Abstract: A method for producing metal zinc by liquid/liquid extraction, comprising leaching of a zinc-bearing solid raw material containing antimony with a slightly acid aqueous solution, at a pH value maintained above 3 and less than or equal to 5, with formation of a suspension, drawing-off from the suspension of an aqueous phase containing zinc in solution to be subject to the extraction, additional leaching of the remaining suspension with an acid aqueous solution, at a pH value maintained below 3.5 and greater than or equal to 1, with formation of a pulp, introduction of a neutralizing agent in this pulp with coprecipitation of antimony and other impurities and separation from this neutralized pulp of a zinc-bearing aqueous solution which is recycled to the step for leaching the zinc-bearing solid raw material.
Abstract: A method for producing metal zinc by liquid/liquid extraction, comprising leaching of a zinc-bearing solid raw material containing antimony with a slightly acid aqueous solution, at a pH value maintained above 3 and less than or equal to 5, with formation of a suspension, drawing-off from the suspension of an aqueous phase containing zinc in solution to be subject to the extraction, additional leaching of the remaining suspension with an acid aqueous solution, at a pH value maintained below 3.5 and greater than or equal to 1, with formation of a pulp, introduction of a neutralizing agent in this pulp with coprecipitation of antimony and other impurities and separation from this neutralized pulp of a zinc-bearing aqueous solution which is recycled to the step for leaching the zinc-bearing solid raw material.
Abstract: Method for producing hydrometallurgical zinc oxide powder having characteristics equivalent to that derived from a French process, comprising formation of an aqueous pulp from a starting zinc oxide having particles of nodular structure, wet milling of this aqueous pulp, separation in this milled pulp between a liquid phase and a solid phase containing the zinc oxide, and drying of said solid phase, coupled with a mechanical deagglomeration of the particles during drying, to obtain a dry zinc oxide powder with particles of nodular structure having a particle size distribution where the particles have an average size (d50) between 0.02 and 20 ?m.
Type:
Grant
Filed:
May 6, 2008
Date of Patent:
May 10, 2011
Assignee:
Zincox Resources PLC
Inventors:
Kevin Clais, Duncan Turner, Philippe Leblanc, Antoine Masse