Abstract: A method for producing a solution containing at least an unsaturated carboxylic acid-modified vinyl alcohol polymer is characterized by reacting a vinyl alcohol polymer and an unsaturated carboxylic acid compound in the presence of an acid catalyst soluble in the reaction system or a solid acid catalyst, and a gas barrier film is obtained by using the same. An example thereof is a method for producing a solution (A) containing an unsaturated carboxylic acid-modified vinyl alcohol polymer (b), the method comprising following two steps of: (1) a reaction step in which the unsaturated carboxylic acid-modified vinyl alcohol polymer (b) is formed by reacting a vinyl alcohol polymer and an unsaturated carboxylic acid compound (a) in the presence of an acid catalyst soluble in the reaction system; and (2) an ion exchange step in which at least the acid catalyst of acidic compounds is removed by an anion exchange resin.

Abstract: The gas-barrier film of the present invention basically comprises a polymer of a polyvalent metal salt of an unsaturated carboxylic acid compound which gives an infrared absorption spectrum in which the ratio of the absorbance A0 at around 1,700 cm?1 attributable to V C?O of the carboxylic acid group to the absorbance A at around 1,520 cm?1 attributable to V C?O of the carboxylate ion, A0/A, is lower than 0.25, and this gas-barrier film and a gas-barrier layered body having the film can be manufactured by applying a solution of a polyvalent metal salt of an unsaturated carboxylic acid compound having a degree of polymerization lower than 20 to at least one side of a substrate layer and then polymerizing the polyvalent metal salt of the unsaturated carboxylic acid compound.

Abstract: The invention aims at providing a polylactic acid composition having specific thermal characteristics and gas barrier properties and at obtaining a polylactic acid composition comprising PLLA and PDLA which composition can form moldings (such as stretched film) excellent in surface smoothness, transparency, heat resistance, and toughness. Specifically, a polylactic acid composition characterized by exhibiting a peak of 30 mJ/mg or above in DSC as determined by cooling at a rate of 10° C./min after the lapse of 10 min at 250° C., preferably a polylactic acid composition characterized by exhibiting a peak (1)/peak (2) ratio of 0.5 or below wherein the peak (1) and peak (2) correspond to a peak of Tm of 150 to 180° C. and a peak of Tm of 200 to 240° C. respectively in DSC as observed in the second heating (namely, re-heating from 0° C. at a rate of 10° C./min which follows the cooling at a rate of 10° C./min conducted after the lapse of 10 min at 250° C.).

Abstract: An object of the present invention is to provide a polylactic acid composition having specific thermal characteristics and gas barrier properties, and to obtain a molding comprising a polylactic acid composition of PLLA and PDLA capable of forming a polylactic acid stretched film or other molding having superior surface smoothness, transparency, heat resistance and toughness, and the constitution thereof is characterized by being a molding comprising a polylactic acid composition in which the peak in DSC measurement during cooling (at a rate of 10° C./min) after allowing to remain at 250° C. for 10 minutes is 30 mJ/mg or more, and preferably comprising a polylactic acid composition such that, in measurement during the DSC 2nd heating (cooling at a rate of 10° C./min after allowing to remain at 250° C. for 10 minutes followed by reheating from 0° C. at a rate of 10° C./min), the peak ratio (peak 1/peak 2) of the peak when Tm is 150 to 180° C. (peak 1) to the peak when Tm is 200 to 240° C. (peak 2) is 0.

Abstract: Disclosed is an excellent gas barrier laminate whose gas-barrier property has little dependency on temperature and which hardly causes fracture even when the laminate is stretched. A gas barrier film comprising a polymer (A) of an unsaturated carboxylic acid compound monovalent metal salt (a), wherein the polymer (A) contains a modified vinyl alcohol polymer (B); a gas barrier laminate comprising a base layer and the gas barrier film formed on at least one surface of the base layer; and a method for production of a gas barrier laminate comprising the steps of: coating a solution of an unsaturated carboxylic acid compound monovalent metal salt (a) having a polymerization degree less than 20 on at least one surface of a base layer, wherein the solution contains a modified vinyl alcohol polymer (B); performing the polymerization to form a layer of the polymer (A) of the unsaturated carboxylic acid compound monovalent metal salt (a) containing the modified vinyl alcohol polymer (B).

Abstract: The object of the present invention is to provide a polylactic acid stretched film having biodegradability and excelling in transparency and heat resistance. The main feature is characterized in that a polylactic acid stretched film is composed of a polylactic acid composition containing poly-L-lactic acid and poly-D-lactic acid in which a peak ratio (peak 1/peak 2) of a peak height (peak 1) of a maximum endothermic peak of endothermic peaks within a range of 150 to 200° C. to a peak height (peak 2) of a maximum endothermic peak of endothermic peaks within a range of 205 to 240° C. in DSC measurements is equal to or less than 0.2.

Abstract: Heat sealable multilayer films can package oil-rich contents to be retort sterilized without separation (delamination) of a cohesive failure heat seal layer due to penetration of oil from the contents and have appropriate heat seal strength and excellent easy openability, and can be opened with stable peel conditions. A heat sealable multilayer film includes a cohesive failure heat seal layer (1) that includes a resin composition including 75 to 85 wt % of a propylene polymer (A) and 15 to 25 wt % of an ethylene polymer (B) (based on the total of (A) and (B) of 100 wt %), and a support layer (2) including a propylene block copolymer (C).

Abstract: The present invention relates to a resin composition having an easy-openable property which comprises an ethylene polymer composition (D) comprising 5 to 65 wt % of a propylene polymer (A), 1 to 35 wt % of an ethylene/?-olefin random copolymer (B) having a density of less than 895 kg/m3 and 10 to 85 wt % of an ethylene polymer (C) having a density of 895 kg/m3 and more (in a total amount of 100 wt %), and a film thereof. The resin composition having an easy-openable property is useful as lid materials especially for propylene polymer containers and provides excellent sealability and easy openability and further provides excellent heat resistance and oil resistance.

Abstract: The present invention provides an industrially advantageous method for producing an unsaturated carboxylic acid-modified vinyl alcohol polymer, and a gas barrier film obtained by using the same.

Abstract: The object of the present invention is to provide a polylactic acid stretched film having biodegradability and excelling in transparency and heat resistance. The main feature is characterized in that a polylactic acid stretched film is composed of a polylactic acid composition containing poly-L-lactic acid and poly-D-lactic acid in which a peak ratio (peak 1/peak 2) of a peak height (peak 1) of a maximum endothermic peak of endothermic peaks within a range of 150 to 200° C. to a peak height (peak 2) of a maximum endothermic peak of endothermic peaks within a range of 205 to 240° C. in DSC measurements is equal to or less than 0.2.

Abstract: Disclosed is an excellent gas barrier laminate whose gas-barrier property has little dependency on temperature and which hardly causes fracture even when the laminate is stretched. A gas barrier film comprising a polymer (A) of an unsaturated carboxylic acid compound monovalent metal salt (a), wherein the polymer (A) contains a modified vinyl alcohol polymer (B); a gas barrier laminate comprising a base layer and the gas barrier film formed on at least one surface of the base layer; and a method for production of a gas barrier laminate comprising the steps of: coating a solution of an unsaturated carboxylic acid compound monovalent metal salt (a) having a polymerization degree less than 20 on at least one surface of a base layer, wherein the solution contains a modified vinyl alcohol polymer (B); performing the polymerizaton to form a layer of the polymer (A) of the unsaturated carboxylic acid compound monovalent metal salt (a) containing the modified vinyl alcohol polymer (B).

Abstract: An object of the present invention is to provide a polylactic acid composition having specific thermal characteristics and gas barrier properties, and to obtain a molding comprising a polylactic acid composition of PLLA and PDLA capable of forming a polylactic acid stretched film or other molding having superior surface smoothness, transparency, heat resistance and toughness, and the constitution thereof is characterized by being a molding comprising a polylactic acid composition in which the peak in DSC measurement during cooling (at a rate of 10° C./min) after allowing to remain at 250° C. for 10 minutes is 30 mJ/mg or more, and preferably comprising a polylactic acid composition such that, in measurement during the DSC 2nd heating (cooling at a rate of 10° C./min after allowing to remain at 250° C. for 10 minutes followed by reheating from 0° C. at a rate of 10° C./min), the peak ratio (peak 1/peak 2) of the peak when Tm is 150 to 180° C. (peak 1) to the peak when Tm is 200 to 240° C. (peak 2) is 0.

Abstract: A biaxially oriented laminated polypropylene film comprising a biaxially oriented polypropylene film substrate layer (B) made from a propylene-based polymer composition (A) in which an inorganic compound powder (a2) has been added to a propylene-based polymer (a1), the biaxially oriented polypropylene film substrate layer (B) has a front surface layer and a back surface layer on its both sides, both layers are made from the propylene-based polymer (a1), wherein the surface roughness (three-dimensional center-line roughness SRa) of the front and the back surface layers is less than 0.08 ?m and the gloss value (at an incidence angle of 60 degrees) is 114% or greater, and the total light transmittance of the laminated polypropylene film is 20% or less and the density is in the range of 0.40 to 0.65 g/cm3.

Abstract: The invention aims at providing a polylactic acid composition having specific thermal characteristics and gas barrier properties and at obtaining a polylactic acid composition comprising PLLA and PDLA which composition can form moldings (such as stretched film) excellent in surface smoothness, transparency, heat resistance, and toughness. Specifically, a polylactic acid composition characterized by exhibiting a peak of 30 mJ/mg or above in DSC as determined by cooling at a rate of 10° C./min after the lapse of 10 min at 250° C., preferably a polylactic acid composition characterized by exhibiting a peak (1)/peak (2) ratio of 0.5 or below wherein the peak (1) and peak (2) correspond to a peak of Tm of 150 to 180° C. and a peak of Tm of 200 to 240° C. respectively in DSC as observed in the second heating (namely, re-heating from 0° C. at a rate of 10° C./min which follows the cooling at a rate of 10° C./min conducted after the lapse of 10 min at 250° C.).

Abstract: The gas-barrier film of the present invention basically comprises a polymer of a polyvalent metal salt of an unsaturated carboxylic acid compound which gives an infrared absorption spectrum in which the ratio of the absorbance A0 at around 1,700 cm?1 attributable to V C?O of the carboxylic acid group to the absorbance A at around 1,520 cm?1 attributable to V C?O of the carboxylate ion, A0/A, is lower than 0.25, and this gas-barrier film and a gas-barrier layered body having the film can be manufactured by applying a solution of a polyvalent metal salt of an unsaturated carboxylic acid compound having a degree of polymerization lower than 20 to at least one side of a substrate layer and then polymerizing the polyvalent metal salt of the unsaturated carboxylic acid compound.

Abstract: The present invention relates to a resin composition having an easy-openable property which comprises an ethylene polymer composition (D) comprising 5 to 65 wt % of a propylene polymer (A), 1 to 35 wt % of an ethylene/?-olefin random copolymer (B) having a density of less than 895 kg/m3 and 10 to 85 wt % of an ethylene polymer (C) having a density of 895 kg/m3 and more (in a total amount of 100 wt %), and a film thereof. The resin composition having an easy-openable property is useful as lid materials especially for propylene polymer containers and provides excellent sealability and easy openability and further provides excellent heat resistance and oil resistance.

Abstract: Disclosed is a biaxially stretched polylactic acid multilayer film and the use thereof as packaging film. The gist of the biaxially stretched polylactic acid multilayer film resides in the construction wherein a substrate layer (1) of the biaxially stretched film comprised of polylactic acid (A) has been laminated on at least one surface thereof with a coating layer (II) of an aliphatic polyester composition (D) comprised of 97˜5% by weight of an aliphatic polyester copolymer (B) having a melting point (Tm) of 80˜120° C., a crystallizing temperature (Tc) of 35˜75° C. and a difference of (Tm)?(Tc) within the range of 35˜55° C. and comprising an aliphatic or alicyclic dicarboxylic acid component (b1), an aliphatic or alicyclic dihydroxyl compound component (b2) and a difunctional aliphatic hydroxycarboxylic acid component (b3) and 3˜95% by weight of a polylactic acid copolymer (C) containing 7˜30% by weight of D-lactic acid, a total of the ingredients (B) and (C) being 100% by weight.

Abstract: An antifouling material and an antifouling film, which are excellent in hydrophilicity and have such a characteristic that the surface is self-cleaned with rain water or the like, or can be easily cleaned up even when a contaminant adheres to the surface thereof, can be obtained by copolymerizing a composition containing an acrylamide derivative having at least one hydroxyl group in the molecule and a compound having at least two (meth)acryloyloxy groups in the molecule.

Abstract: Disclosed is a biaxially stretched polylactic acid multilayer film and the use thereof as packaging film. The gist of the biaxially stretched polylactic acid multilayer film resides in the construction wherein a substrate layer (1) of the biaxially stretched film comprised of polylactic acid (A) has been laminated on at least one surface thereof with a coating layer (II) of an aliphatic polyester composition (D) comprised of 97˜5% by weight of an aliphatic polyester copolymer (B) having a melting point (Tm) of 80˜120° C., a crystallizing temperature (Tc) of 35˜75° C. and a difference of (Tm)?(Tc) within the range of 35˜55° C. and comprising an aliphatic or alicyclic dicarboxylic acid component (b1), an aliphatic or alicyclic dihydroxyl compound component (b2) and a difunctional aliphatic hydroxycarboxylic acid component (b3) and 3˜95% by weight of a polylactic acid copolymer (C) containing 7˜30% by weight of D-lactic acid, a total of the ingredients (B) and (C) being 100% by weight.

Abstract: Disclosed are an aliphatic polyester composition which comprises 98˜35% by weight of an aliphatic polyester copolymer (copolycondensate) (A) having a melting point (Tm) of 80˜120° C., a crystallizing temperature (Tc) of 35˜75° C., and a difference of (Tm)?(TC) within the range of 35˜55° C. and comprised of (a1) an aliphatic or alicyclic dicarboxylic acid component, (a2) an aliphatic or alicyclic dihydroxyl compound component, and (a3) a difunctional aliphatic hydroxycarboxylic acid component; and 2˜65% by weight of an aliphatic and aromatic polyester (B) comprised of an acid component of (i) 20˜95 mol % of (b1) an aliphatic or alicyclic dicarboxylic acid component and (ii) 80˜5 mol % of (b2) an aromatic carboxylic acid and a dihydroxyl component of (b3) an aliphatic and alicyclic dihydroxyl compound, films and multilayer films produced therefrom. The films and multilayer films are excellent in transparency, impact-resistance and piercing-resisting property and suitable for packaging use.