Abstract: A near-infrared ray shielding film which has high adhesion between layers, is substantially transparent, can shield a wide near-infrared region at a high level and is free from electromagnetic interference. This near-infrared ray shielding film is a multi-layer laminated film consisting of a first laminated film portion and a second laminated film portion, each consisting of first layers and second layers alternated with each other, and the average thickness of all the layers of the second laminated film portion is 1.05 to 1.6 times the average thickness of all the layers of the first laminated film portion.

Abstract: A laminated film for a reflecting plate is provided that comprises a layer A and a layer B, the layer A comprising a polyester that comprises substantially no antimony element and preferably comprises 1 to 25 wt % of inert particles having an average particle diameter of 0.3 to 3.0 ?m and the layer B being in contact with the layer A and comprising a polyester which preferably comprises 31 to 80 wt % of inert particles having an average particle diameter of 0.3 to 3.0 ?m. This laminated film has a practically satisfactory capability of reflecting visible light, can be produced stably even if inert particles are added in high concentration, hardly has streak-like defects, and can be suitably used as a substrate for a reflecting plate for a liquid crystal display or an internally illuminating electrical billboard.

Abstract: A white laminated film which has practically sufficient reflectivity at a visible range, can be formed stably, is free from deterioration (yellowing) by ultraviolet radiation, rarely deforms by heat and can be advantageously used as a reflector substrate for liquid crystal displays and internal illumination type electrically spectacular signs, is provided. The laminated film includes a first layer of a composition which includes 31 to 60 wt % of inert particles having an average particle diameter of 0.3 to 3.0 ?m and 40 to 69 wt % of a polyester consisting of 1 to 100 mol % of naphthalenedicarboxylic acid and 0 to 99 mol % of terephthalic acid as a dicarboxylic acid component and ethylene glycol as a diol component, and a layer B of a composition which includes 0 to 30 wt % of inert particles having an average particle diameter of 0.3 to 3.

Abstract: There is provided a conductive film which is formed by laminating an anchor coating layer containing a polyester resin and an acrylic resin having an oxazoline group and a polyalkylene oxide chain as constituents and a transparent conductive coating layer on at least one surface of a base material film in this order and which has a total light transmittance of at least 60% and a surface resistance value of 1×101 to 1×104?/ This conductive film has excellent transparency and conductivity, can retain a satisfactory conductive performance even when an external force is applied since adhesion between the base material and the transparent conductive coating layer is good, and is suitably used as a transparent electrode or electromagnetic shielding material for a liquid crystal display (LCD), transparent touch panel, organic electroluminescent device and inorganic electroluminescent lamp.

Abstract: An easily adhesive polyester film is provided which is used for protection of the back side of a solar cell, the adhesive polyester film comprising a polyester film and a resin film situated on a surface of the polyester film, the resin film comprising a crosslinking agent and a resin selected from the group consisting of a polyester resin having a glass transition point of 20 to 100° C., an acrylic resin having a glass transition point of 20 to 100° C., a combination of the resins and a combination of at least one of the resins and a polyvinyl alcohol having a saponification degree of 70 to 90 mol %. This film has excellent adhesion to EVA while having excellent mechanical properties, heat resistance and moisture resistance.

Abstract: An object of the invention is to provide such an oriented polyester film that has a constant thickness, and is excellent in dimensional stability at a high temperature and dimensional stability to temperature change in a working temperature range. The invention relates to an oriented polyester film containing as a major component of a substrate layer polyethylene-2,6-naphthalene dicarboxylate, being stretched at least in one direction, and having a film thickness of from 12 to 250 ?m, wherein (1) a coefficient of linear thermal expansion ?t at a temperature of from 30 to 100° C. is from 0 to 15 ppm/° C. in both longitudinal and width directions of the film, and (2) a thermal shrinkage rate at 100° C. for 10 minutes is 0.5% or less in both longitudinal and width directions of the film.

Abstract: An object of the present invention is to provide a thin biaxially oriented film excellent in dimensional stability against humidity change, as well as a magnetic recording medium and a film capacitor using the same. The present invention provides a single layered or laminated biaxially oriented film comprising an aromatic polyester (a) and a polyolefin (b) having a melting point of from 230 to 280° C., wherein the ratio of the polyolefin (b) is from 2 to 60% based on the entire weight of the film, and the film thickness is from 1 to 10 ?m.

Abstract: According to an optical film laminated body containing a reflective polarizing film having a water vapor transmittance of from 5 to 20 g/m2/day, an absorptive polarizing film and a transparent film having a water vapor transmittance of from 100 to 500 g/m2/day, in this order, characterized in that a transmission axis of the reflective polarizing film is in parallel to a transmission axis of the absorptive polarizing film, sufficient adhesion property between the reflective polarizing film and the absorptive polarizing film can be obtained, so as to provide an optical film laminated body causing no warpage.

Abstract: The object of the present invention is to provide a laminated film excellent in light resistance, scratch resistance, transparency, dimensional stability and adhesion to a hard coating layer. The present invention is a laminated film comprising a base material layer, an easily adhering layer and a hard coating layer, wherein the easily adhering layer is formed on the base material layer and the hard coating layer is formed on the easily adhering layer, and further wherein (1) the base material layer is formed of a polyester resin formed from naphthalenedicarboxylic acid as a main dicarboxylic acid component and ethylene glycol as a main glycol component, (2) the hard coating layer has an ultraviolet absorbing function and has a pencil hardness of H or higher on the hard coating layer surface, and (3) said laminated film has a variation (?b*) of less than 2.0 between transmittance b* values obtained before and after a 300 hours' xenon arc test of said laminated film.

Abstract: There is provided a white polyester film which retains practically satisfactory reflectivity with respect to the visible light range, can undergo stable film production even when inorganic fine particles are added in high concentration and is stable against a dimensional change caused by heat generated from a light source. The polyester film is a polyester film which comprises a composition comprising a copolyester and 30 to 50 wt % of inorganic fine particles based on the composition, shows a thermal shrinkage at 85° C. in longitudinal and transverse directions of not higher than 0.7% and a thermal shrinkage at 150° C. in the longitudinal and transverse directions of not higher than 5.0%, and shows an average reflectance at a wavelength of 400 to 700 nm of not lower than 90%.

Abstract: A laminated film obtained by carrying out anti-reflection processing on the surface of a reflection polarizing film. This laminated film comprising (A) a monoaxially oriented laminated film consisting of 501 or more alternating first layers made of a first thermoplastic resin having a positive stress optical coefficient and a thickness of 0.05 to 0.5 ?m and second layers made of a second thermoplastic resin different from the first thermoplastic resin and having a thickness of 0.05 to 0.5 ?m, and a low-reflectance layer formed on at least one side of the monoaxially oriented laminated film and having a reflectance of the surface measured from the input side of 3% or less.

Abstract: A laminated polyester film comprising a coating layer formed on at least one side of a polyester film, this coating layer comprising a polymer binder and inorganic-organic composite particles having an average particle diameter of 200 to 2,000 nm. This film has excellent scratch resistance, adhesion, transparency and slipperiness and is useful as an adhesive film for optical use.

Abstract: An antistatic film having an antistatic coating film on at least one surface of a polyester film, the antistatic coating film comprising a polymer having a polymerized unit represented by the following formula (1): wherein R1 and R2 each independently represent a hydrogen atom or a methyl group, R3 represents an alkylene group having 2 to 10 carbon atoms, R4 and R5 each independently represent an alkyl group having 1 to 5 carbon atoms, R6 represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a hydroxyalkyl group having 2 to 10 carbon atoms, and Y? represents a halogen ion, a halogenated alkyl ion, a nitrate ion, a sulfate ion, an alkyl sulfate ion, a sulfonate ion or an alkyl sulfonate ion. The film is used in such applications requiring an antistatic property such as a protective film for a liquid crystal polarizing plate.

Abstract: An ultraviolet radiation absorbent for thermoplastic polymer materials such as polyethylene terephthalate or polycarbonate contains cyclic imino ester compound of a specified structure in an amount of over 99.5 weight % and less than 100 weight % and having an acid value in the range of 1×10?3–1 and/or a chlorine ion content in the range of 1×10?1–1×103 ppm.

Abstract: An ultraviolet radiation absorbent for thermoplastic polymer materials such as polyethylene terephthalate or polycarbonate contains cyclic imino ester compound of a specified structure in an amount of over 99.5 weight % and less than 100 weight %, having the melt beginning temperature obtained by melting point measurement in differential thermal analysis within the range of 300–310° C. and/or the weight loss beginning temperature obtained by thermogravimetric measurement within the range of 270–305° C.

Abstract: There is provided a laminated film for optical use comprising a polyester film which has a lubricity layer containing globular particles in at least one side thereof, wherein the laminated film has a thickness irregularity of 0.5 to 7.0%, and wherein the polyester film contains inert particles derived from catalysts and the amount of the inert particles determined by a dark-field microscopy satisfies the following conditions: the number of inert particles having a particle size of from 1 to 10 ?m is 200 to 20,000/mm2; and the number of inert particles having a particle size of greater than 10 ?m is 10/mm2 or less. The laminated film for optical use which is improved in uniformity, transparency, lubricity, color tone and scratch resistance, which deposits only a reduced amount of low molecular materials, and which is excellent in the adhesion to a layer adopted for various optical purposes.

Abstract: There is provided a membrane switch film comprising polyethylene 2, 6-naphthalenedicarboxylate as the major component and having excellent handling properties and durability, and particularly a film which is suitable for a membrane switch to be used in automobile interior devices which are potentially exposed to high temperature. The film is a membrane switch film having a refractive index in the range of 1.770–1.790 on both surfaces in either or both the film processing direction and the widthwise direction and an absolute value of no greater than 0.015 for the difference between the refractive indexes of both surfaces.

Abstract: There is provided a laminated polyester film which is improved in lubricity, transparency, dimensional stability, shock resistance and adhesion, and which comprises a polyester base film comprising polyester and to at least one direction, and a coating layer provided on at least one surface of the base film, wherein said coating layer contains polymer binder and inert particles, the refractive index of the inert particles being substantially same as that of the polymer binder, and wherein the laminated polyester film has a haze of 1.5% or less, a total light transmittance of 85% or more, 50% destructing energy per 100 ?m film thickness of 0.3 J or more, and a thermal shrinkage at 230° C. for 30 minutes of 4% or less.

Abstract: An optical adhesive polyester film comprising (A) a polyester film layer containing an aromatic polyester and an ultraviolet absorber and (B) a coating formed on at least one surface of the polyester film (A). The coating (B) contains at least one polymer selected from the group consisting of a coating polyester having a glass transition point of 40 to 100° C. and an acryl polymer having a glass transition point of 20 to 80° C. in an amount of 50 to 95% by weight based on the coating. The optical adhesive polyester film is disposed on the front of a plasma display so as to block externally incoming ultraviolet light.

Abstract: An antistatic film having an antistatic coating film on at least one surface of a polyester film, the antistatic coating film comprising a polymer having a polymerized unit represented by the following formula (1): wherein R1 and R2 each independently represent a hydrogen atom or a methyl group, R3 represents an alkylene group having 2 to 10 carbon atoms, R4 and R5 each independently represent an alkyl group having 1 to 5 carbon atoms, R6 represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a hydroxyalkyl group having 2 to 10 carbon atoms, and Y? represents a halogen ion, a halogenated alkyl ion, a nitrate ion, a sulfate ion, an alkyl sulfate ion, a sulfonate ion or an alkyl sulfonate ion. The film is used in such applications requiring an antistatic property such as a protective film for a liquid crystal polarizing plate.