Abstract: A high critical temperature and high critical current density superconductor is disclosed which contains a metal oxide expressed by the following formula (I):(R.sup.1.sub.1-x, Ba.sub.x)Ba.sub.2 Cu.sub.3 O.sub.d (I)wherein R.sup.1 stands for at least one element selected from the group consisting of La, Nd, Sm, Eu and Gd, x is a number greater than 0 but not greater than 0.5 and d is a number between 6.2 and 7.2. Fine phases of RE211, RE422 and/or a metal oxide expressed by the formula (R.sup.2.sub.1-z, Ba.sub.z) (Ba.sub.1-y, R.sup.2.sub.y).sub.2 Cu.sub.3 O.sub.p (R.sup.2 =La, Nd, Sm, Eu or Gd) may be dispersed in a matrix of the matrix phase of the formula (I). The above superconductor may be obtained by cooling a melt having a temperature of 1,000.degree.-1,300.degree. C. and containing R.sup.1, Ba, Cu and O at a cooling rate of 5.degree. C./hour or less under a partial pressure of oxygen of between 0.00001 and 0.05 atm, followed by annealing at 250.degree.-600.degree. C. in an oxygen atmosphere.

Abstract: A high critical temperature and high critical current density superconductor is disclosed which contains a metal oxide expressed by the following formula (I):(R.sup.1.sub.1-x,Ba.sub.x)Ba.sub.2 Cu.sub.3 O.sub.d (I)wherein R.sup.1 stands for at least one element selected from the group consisting of La, Nd, Sm, Eu and Gd, x is a number greater than 0 but not greater than 0.5 and d is a number between 6.2 and 7.2. Fine phases of RE211, RE422 and/or a metal oxide expressed by the formula (R.sup.2.sub.1-z, Ba.sub.z) (Ba.sub.1-y, R.sup.2.sub.y).sub.2 Cu.sub.3 O.sub.p (R.sup.2 =La, Nd, Sm, Eu or Gd) may be dispersed in a matrix of the matrix phase of the formula (I). The above superconductor may be obtained by cooling a melt having a temperature of 1,000.degree.-1,300.degree. C. and containing R.sup.1, Ba, Cu and O at a cooling rate of 5.degree. C./hour or less under a partial pressure of oxygen of between 0.00001 and 0.05 atm, followed by annealing at 250.degree.-600.degree. C. in an oxygen atmosphere.