Abstract: A gas injection system includes a tubular wall 3 capable of being thermally stressed and having a proximal extremity and a distal extremity 11, at the distal extremity, at least one extremity opening through which at least one gas is projected. A cooling is system located in the tubular wall including axial channels 12 which extend axially towards the distal extremity and in which a cooling fluid is circulated. Connecting channels 13 circumferentially join the axial channels to each other at the distal extremity of the tubular wall. The connecting channels, which circumferentially join the axial channels at the distal extremity of the tubular wall, have a rounded shape in the direction of the distal extremity.

Abstract: A method and apparatus for nitride capping of titanium materials via chemical vapor deposition techniques is provided. The method includes forming a titanium nitride layer upon a titanium material layer formed on a substrate. The titanium nitride layer is formed by exposing the titanium material layer to a hydrogen-rich nitrogen-containing plasma followed by exposing the titanium material layer to a nitrogen-rich nitrogen-containing plasma. The titanium nitride layer is then exposed to an argon plasma followed by exposing the titanium nitride layer to a halide soak process.

Abstract: Compositions, methods, and reactors related to hydrogen production are generally described.

Abstract: A method and system for operating a seal gas compressor utilized in a direct reduction process including: monitoring a pH level of a water stream used in the seal gas compressor, wherein the pH level of the water stream is affected by a reformer flue gas stream that comes into contact with the water stream, wherein the monitoring step is carried out one or more of upstream of the seal gas compressor and downstream of the compressor; and adjusting the pH level of the water stream to maintain the pH level of the water stream within a predetermined range based on feedback from the monitoring step. The method includes maintaining the pH level of the water stream upstream of the seal gas compressor in a range between 7.5 and 10 and maintaining the pH level of the water stream downstream of the seal gas compressor in a range between 7.8 and 9.5.

Abstract: A workpiece made from a self-passivating metal and having one or more surface regions defining a Beilby layer as a result of a previous metal shaping operation is activated for subsequent low temperature gas hardening by exposing the workpiece to the vapors produced by heating a non-polymeric N/C/H compound.

Abstract: A method of treating refractory-lined equipment includes accessing an interior of the refractory-lined equipment with an equipment repair apparatus, wherein the equipment repair apparatus includes a robotic arm and one or more end effectors coupled to an end of the robotic arm, inspecting refractory material that lines an inner wall of the refractory-lined equipment with a first end effector coupled to the end of the robotic arm, removing damaged refractory material from the inner wall with a second end effector coupled to the end of the robotic arm, removing one or more anchors from the inner wall with a third end effector coupled to the end of the robotic arm, and installing new refractory material on the inner wall with a fourth end effector coupled to the end of the robotic arm.

Abstract: The present invention relates to a nickel-based self-fluxing alloy, a glass manufacturing member, a mold, and a glass gob transporting member having an improved slipperiness against a glass gob. A nickel-based self-fluxing alloy used in a glass manufacturing member for transporting or molding glass with a viscosity of log ?=3 to 14.6, comprises: boron (B) in an amount of ranging from 0 percent to 1.5 percent by mass; hard particles; and silicon (Si). Preferably, the amount of boron (B) ranges from 0 percent to less than 1.0 percent by mass. Preferably, the hard particles contain at least one of a carbide, a nitrides, an oxide and a cermet. Preferably, the nickel-based self-fluxing alloy comprises at least one metal selected from Group 4, 5 and 6 elements in an amount of ranging from 0 percent to 30 percent by mass.

Abstract: A gas blower device for blowing gas onto a surface of a traveling strip includes a plenum in the form of a hollow box for containing gas and comprising two side surfaces, a back surface and a front surface opposite to the back surface. The front surface having a profile of convex type symmetry with respect to a mid-plane perpendicular to the plane of the strip, so that a middle ridge of the front surface is located at the smallest distance from the plane of the strip. The front surface further presenting multiple tubular nozzles protruding at the front surface and having a gas outlet orifice facing in use the traveling strip. All the outlet orifices are essentially in a plane parallel to the strip plane. The gas blower device further includes a gas intake tube for feeding the plenum with gas.

Abstract: Methods of hardening a case-nitrided metal article, methods of producing a hardened case-nitrided metal article, and hardened case-nitrided metal articles. The methods of hardening a case-nitrided metal article include heating the case-nitrided metal article to an aging temperature, maintaining the case-nitrided metal article at the aging temperature for an aging time, and cooling the case-nitrided metal article from the aging temperature. The methods of producing a hardened case-nitrided metal article include case-nitriding a metal article to produce a case-nitrided metal article and subsequently hardening the case-nitrided metal article. The hardened case-nitrided metal article comprises a body formed of a metal or a metal alloy, a surface surrounding the body, and a nitrided case layer formed in the body and extending inwardly from the surface of the body toward the core that includes a hardness that is greater than that of an otherwise equivalent case-nitrided metal article.

Abstract: The present disclosure provides an aluminum alloy to be used in laminate molding containing Si, Fe, Mn and inevitable impurities, in which ?-phase Al—Si—Fe intermetallic compound is present in the aluminum alloy. In addition, a manufacturing method of a laminated molding is provided which laminate molds using powder of this aluminum alloy. Further, a laminate molding of this aluminum alloy is provided.

Abstract: In various embodiments, a metal alloy resistant to aqueous corrosion consists essentially of or consists of niobium with additions of tungsten, molybdenum, and one or both of ruthenium and palladium.

Abstract: The disclosure relates to a method for producing feedstock in piece form from metal, in particular aluminium and/or aluminium alloys, for a metal-casting installation, in particular aluminium-casting installation, in which scrap parts of metal, in particular of aluminium and/or aluminium alloys, are sorted on the basis of their alloying constituents and/or alloy contents and subsequently, on the basis of an alloy to be produced in the feedstock, the scrap parts are mixed into a composition having a homogeneous distribution of the alloy and fed to a press, in which the scrap parts of the composition are subjected to a pressure that compresses the scrap parts while generating a temperature, wherein, as a result of the application of pressure, the scrap parts are heated up to the transition temperature between solid and liquid of at least some of the scrap parts and/or the alloys and/or alloying constituents thereof before the feedstock is discharged in a specific geometrical form.

Abstract: A method of refining a microstructure of a titanium material can include providing a solid titanium material at a temperature below about 400° C. The titanium material can be heated under a hydrogen-containing atmosphere to a hydrogen charging temperature that is above a ? transus temperature of the titanium material and below a melting temperature of the titanium material, and held at this temperature for a time sufficient to convert the titanium material to a substantially homogeneous ? phase. The titanium material can be cooled under the hydrogen-containing atmosphere to a phase transformation temperature below the ? transus temperature and above about 400° C., and held for a time to produce ? phase regions. The titanium material can also be held under a substantially hydrogen-free atmosphere or vacuum at a dehydrogenation temperature below the ? transus temperature and above the ? phase decomposition temperature to remove hydrogen from the titanium material.

Abstract: A manufacturing method of an aluminum alloy with high thermal conductivity comprising steps of: preparing materials including pure aluminum ingots, silicon alloy, iron alloy and magnesium alloy; melting the pure aluminum ingots in a reverberatory furnace at two stages, melting, stirring, sampling for compositions determination; transferring the molten aluminum into a holding furnace, putting the ingots in, melting, removing slag, determining the compositions; calculating amount of the alloys to be added; melting the silicon alloy and iron alloy in the molten aluminum and analyzing the compositions; adding the ingots to cool the temperature of the molten aluminum down and then adding the magnesium alloy, confirming and making corrections if insufficient compositions; degassing and purifying the molten aluminum by adding drossing flux in the furnace and making a final compositions determination; transferring the molten aluminum into online degassing system to degas and purify; casting the molten aluminum into a

Abstract: An enhanced aluminum alloy galvanically compatible with a magnesium alloy component is disclosed. The aluminum alloy comprises aluminum, less than 0.2 weight percent copper, less than 0.2 weight percent iron, 6.0 to 9.0 weight percent silicon, 0.6 to 1.5 weight percent magnesium, and greater than 0.8 weight percent manganese. The aluminum alloy further comprises less than 2 weight percent zinc, less than 0.1 weight percent nickel, less than 0.2 weight percent tin, less than 0.05 weight percent titanium; and 0.008 to 0.02 weight percent strontium. Manganese and iron have a weight ratio of at least 30:1. Furthermore, iron and manganese combined content is less than 2.0 weight percent.

Abstract: The present invention relates to a furnace device for heating a plate, in particular a metal plate, by convection. The furnace device has a housing, in which a temperature control region for temperature-controlling a component part and an adjustment region are formed, wherein the adjustment region has a temperature control device for adjusting a temperature of a temperature control fluid. Further, the furnace device has a positioning device for positioning the plate in the temperature control region in a predetermined orientation, and a ventilator, which is arranged in the housing and which is adapted to circulate the temperature control fluid in the housing between the temperature control region and the adjustment region such that the temperature control fluid is flowable in a flow direction along a surface of the plate.

Abstract: A nickel-cobalt material and component includes a thermally stabilized nickel-cobalt alloy. The nickel-cobalt alloy disclosed herein includes nanocrystalline grain structures, pinning, such as Zener pinning, and intragranular twinning. The nickel-cobalt alloy disclosed herein exhibits multiple properties including an improved fracture toughness, an increased thermal stability, and an improved ultimate tensile strength.

Abstract: A method of colorizing stainless steel strip involves the continuous surface treatment of stainless steel strip with aqueous suspensions of rare earth oxide nano or micro particles or aqueous rare earth nitrate solutions of nano or micro particles. The surface treatment can be applied by roll coating, spraying or other conventional application techniques. The coated strip is then continuously annealed. The surface treatment can provide a variety of colors. It also improves corrosion resistance of the processed stainless steel strip. Steel strip treated in this manner is suitable for a variety of applications in the building systems, automotive and appliance markets.

Abstract: A high-performance metal alloy is disclosed being suitable for additive manufacturing of machine components, in particular machine components which are subjected to high gas temperature stress. Exemplary machine components are statoric components of gas turbines, such as nozzles.

Abstract: The present invention relates to a continuous furnace system for heat treating a metal component, in particular an aluminium strip. The continuous furnace system has a first heating unit, in which the metal component is heatable for solution annealing up to a first temperature in the range of from 350° C. to 700° C., a cooling unit, in which the metal component is coolable from 300° C. to 750° C. down to 70° C. to 250° C., and a second heating unit, in which the metal component is heatable up to from 150° C. to 290° C. The first heating unit, the cooling unit, and the second heating unit both have a common support structure, on which the first heating unit, the cooling unit, and the second heating unit are fixed together.