Abstract: The present invention relates to an aromatic polycarbonate obtained via the melt transesterification of a diaryl carbonate, a bisphenol and an endcapping agent selected from paracumyl phenol, dicumyl phenol, p-tert-butyl phenol and mixtures of at least two of said endcapping agents, said polycarbonate having a melt volume rate of at least 20 cm3/10 min (ISO 1133, 300° C., 1.2 kg), a terminal hydroxyl group content of at most 800 ppm by weight, a Fries branching content of at most 1300 ppm by weight and a content of bulky end groups of at least 20 mol % defined as the sum of the mol % of end-groups based on said bisphenol and the mol % of end-groups based on said endcapping agent.

Abstract: An object of the present invention is to provide a golf ball having excellent spin performance on approach shots under a wet condition and excellent spin performance on approach shots under a condition that there is grass between the golf ball and the club face. The present invention provides a golf ball comprising a golf ball body and a paint film composed of at least one layer and formed on a surface of the golf ball body, wherein an outermost layer of the paint film located at the outermost layer of the golf ball contains a base resin and a porous filler, the base resin contains a polyurethane obtained by a reaction between a polyisocyanate composition and a polyol composition, and the porous filler contains SiO2 in an amount of 50 mass % or more as a constituent component.

Abstract: A reinforced polycarbonate composition includes 30-60 wt % of a homopolycarbonate; 5-30 wt % of a poly(carbonate-siloxane); 10-40 wt % of a high heat polycarbonate having a glass transition temperature of 170° C. or higher determined per ASTM D3418 with a 20° C./min heating rate; 1-10 wt % of a phosphorous-containing flame retardant present in amount effective to provide 0.1-1.5 wt % phosphorous; 0.01-0.5 wt % of an anti-drip agent; 5-30 wt % of a reinforcing fiber; and optionally, up to 10 wt % of an additive composition, wherein each amount is based on the total weight of the reinforced polycarbonate composition, which sums to 100 wt %. A molded sample of the polycarbonate composition has a heat deflection temperature greater than 115° C., preferably greater than 125° C., more preferably greater than 130° C., or a flame test rating of V1, preferably V0 as measured according to UL-94 at a thickness of 0.8 millimeter, or at a thickness of 0.6 mm, or at a thickness of 0.4 mm.

Abstract: An object of the present invention is to provide a golf ball having excellent spin performance on approach shots under a wet condition and excellent spin performance on approach shots under a condition that there is grass between the golf ball and the dub face.

Abstract: Provided is a polycarbonate resin composition and a molded product comprising same. The polycarbonate resin composition comprises a linear polycarbonate resin, a branched polycarbonate resin, a fluorinated sulfonate-based metal salt, a phenyl methyl silicone oil, and a phenyl methyl silicone resin. The linear polycarbonate resin and branched polycarbonate resin include a repeating unit of the following Chemical Formula 1: wherein in Chemical Formula 1: R1 to R4 are each independently hydrogen, C1-10 alkyl, C1-10 alkoxy, or halogen; and Z is C1-10 alkylene unsubstituted or substituted with phenyl, C3-15 cycloalkylene unsubstituted or substituted with C1-10 alkyl, O, S, SO, SO2, or CO.

Abstract: A core-shell particle including a core containing a perfluoropolymer and a shell containing a non-fluorine resin, the core having a periphery coated with the non-fluorine resin at a coverage of 90% or more, the perfluoropolymer being a polymer containing a polymerized unit based on a perfluoro monomer in an amount of 90 mol % or more relative to all polymerized units, and the shell having a mass of 50 or less relative to a total mass of the core and the shell of 80. Also disclosed is a method for producing the core-shell particle.

Abstract: A composition includes specific amounts of a reinforcing filler and a copolycarbonate containing bisphenol A carbonate units and second carbonate units of the formula wherein Ra, Rb, R3, R4, j, p, and q are defined herein. The composition is useful for fabricating articles that exhibit a desirable balance of heat resistance, printability in large format additive manufacturing, and good surface appearance in printed parts. Also described is a method of additive manufacturing utilizing the composition.

Abstract: Provided is a curable composition which forms a cured product that has excellent fireproof performance, while having excellent shape retainability even in cases where the expansion ratio of the cured product after firing is set to a high value. This curable composition includes a shape retention agent, while having fluidity when applied; and if a cured product that is obtained by curing this curable composition is fired in 600° C. air atmosphere for 30 minutes, the cured product after firing has shape retainability.

Abstract: A plastic pro-biodegradation additive includes a carrier polymer and a nanostarch compound. The nanostarch compound can include nanostarch with a particle size in a range of about 40 to about 500 nm. The nanostarch compound can include small-size and/or large-size regular starch. The carrier polymer can be a biodegradable polymer. The additive can include: a polysaccharide; an organic filler; one or more of a monosaccharide, a disaccharide and an oligosaccharide; a surfactant; and/or an inorganic filler. The carrier polymer can include a non-biodegradable polymer. Biodegradable plastic compositions and methods of preparing a biodegradable plastic material are also disclosed.

Abstract: The present invention provides a heat shrinkable film which is capable of replacing polyvinyl chloride-based heat shrinkable films, exhibits appropriate rigidity and appropriate shrinkage force, and is excellent in stability during storage, The heat shrinkable film including a polyester resin A having a glass transition temperature of 65° C. or higher, and a polyester resin B having a glass transition temperature higher than the glass transition temperature of the polyester resin A by 10° C. or more, wherein a content of the polyester resin B is from 5 to 25% by mass with respect to 100% by mass of the heat shrinkable film, and a thickness is 25 ?m or more and less than 80 ?m.

Abstract: The invention relates to a composition obtainable by mixing polycarbonate, unsized talc and a specific anhydride-modified alpha-olefin polymer, wherein the amounts of the talc and the specific anhydride-modified alpha-olefin polymer are matched to one another such that, for every 10 parts by weight of the talc, 0.10 to 1.4 parts by weight of the anhydride-modified alpha-olefin polymer are used. It has been shown that in situ sizing of talc with the wax can minimize the degradation of the polycarbonate only in the course of mixing with the polycarbonate and, at the same time, properties such as multiaxial impact resistance and flowability can be improved.

Abstract: A thermoplastic resin composition according to the present invention contains about 100 parts by weight of a polycarbonate resin, about 5 to about 50 parts by weight of a polyolefin resin, about 5 to about 50 parts by weight of a glass fiber, and about 1 to about 20 parts by weight of a modified olefin-based copolymer, wherein the modified olefin-based copolymer includes an epoxy-modified olefin-based copolymer and a maleic acid anhydride-modified olefin-based copolymer, and the weight ratio of the epoxy-modified olefin-based copolymer to the maleic acid anhydride-modified olefin-based copolymer is about 1:0.05 to about 1:15. The thermoplastic resin composition has excellent stiffness, impact resistance, and the like, and has a low specific gravity, dielectric constant, dielectric dissipation factor, and the like.

Abstract: A thermoplastic resin composition of the present invention comprises: about 100 parts by weight of a polycarbonate resin; about 1 part by weight to about 5 parts by weight of a silicone-based rubber modified vinyl graft copolymer; and about 0.03 parts by weight to about 0.2 parts by weight of a metallic salt compound; wherein the metallic salt compound comprises a compound represented by the Formula 1, a compound represented by the Formula 2 and/or a compound represented by the Formula 3 as defined herein. The thermoplastic resin composition can have good properties in terms of impact resistance, impact resistance after ultrasonic welding, flame retardancy, heat resistance, and the like.

Abstract: An object of the present invention is to provide a golf ball having improved ball speed or aerodynamic performance on a rainy day or the like by controlling the formulation of the paint film. The present invention provides a golf ball comprising a golf ball body and a paint film covering the golf ball body, wherein a paint film surface of the golf ball has a water contact angle A1 of 70° or more and a water sliding angle B1 of less than 50°. The present invention also provides a golf ball comprising a golf ball body and a paint film covering the golf ball body, wherein when a sheet consisting of a slab formed from a composition constituting a golf ball body surface and a coating film formed by applying a paint constituting the paint film on the slab is prepared, a coating film surface of the sheet has a water contact angle A2 of 90° or more and a water sliding angle B2 of less than 52°.

Abstract: The present invention provides a polycarbonate alloy including the following components in parts by weight: 50 parts to 80 parts of a polycarbonate; 1 part to 50 parts of a crystalline polyester; 0.01 part to 4 parts of a maleic anhydride polymer; and 0.01 part to 4 parts of a metal phosphate. The polycarbonate alloy of the present invention has advantages of good alloy stability, and a continuous and uniform distribution of the crystalline polyester in the alloy.

Abstract: The use of a low molecular weight farnesene, poly(farnesene), and farnesene copolymer in a golf ball is disclosed herein. In a core, low molecular weight farnesene, poly(farnesene) or farnesene copolymer is blended with 1,4 polybutadiene or a polyalkenamer. In a mantle layer, low molecular weight farnesene, poly(farnesene), and/or farnesene copolymer can be blended with non- or partially neutralized copolymeric or terpolymeric ionomer(s). In a cover, low molecular weight farnesene, poly(farnesene), and farnesene copolymer can be blended with highly neutralized ionomer.

Abstract: A transparent static-dissipative polycarbonate (PC) resin composition includes the following components: 70-95 parts by weight of PC resin, 5-30 parts by weight of antistatic agent masterbatch and 0.5-1.5 parts by weight of a transesterification inhibitor. The antistatic agent masterbatch includes the following components by mass percentage: 40-60% of an antistatic agent, 0.5-1.6% of a transesterification accelerator, 1-3% of an assistant cross-linkinger, and the balance of PC resin. A method for preparing the transparent static-dissipative PC resin composition includes the following steps: (I) preparing the components of the transparent static-dissipative PC resin composition according to the formulation, and mixing the components evenly to obtain a premix; and (II) adding the premix into a twin-screw extruder, melting, extruding, cooling and pelletizing, to obtain a target product.

Abstract: The present application relates to a flame retardant impact-modified polycarbonate composition and shaped parts as well as articles made therefrom. The polycarbonate composition comprises the following components: an aromatic polycarbonate, a rubber-modified vinyl (co)polymer, and a flame retardant combination. The shaped article made from the polycarbonate composition according to the present invention has a good balance among heat resistance, flame retardance and impact strength.

Abstract: A thermoplastic resin composition of the present invention comprises: approximately 100 parts by weight of a polycarbonate resin; approximately 1-10 parts by weight of a first rubber-modified vinyl-based graft copolymer in which a monomer mixture comprising an aromatic vinyl-based monomer and a cyanovinyl-based monomer is graft-polymerized onto a rubbery polymer; approximately 1-10 parts by weight of a second rubber-modified vinyl-based graft copolymer in which an alkyl (meth)acrylate-based monomer is graft-polymerized onto a rubbery polymer; approximately 1-30 parts by weight of a phosphorus flame retardant; and approximately 0.1-5 parts by weight of an encapsulated fluoropolymer. The thermoplastic resin composition has excellent impact resistance, thin film flame retardancy, heat resistance, flowability and the like.

Abstract: The present invention relates to a modified polyisobutylene polymer for rubber compounding including polyisobutylene having isobutylene as a main chain, unsaturated dicarboxylic anhydride, and a silane compound, and more particularly, 20 to 80 wt % of polyisobutylene having isobutylene as a main chain, 1 to 20 wt % of unsaturated dicarboxylic anhydride, and 1 to 60 wt % of a silane compound. In particular, when the polyisobutylene polymer of the present invention is used as an additive for rubber, the dispersibility of a filler can be significantly increased and both grip performance and rolling resistance can be improved.