a remaining structure, one or more selected from the group consisting of martensite, austenite, and phase martensite (MA), wherein a fraction of the ferrite and bainite is 95-99 area % and Equation 1 is satisfied. [Equation 1] FCO{110}<112>+FCO{112}<111>?10 where, FCO{110}<112> and FCO{112}<111>, each representing an area fraction occupied by a structure having ac crystal orientation of {110}<112> and {112}<111>.

Abstract: The present disclosure provides a hot-press formed part comprising a plated steel sheet and an aluminum alloy plated layer formed on the plated steel sheet, wherein the aluminum alloy plated layer comprises: an alloying layer (I) formed on the plated steel sheet and containing, by weight %, 5-30% of Al; an alloying layer (II) formed on the alloying layer (I) and containing, by weight %, 30 to 60% of Al; an alloying layer (III) formed on the alloying layer (II) and containing, by weight %, 20-50% of Al and 5-20% of Si; and an alloying layer (IV) formed continuously or discontinuously on at least a part of the surface of the alloying layer (III), and containing 30-60% of Al, wherein the rate of the alloying layer (III) exposed on the outermost surface of the aluminum alloy plated layer is 10% or more.

Abstract: An method of manufacturing a hot press-formed member comprises heating a blank of an aluminum-based plated steel sheet in a heating furnace, removing the heated blank from the heating furnace and conveying the removed blank between an upper mold portion and a lower mold portion of a mold, mounted on a press, to be seated; and performing a forming process after the upper mold portion of the mold is in contact with the seated blank.

Abstract: The present invention relates to an automotive steel sheet and, more specifically, provides: an ultrahigh-strength and high-ductility steel sheet ensuring ultrahigh strength and high ductility and, simultaneously, having excellent cold formability due to a high yield strength ratio, and improved collision characteristics.

Abstract: The present disclosure relates to an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: The present invention relates to a method for producing lithium phosphate, comprising: passing a lithium-containing solution through an aluminum-based adsorbent to adsorb lithium on the aluminum-based adsorbent, passing the distilled water or an aqueous solution having a lower lithium concentration than the lithium-containing solution through the aluminum-based adsorbent on which the lithium is adsorbed to obtain a lithium-containing desorption solution, and putting a phosphorous supplying material in the lithium-containing desorption solution to obtain lithium phosphate.

Abstract: Disclosed are a high-strength ultra-thick steel material and a method for manufacturing same. The high-strength ultra-thick steel material comprises in weight % 0.04-0.1% of C, 0.05-0.5% of Si, 0.01-0.05% of Al, 1.6-2.2% of Mn, 0.5-1.2% of Ni, 0.005-0.050% of Nb, 0.005-0.03% of Ti and 0.2-0.6% of Cu, 100 ppm or less of P and 40 ppm or less of S with a balance of Fe, and inevitable impurities, and comprises, in a subsurface area up to t/10 (t hereafter being referred to as the thickness of the steel material), bainite of 90 area % or greater (including 100 area %) as microstructures. And the particle size of crystallites having a high inclination angle boundary of 15° or higher measured by EBSD is 10 ?m or less (not including 0 ?m).

Abstract: The purpose of one aspect of the present invention is to provide: a thick steel plate capable of removing a conventional normalizing treatment required for ensuring toughness low temperature and cryogenic environments, and having properties equal to or better than those of a conventional steel subjected to the normalizing treatment; and a method for manufacturing the method.

Abstract: Provided is a multilayer zinc alloy plated steel material comprising a base steel material and multiple plating layers formed on the base steel material, wherein each of the multiple plating layers includes one of a Zn plating layer, a Mg plating layer, and a Zn—Mg alloy plating layer, and the ratio of the weight of Mg contained in the multiple plating layers to the total weight of the multiple plating layers is from 0.13 to 0.24.

Abstract: Provided are: a SOUR-resistant heavy-wall steel plate having excellent low-temperature toughness and post-heat treatment characteristics; and a method for manufacturing the same. The SOUR-resistant heavy-wall steel plate of the present invention comprises: in terms of weight %, 0.02-0.06% of C; 0.5% or less of Si (excluding 0%); 0.8-2.0% of Mn; 0.03% or less of P; 0.003% or less of S; 0.06% or less of Al; 0.01% or less of N; 0.005-0.1% of Nb; 0.005-0.05% of Ti; 0.0005-0.005% of Ca; one or more selected from 0.05-0.5% of Ni, 0.05-0.5% of Cr, 0.02-0.4% of Mo, and 0.005-0.1% of V; and the remainder Fe and unavoidable impurities, wherein the heavy-wall steel plate satisfies relational expressions 1-3, and has a percent ductile fracture of 85% or more in the drop weight tear test (DWTT) at ?20° C.

Abstract: The present disclosure relates to a plated steel material that can be used in an automobile, a household appliance, a building material, and the like, and more particularly, to a zinc alloy plated steel material having excellent surface quality and corrosion resistance, and a method for manufacturing the same.

Abstract: The present invention relates to a steel material used for a line pipe for transporting crude oil or natural gas and the like and, more specifically, to a steel material for a welded steel pipe, having excellent longitudinal uniform elongation for the pipe, a manufacturing method therefor, and a steel pipe using the same.