Abstract: Process for distillatively purifying polymerizable compounds using a high-boiling, inert, thermally long-term-stable substance as a boiling oil, characterized in that the boiling oil is disposed in the bottom of a rectification column.

Abstract: The present invention relates in general terms to a process for preparing acetone cyanohydrin, comprising as steps: A. contacting acetone and hydrocyanic acid in a reactor to give a reaction mixture, the reaction mixture being circulated, to obtain acetone cyanohydrin; B. cooling at least some of the reaction mixture by flowing it through a cooling region of a cooler, the cooler including one cooling element or at least two cooling elements; C.

Abstract: The invention relates in general terms to a process for preparing to a process for purifying an alkyl methacrylate, comprising the steps of: A. providing an alkyl methacrylate with an impurity: B. adsorbing at least some of the impurity onto a purifying solid to obtain an ultrapure alkyl methacrylate, to a process for preparing an ultrapure alkyl methacrylate, to an apparatus for preparing alkyl methacrylates, to a process for preparing a polymer based at least partly on alkyl methacrylates, to the use of an alkyl methacrylate obtained according to the invention in chemical products, and to chemical products comprising an alkyl methacrylate obtained according to the invention.

Abstract: A method for producing a swellable polymer by polymerizing a composition containing at least one polyalkylene glycol di(meth)acrylate having a weight-average molecular weight from 2500 g/mol to 10000 g/mol, wherein the polymer contains at least 50.0% by weight based on the total weight of the polymer of said at least one polyalkylene glycol di(meth)acrylate.

Abstract: Flame-retardant plastics mouldings composed of polyphenyl sulphones (PPSUs) or of polycarbonates (PCs) are coloured with Iridoin® pigments in such a way as to have a metallic effect. The effect is resistant to the usual stresses present in an aircraft cabin and complies with the respective fire-protection requirements.

Abstract: Composition containing, based in each case on its total weight, A) 50.0% by weight to 99.5% by weight of at least one (meth)acrylate (co)polymer and B) 0.5% by weight to 50.0% by weight of at least one copolymer obtainable by polymerization of a monomer mixture comprising i. 70% by weight to 92% by weight of a vinylaromatic monomer and ii. 8% by weight to 30% by weight of acrylonitrile or methacrylonitrile or mixtures thereof and iii. 0% by weight to 22% by weight of at least one further monomer, the composition having a haze according to ASTM D1003 of less than 2.0% at 23° C. and a haze according to ASTM D1003 of less than 4.0% at 40° C. and the composition containing at least one (meth)acrylate (co)polymer a) having a solution viscosity in chloroform at 25° C. (ISO 1628—part 6) of greater than 55 ml/g. The moldings obtainable from the composition are distinguished in particular by improved stress cracking resistance and are suitable in particular for coverings, finishes or films.

Abstract: The present invention relates to an aqueous dispersion comprising at least one alkyd resin and at least one addition polymer having at least one (meth)acrylate segment which comprises 1% to 30% by weight of units derived from (meth)acrylates which in the alkyl radical have at least one double bond and 8 to 40 carbon atoms, 0.1% to 10% by weight of units derived from monomers containing acid groups, and 50% to 98.9% by weight of units derived from (meth)acrylates having 1 to 6 carbon atoms in the alkyl radical, based on the weight of the (meth)acrylate segment.

Abstract: The present invention relates to a process for preparing (meth)acrylic acid, characterized in that a cyclic ester is converted to (meth)acrylic acid in the presence of a catalyst. The (meth)acrylic acid prepared can in particular be converted to (meth)acrylates.

Abstract: The present invention describes a process for the surface finishing of materials via application of specific polymethacrylate layers. The polymethacrylate layers are composed of blends of at least two (co)polymers of polymethacrylates, and specific “reactive monomers” are present here in a polymerized mixture which forms the polymethacrylate layer. At the application temperature established, these form a chemical and, where appropriate, also a physical bond to the substrate, and therefore have adhesion-promoting action.

Abstract: The use of polymeric microparticles having a cavity in hydraulically setting building material mixtures is described, from 1 to 100% by volume of the cavity of these microparticles being filled with water. In this way, remarkable concrete resistance to the freezing and thawing cycle is achieved, these microparticles providing improved protection for the concrete from the effects of the freezing and thawing cycle, even at a diameter of from 0.1 to 1 ?m and in doses which are 1 to 2 orders of magnitude lower than those described in the prior art. Moreover, the compressive strength of the correspondingly hardened concrete is substantially improved, which was likewise not foreseeable.

Abstract: The invention relates to a composition containing, in relation to the total weight of said composition, A) between 50.0% by weight and 99.5% by weight of at least one (meth)acrylate (co)polymer and B) between 0.5% by weight and 50.0% by weight of at least one copolymer, obtained by the polymerization of a monomer mixture consisting of i. between 70% by weight and 92% by weight of a vinyl aromatic monomer and ii. between 8% by weight and 30% by weight of acryl nitrile or methacryl nitrile or mixtures thereof iii. between 0% by weight and 22% by weight of at least one other monomer, the composition having at 50° C. a ?E of less than 0.15, ?E being defined according to the relationship (1): (1) in which ?L*: the modification of the color co-ordinates L* compared with the color co-ordinates L* at 23° C., ?a*: the modification of the color co-ordinates a* compared with the color co-ordinates a* at 23° C., ?b*: the modification of the color co-ordinates b* compared to the color co-ordinates b* at 23° C.

Abstract: The invention describes an emulsion polymer which can be obtained by polymerization of a mixture comprising a) from 5 to 99.9% by weight of one or more monomers having a solubility in water of <2% by weight at 20° C. and selected from the group consisting of monofunctional (meth)acrylate monomers, styrene and vinyl esters; b) from 0 to 70% by weight of one or more monomers which can be copolymerized with the monomers a); c) from 0 to 20% by weight of one or more doubly or multiply vinylically unsaturated compounds; d) from 0 to 20% by weight of one or more polar monomers having a solubility in water of >2% by weight at 20° C.; and e) 0.

Abstract: The present invention relates to the in situ acid end group functionalization of polymer chains which have been prepared by means of atom transfer radical polymerization, and to the simultaneous removal of transition metals from polymer solutions.

Abstract: The present invention relates in general terms to a process for preparing acetone cyanohydrin, comprising as steps: A. contacting acetone and hydrocyanic acid in a reactor to give a reaction mixture, the reaction mixture being circulated, to obtain acetone cyanohydrin; B. cooling at least some of the reaction mixture; C. discharging at least a portion of the acetone cyanohydrin obtained from the reactor; D. continuously distilling the discharged acetone cyanohydrin obtained to obtain an acetone cyanohydrin bottom product and an acetone top product in a distillation column; E. recycling at least a portion of the acetone top product into step A, the acetone top product being kept at less than 60° C.

Abstract: The invention relates to a process for preparing acetone cyanohydrin and to a process for preparing alkyl methacrylates, in which an acetone cyanohydrin as can be prepared in accordance with the present invention is used.

Abstract: The invention relates to a method for producing meth)acrylate-based ABA triblock copolymers in which the A blocks are amine-functionalized.

Abstract: The invention relates to a method for producing a thermoplastic plastic film. According to said method, the thermoplastic plastic is melted and transported in an extrusion installation comprising an extruder, an extrusion nozzle with a wide-slot delivery opening and a chill roll, which is fixed to a roll system and then leaves the delivery opening of the extrusion nozzle in the form of a flat melted web. Said melted web is then applied to the chill roll and is cooled. The invention is characterised in that it uses an extrusion installation, in which the distance between the delivery opening of the extrusion nozzle and the surface of the cooled roll does not vary by more than +/?50 ?m during the operating time. The invention also relates to a film of this type and to uses of the latter.

Abstract: The invention relates to a heat-sealable coating system suitable for the sealing of various types of substrate and comprising a film-forming dispersion, characterized in that a polymer type A is present and is a polyester or a polyester mixture, a polymer type B is present and is a (meth)acrylate homo- or/and copolymer, containing standard methacrylates and/or standard acrylates, and a polymer type AB is present and is a graft copolymer composed of polymer type A and polymer type B, and if appropriate a polymer type C is present and is an olefin polymer or is an olefin copolymer, and a polymer type CB is present and is a graft polymer composed of polymer type C and polymer type B, and also if appropriate a polymer type D and/or a polymer type DA is present.

Abstract: The invention relates to a controlled release pharmaceutical composition, comprising a core, comprising a pharmaceutical active ingredient, whereby the core is coated by an ethanol resistance conferring coating layer which has the effect of conferring the release profile of the pharmaceutical active ingredient to be resistant against the influence of ethanol. The coating layer comprises a polymeric portion consisting of a water-insoluble neutral vinyl polymer or vinyl copolymer and an amino methacrylate copolymer and an excipients portion consisting of a lubricant, an emulsifier, a plasticizer and optionally a cellulosic compound.

Abstract: The invention relates to a novel halogen-free and acid-free, readily soluble adhesion promoter for polyolefins, said promoter containing (meth)acrylate-grafted, amorphous polyolefins.