Abstract: The invention relates to a process for the preparation of an acid-resistant coating and calcium carbonate particles, in which process a slurry of calcium carbonate particles is mixed simultaneously with the solution of a zinc compound and a solution of a silica-containing substance at a temperature of 70.degree.-95.degree. C., the pH being maintained at 8-11.The invention also relates to calcium carbonate particles having an acid-resistant coating in accordance with the above-mentioned process.In addition, the invention relates to the use of calcium carbonate particles having a acid-resistant coating in accordance with the above-mentioned process, as an acid-resistant filler in the production of paper at pH 4.0-7.0.