Abstract: A (per)fluoroelastomeric composition curable by peroxidic way comprising: 100 phr as (per)fluoroelastomer as filler, 0.5-50 phr of silica having a pH value, determined according to the DIN ISO 787-9 standard, higher than 7, preferably higher than 8, as crosslinking agent, from 0.5 to 10 phr of a bis-olefin having general formula: wherein: R1, R2, R3, R4, R5, R6, equal to or different from each other, are H or C1-C5 alkyls; Z is selected between a C1-C18 linear or branched alkylene or cycloalkylene radical, optionally containing oxygen atoms, preferably at least partially fluorinated, or a (per)fluoropolyoxyalkylene radical.

Abstract: The invention pertain to a process for purifying a fluoropolymer dispersion, said process comprising: (i) providing an aqueous dispersion (D) of at least one fluoropolymer [polymer (F)] comprising at least one fluorinated surfactant [surfactant (FS)], having a solids content (SC) of 15% by weight or more; (ii) adding to said aqueous dispersion (D) at least one non-ionic non-fluorinated surfactant [surfactant (NS)]; (iii) adjusting said solid content (SC) to less than 10% by weight, to obtain a diluted aqueous dispersion (dD); (iv) contacting said diluted aqueous dispersion (dD) with at least one adsorbing material, so as to obtain an aqueous dispersion of polymer (F) having a content of the fluorinated surfactant (FS) of less than 1 ppm based on the total weight of solids. Still an object of the invention is an aqueous fluoropolymer dispersion comprising less than 1 ppm of fluorinated surfactant.

Abstract: Fluoroelastomers, curable by peroxidic route, obtainable by polymerizing the following monomers: a) C2-C8 hydrogenated fluoroolefins; b) fluorovinylethers of general formula: CFX?CXOCF2OR ??(I) c) bis-olefins having general formula: RI1RI2 C?CRI3-Z-CRI4?CRI5RI6??(IA) and optionally: d) one or more fluorinated olefinic comonomers selected from perfluoroalkylvinylethers (PAVE) CF2?CFOR2f, perfluorooxyalkylvinylethers CF2?CFOXa, e) C2-C8 perfluorolefins; f) one or more C2-C8 non fluorinated olefinic comonomers said fluoroelastomers comprising iodine and/or bromine atoms in the chain and/or in end position.

Abstract: A process for preparing fluorovinylethers having general formula: RfO—CF?CF2??(IA) wherein Rf is a fluorinated or perfluorinated alkyl or cycloalkyl substituent; comprising the following reaction steps: 1) reaction of a hypofluorite; 2) dehalogenation or dehydrohalogenation of the fluorohalogenethers obtained in step 1) and obtainment of vinyl ethers; 3) fluorination with fluorine of the vinyl ethers and obtainment of fluorohalogenethers; and 4) dehydrohalogenation of the fluorohalogenethers and obtainment of the fluorovinylethers of formula (IV). The compounds of formula (IA) can be used, for example, in the preparation of various polymers, such as fluorinated elastomers and fluorinated thermoprocessable semicrystalline polymers.

Abstract: Liquid formulations of imidoalkanepercarboxylic acids, in the form of aqueous dispersions comprising, in percentages by weight relative to the total weight of the composition: A) from ?7% to 40% and preferably from 10% to 20% of imidoalka-nepercarhoxylic acids having the general formula (I), the said imidoalkanepercarboxylic acids being in the ? form and having a dissolution time, determined via the test of the rate of dissolution at a temperature of 40° C. or 18° C., of not more than 5 minutes when determined at 40° C. or 15 minutes when determined at 18° C., for an amount of dissolved acid equal to 99% of the theoretical amount; B) from 0.001% to 0.9% of a nonionic surfactant; the said dispersions having a viscosity of not more than 2000 mPa·sec at 25° C. by applying a shear rate of 20 s?1; in which the dissolution time of the component A), determined via the test of the rate of dissolution at a temperature of 40° C. or 18° C., is not more than 5 minutes when determined at 40° C.

Abstract: MEA 7-layer assemblies with gasket, comprising: a film of ionomeric membrane (3), containing functional acid groups —SO3H and/or —COOH, having in at least one direction, called direction x, a size variation lower than 0.08%; two GDL sheets (1) and (2) in porous material having on one surface an electrocatalytic layer, not shown in the Figures, of which: the first sheet DGL (1) is coextensive with the membrane (3) surface, positioned so as to overlap thereto; the second sheet GDL (2), having a lower width but the same length of the film of membrane (3), measured in the x direction; the two sheets (1) and (2) placed so that the electrocatalytic layer comes into contact, respectively, with each of the two membrane faces; a gasket positioned according to a frame shape along the assembly perimeter.

Abstract: A cyclic phosphazene compound complying with formula (I) or (II): wherein: Rf and R?f represent independently a (per)fluoropolyoxyalkylene chain comprising recurring units Ro, said recurring units, distributed randomly through the (per)fluoropolyoxyalkylene chain, being chosen among; (i)—CFXO—, X being F or CF3; (ii) —CF2CFXO—, X being F or CF3; (iii) —CF2CF2CF2O—; (iv) —CF2CF2CF2CF2O—; Z and Z? represent a polar group of formula —O?M+, M being chosen among hydrogen, a monovalent metal, or an ammonium radical of formula NR1R2R3R4, or represent a polar group of formula —O?)2M?2+, M? being a divalent metal; nZ is an integer from 1 to 3; nZ? is an integer from 1 to 4; nf? is an integer such that nZ?+nf? is equal to 8; and nf is an integer such that nZ+nf is equal to 6.

Abstract: The invention pertains to a thermoplastic fluoropolymer composition comprising: at least one thermoplastic partially fluorinated fluoropolymer having a melt flow index (MFI) of less than 10 g/10 min. as measured according to ASTM D-1238 under a piston load of 5 kg polymer A; from 0.05 to 5% by weight of A at least one (per)fluoropolyether, polymer B; and from 0 to 10% by weight of A of at least one per(halo)fluoropolymer polymer C. The addition of a (per)fluoropolyether B and, optionally, of a per(halo) fluoropolymer C advantageously enables improvement of rheological behavior of thermoplastic partially fluorinated fluoropolymer A, making possible processing in less severe conditions and yielding final parts with outstanding surface aspect and good homogeneity and coherency. Still objects of the inventions are the process for manufacturing said thermoplastic fluoropolymer composition and the articles thereof.

Abstract: Catalyst-polymer liquid dispersion (LD) comprising (i) catalyst particles, (ii) polymer particles consisting of at least one (per)fluoro sulfonyl fluoride polymer in the —SO2F form, and (iii) an aqueous suspending medium. Catalyst coated membrane precursor (CCMP), catalyst coated membrane (CCM) and catalytic ionomeric ink (CII) derived therefrom and methods for their manufacture. Catalyst coated membrane (CCM-CII) derived from said (CII).

Abstract: Use in LAN cable applications, as materials for the coating of the primary cable and for the external jacket, of TFE thermoprocessable perfluoropolymers comprising perfluoroalkylvinylethers in the following amounts, expressed as percent by weight on the total of the monomers: a) 0-5.5% of perfluoromethylvinylether (PMVE); b) 0.4-4.5% of perfluoroethylvinylether (PEVE) and/or perfluoropropylvinylether (PPVE); when a) is present, then a)+b) ranges from 1.5% to 5.5% by weight on the total of the monomers; optionally c) 0-6% of hexafluoropropene (HFP); the TFE amount being the complement to 100% by weight.

Abstract: The invention pertains to a thermoplastic fluoropolymer composition comprising: at least one thermoplastic partially fluorinated fluoropolymer having a melt flow index (MFI) of less than 10 g/10 min, as measured according to ASTM D-1238 under a piston load of 5 kg polymer A; from 0.05 to 5% by weight of A at least one (per)fluoropolyether, polymer B; and from 0 to 10% by weight of A of at least one per(halo)fluoropolymer polymer C. The addition of a (per)fluoropolyether B and, optionally, of a per(halo)fluoropolymer C advantageously enables improvement of rheological behavior of thermoplastic partially fluorinated fluoropolymer A, making possible processing in less severe conditions and yielding final parts with outstanding surface aspect and good homogeneity and coherency. Still objects of the inventions are the process for manufacturing said thermoplastic fluoropolymer composition and the articles thereof.

Abstract: TFE-based thermoprocessable copolymers having the following composition, expressed in percentage by moles on the total of the monomers: A) from 0.01 to 15% of the monomer of formula: CF2?CFOCF2OCF3??(a); A1) tetrafluoroethylene from 99.99 to 85%; optionally B) one or more (per)fluorinated comonomers having at least one unsaturation of ethylene type, different from TFE; the sum of the molar percentages A)+B) being such as to give polymers showing at least one melting peak at the thermogravimetric analysis (DSC).

Abstract: Fluorovinyl ethers having the formula CFX?CXOCF2OR, wherein R is a C2-C6 linear, branched or C5-C6 cyclic (per) fluoroalkyl group, or a C2-C6 linear, branched (per)fluoro oxyalkyl group containing from one to three oxygen atoms; when R is fluoroalkyl or fluorooxyalkyl group as above defined, it can contain from 1 to 2 atoms, equal or different, selected from the following: H, Cl, Br, I; X?F, H; and homopolymers or polymers obtainable polymerizing said Fluorovinyl ethers with at least another polymerizable monomer.

Abstract: Dispersions of fluorinated polymers substantially free from fluorinated surfactants, having high stability to shear combined with high stability to segregation, said dispersions comprising one or more anionic surfactants having the following general formula (1): Y?-(P1)n-CH(Y)-(P2)n?-Y???(1) wherein: Y, Y? and Y? are anionic or nonionic groups, with the proviso that at least one of Y, Y? or Y? is an anionic group and at least one of the remaining of Y, Y? or Y? is a nonionic group; p1 and p2, equal or different, are linear or branched alkylene groups, optionally containing one or more unsaturations, having a number of carbon atoms from 1 to 10, preferably from 1 to 6; n and n? equal or different, are zero or 1.

Abstract: Use for the oleo-repellent paper sizing of carboxylic perfluoropolyethers of formula T-O—Rf-T??(I) wherein T=—CF2—COOH or —CF2CF2—COOH and Rf is a (per)fluoropolyoxyalkylene chain.

Abstract: A process for preparing monocarboxylic perfluoropolyethers of formula: A-O-(RF)z-(CFY)t-C(O)OX (I) wherein: X is H, C1-C10 alkyl, or an aryl group; Y=F, CF3; t=1, 2 or 3; A is a C1-C4 perfluoroalkyl end group; z=0 or 1; RF is a perfluorooxyalkylene chain; having a number average molecular weight in the range 180-8,000; comprising the following steps: a) one or more distillations of perfluoropolyethers (PFPE) of formula T-O-(RF)z-T? (II) wherein: z and RF are as above defined; T, T?, equal to or different from each other, are selected from acyl fluoride or carbonyl-containing functional end groups and non functional end groups to obtain one PFPE fraction of formula (II) wherein the difference between the minimum and the maximum molecular weight of the components is lower than or equal to 600; b) partial fluorination of the fraction obtained in a); c) esterification c1) and/or hydrolysis c2) of the mixture obtained in b); d) distillation of the product obtained in c2) or in c1).

Abstract: A fluoropolymer [polymer (F)], a polymerisation process for its manufacture, and a moulding process using such fluoropolymer [polymer (F)]. The polymerisation process comprises polymerising at least one fluorinated monomer in a polymerization medium, in which the polymerization medium is mixed by means of a stirring system comprising at least two counter-rotating impellers. Surprisingly and advantageously, the polymerization occurs without fouling or deposit formation on the reactor walls, and moreover, occurs with improved homogeneity, without composition, pressure or temperature gradients, thus enabling obtaining homogeneous polymer composition with no risk of local overheating. A polymer (F) obtained from such process has improved morphology (percentage of organized structures, i.e.

Abstract: This invention pertains to a thermoplastic fluoropolymer composition comprising: at least one thermoplastic hydrogen-containing fluoropolymer [polymer (A)]; and from 0.1 to 10% by weight of (A) of at least one per(halo)fluoropolymer chosen among tetrafluoroethylene (TFE) copolymers having a dynamic viscosity at a shear rate of 1 rad sec?1 of less than 10 Pa sec at a temperature of 280° C. [polymer (B)]. The addition of a TFE copolymer [polymer (B)] of low melt viscosity advantageously enables improvement of rheological behavior of thermoplastic hydrogen-containing fluoropolymer (A), making possible processing in less severe conditions and yielding final parts with outstanding surface aspect and good homogeneity and coherency. Still objects of the invention are a process for manufacturing said thermoplastic fluoropolymer composition and the articles, such as shaped articles, films, cable sheathing, pipes, flexible pipes, hollow bodies comprising said thermoplastic fluoropolymer composition.

Abstract: VDF-based curable fluoroelastomers having glass transition temperature lower than ?35° C. and an amount of —COF end groups in the polymer lower than the sensitivity limit of the method using the FT-IR spectroscopy described in the present application.

Abstract: The invention concerns a composition comprising: at least one melt-processible per(halo)fluoropolymer (polymer A); from 0.01 to 5% by weight of polymer A of at least one smoke-suppressant agent (S) having a decomposition temperature of at least 350° C., selected from the group consisting of molybdenum derivatives, borates of an alkaline-earth metal or of a group 12 transition metal, and mixtures thereof; optionally, at least one oxide of a metal different from molybdenum. The composition of the invention excels simultaneously in providing excellent insulating properties on meal wires or optical fibers, outstanding processing parameters for high speed cable manufacture and high performance ratings on flammability, smoke generation and fuel load. Advantageously, cables comprising said composition comply with 25/50/8 requirements according to NFPA-255 and -259 for limited combustible materials.