Abstract: A tempering-free wear-resistant hot rolled strip, includes components in percentage by weight: 0.08-0.22% of C, 0.1-0.55% of Si, 0.8-1.5% of Mn, less than or equal to 0.012% of P, less than or equal to 0.005% of S, 0.01-0.055% of Als, 0.005-0.019% of Ti, and less than or equal to 0.007% of N. A method for producing the same includes: desulfurizing molten iron, smelting desulfurized molten iron, and casting into a blank; heating the casting blank; performing rough rolling; performing finish rolling; performing rapid cooling; performing coiling; and performing conventional temper rolling. According to the present disclosure, on the premise that the tensile strength of a steel plate is greater than or equal to 1100 MPa and the elongation is greater than or equal to 12%, the steel plate has a surface Brinell hardness of 330-390 and a core hardness that is 95% or above of the surface hardness.

Abstract: The present invention discloses an online color difference detection system and detection method, and belongs to the color difference detection field, the system including: an online non-contact colorimeter and a bracket, the online non-contact colorimeter being located on the bracket, and the online non-contact colorimeter emitting a light source directed towards a sample under detection to perform color difference detection on the sample under detection, wherein an angle between reflected light received by a reflected light meter of the online non-contact colorimeter and a vertical line of the sample under detection has an error within plus or minus 1 degree from an angle between reflected light received by a reflected light meter of an offline benchtop colorimeter and the vertical line of the sample under detection.

Abstract: The device has a short production line, and all components are reasonably configured. A multifunctional cooling control device is adopted to integrate high-pressure water descaling and intermediate billet cooling functions, which is simpler and more efficient. Layout of a 4R+(3?4)F rolling mill, four thermos-detectors and short-distance underground coilers are use. The method includes the steps: carrying out continuous casting to manufacture a slab, high-pressure water rotating descaling, rough rolling by a four-stand high reduction rough rolling unit, machining by a drum shear, cooling after high-pressure water descaling in the multifunctional cooling control device, finish rolling by a three-stand or four-stand finish rolling unit, air cooling, dividing coils by a high-speed flying shear, and coiling by underground coilers, wherein temperature monitoring is respectively carried out after rough rolling, before finish rolling, after finish rolling, and before coiling by the underground coiler.

Abstract: A press hardening steel by a thin slab and having a tensile strength of 1900 MPa or more includes following components by weight: C: 0.31-0.40%, Si: 0.36-0.44%, Mn: 1.6-2.0%, P?0.006%, S?0.004%, Als: 0.015-0.060%, Cr: 0.36-0.49%, Ti: 0.036-0.045% or Nb: 0.036-0.045% or V: 0.036-0.045% or a mixture of any two or more of the above in any proportion, B: 0.004-0.005%, Mo: 0.26-0.35%, and N?0.005%. A method for producing the press hardening steel includes following steps: molten iron desulphurization; smelting and refining by an electric furnace or converter; continuous casting; descaling treatment before entering a soaking furnace; heating and soaking; high pressure water descaling before entering a rolling mill; hot rolling; cooling; coiling; austenitizing; die deforming and quenching.

Abstract: A press hardening steel by a thin slab casting and direct rolling has a tensile strength of 1500 MPa or more. The press hardening steel has a components by weight percent: C: 0.21-0.25%, Si: 0.26-0.30%, Mn: 1.0-1.3%, P?0.01%, S?0.005%, Als: 0.015-0.060%, Cr: 0.25-0.30%, Ti: 0.026-0.030% or Nb: 0.026-0.030% or V: 0.026-0.030%, or a mixture of two or more of the above in any proportion; B: 0.003-0.004%, and N?0.005%. A method for producing the press hardening steel includes following steps: hot metal desulphurization; electric-furnace or converter smelting and refining; continuous casting; descaling, then entering a soaking furnace; heating and soaking; high-pressure water descaling, then entering a rolling mill; hot rolling; cooling; coiling; austenitizing; die deforming and quenching.

Abstract: A press hardening steel by a medium thin slab and having a tensile strength of 1500 MPa or more, includes following components by weight percent: C: 0.21%-0.25%, Si: 0.26%-0.30%, Mn: 1.0%-1.3%, P?0.01%, S?0.005%, Als: 0.015%-0.060%, Cr: 0.25%-0.30%, Ti: 0.026%-0.030% or Nb: 0.026%-0.030% or V: 0.026%-0.030% or a mixture of any two or more of the above in any proportion, B: 0.003%-0.004%, Mo: 0.17-0.19% and N?0.005%. A method for producing the press hardening steel includes following steps: molten iron desulphurization; smelting and refining by an electric furnace or converter; continuous casting; descaling treatment before entering a soaking furnace; hating and soaking; high pressure water descaling before entering a rolling mill; hot rolling; cooling; coiling; austenitizing; die deforming and quenching.

Abstract: A press hardening steel by a thin slab casting and direct rolling has a tensile strength of 1500 MPa or more. The press hardening steel has a components by weight percent: C: 0.21-0.25%, Si: 0.26-0.30%, Mn: 1.0-1.3%, P?0.01%, S?0.005%, Als: 0.015-0.060%, Cr: 0.25-0.30%, Ti: 0.026-0.030% or Nb: 0.026-0.030% or V: 0.026-0.030%, or a mixture of two or more of the above in any proportion; B: 0.003-0.004%, and N?0.005%. A method for producing the press hardening steel includes following steps: hot metal desulphurization; electric-furnace or converter smelting and refining; continuous casting; descaling, then entering a soaking furnace; heating and soaking; high-pressure water descaling, then entering a rolling mill; hot rolling; cooling; coiling; austenitizing; die deforming and quenching.

Abstract: A press hardening steel by a thin slab and having a tensile strength of 1900 MPa or more includes following components by weight: C: 0.31-0.40%, Si: 0.36-0.44%, Mn: 1.6-2.0%, P?0.006%, S?0.004%, Als: 0.015-0.060%, Cr: 0.36-0.49%, Ti: 0.036-0.045% or Nb: 0.036-0.045% or V: 0.036-0.045% or a mixture of any two or more of the above in any proportion, B: 0.004-0.005%, Mo: 0.26-0.35%, and N?0.005%. A method for producing the press hardening steel includes following steps: molten iron desulphurization; smelting and refining by an electric furnace or converter; continuous casting; descaling treatment before entering a soaking furnace; heating and soaking; high pressure water descaling before entering a rolling mill; hot rolling; cooling; coiling; austenitizing; die deforming and quenching.

Abstract: A press hardening steel by a medium thin slab and having a tensile strength of 1500 MPa or more, includes following components by weight percent: C: 0.21%-0.25%, Si: 0.26%-0.30%, Mn: 1.0%-1.3%, P?0.01%, S?0.005%, Als: 0.015%-0.060%, Cr: 0.25%-0.30%, Ti: 0.026%-0.030% or Nb: 0.026%-0.030% or V: 0.026%-0.030% or a mixture of any two or more of the above in any proportion, B: 0.003%-0.004%, Mo: 0.17-0.19% and N?0.005%. A method for producing the press hardening steel includes following steps: molten iron desulphurization; smelting and refining by an electric furnace or converter; continuous casting; descaling treatment before entering a soaking furnace; hating and soaking; high pressure water descaling before entering a rolling mill; hot rolling; cooling; coiling; austenitizing; die deforming and quenching.

Abstract: A press hardening steel by a medium and thin slab casting and direct rolling has a tensile strength 1900 MPa or more. The press hardening steel includes following chemical components by weight percent: C: 0.31-0.40%, Si: 0.36-0.44%, Mn: 1.6-2.0%, P?0.006%, S?0.004%, Als: 0.015-0.060%, Cr: 0.36-0.49%, Ti: 0.036-0.045% or Nb: 0.036-0.045% or V: 0.036-0.045%, or a mixture of the above two or more in any ratio, B: 0.004-0.005%, Mo: 0.26-0.35%, Ni: 0.11-0.20%, and N?0.005%. A method for producing the press hardening steel includes following steps: desulphurizing molten iron; electric furnace or converter smelting and refining; continuous casting; descaling treatment before entering a soaking furnace; heating and soaking; high-pressure water descaling before entering a rolling mill; hot rolling; cooling; coiling; austenitizing; die deforming and quenching.