Abstract: The invention relates to a modified strontium ferrite of the general chemical formula: Sr1-xLaxFe12-yCoyO19; in which x=y=0.01-1.00 or x=0.15 and y=x/1.6n to =x/2.6n, where n is the Fe2O3:SrO ratio used and may be 5-6. According to the invention, lanthanum and cobalt are added in an amount such that 0.14?x?0.145 and 0.14?y?0.145. The modified strontium ferrite thus prepared has excellent magnetic properties with regard to the remanence BR, the coercive force HCJ and the ratio of HK to HCJ.
Abstract: The invention relates to a modified strontium ferrite of the general chemical formula: Sr1-xLaxFe12-yCoyO19; in which x=y=0.01-1.00 or x=0.15 and y=x/1.6n to =x/2.6n, where n is the Fe2O3:SrO ratio used and may be 5-6. According to the invention, lanthanum and cobalt are added in an amount such that 0.14?x?0.145 and 0.14?y?0.145. The modified strontium ferrite thus prepared has excellent magnetic properties with regard to the remanence BR, the coercive force HCJ and the ratio of HK to HCJ.