Abstract: Red rust staining of Al/Zn coated steel strip in “acid rain” or “polluted” environments can be minimised by forming the coating as an Al—Zn—Si—Mg alloy coating with an OT:SDAS ratio greater than a value of 0.5:1, where OT is the overlay thickness on a surface of the strip and SDAS is the measure of the secondary dendrite arm spacing for the Al-rich alpha phase dendrites in the coating. Red rust staining in “acid rain” or “polluted” environments and corrosion at cut edges in marine environments can be minimised in Al—Zn—Si—Mg alloy coatings on steel strip by selection of the composition (principally Mg and Si) and solidification control (principally by cooling rate) and forming Mg2Si phase particles of a particular morphology in interdendritic channels.

Abstract: Red rust staining of Al/Zn coated steel strip in “acid rain” or “polluted” environments can be minimised by forming the coating as an Al—Zn—Si—Mg alloy coating with an OT:SDAS ratio greater than a value of 0.5:1, where OT is the overlay thickness on a surface of the strip and SDAS is the measure of the secondary dendrite arm spacing for the Al-rich alpha phase dendrites in the coating. Red rust staining in “acid rain” or “polluted” environments and corrosion at cut edges in marine environments can be minimised in Al—Zn—Si—Mg alloy coatings on steel strip by selection of the composition (principally Mg and Si) and solidification control (principally by cooling rate) and forming Mg2Si phase particles of a particular morphology in interdendritic channels.

Abstract: A method of forming a coating of a metal alloy on a steel strip to form a metal alloy coated steel strip is disclosed. The method includes a hot dip coating step of dipping steel strip into a bath of molten metal alloy and forming a metal alloy coating on exposed surfaces of the steel strip. A native oxide layer as defined herein forming on the metal alloy coating of the metal alloy coated strip emerging from the metal coating bath. The method includes controlling the method downstream of the hot dip coating step and/or selecting the metal coating composition to maintain the native oxide layer at least substantially intact on the metal alloy coating during the downstream steps.

Abstract: A method of forming a coating of an Al—Zn—Si—Mg alloy on a steel strip to form an Al—Zn—Mg—Si coated steel strip is disclosed. The method includes the steps of dipping steel strip into a bath of molten Al—Zn—Si—Mg alloy and forming a coating of the alloy on exposed surfaces of the steel strip and cooling the coated strip with cooling water. The cooling step includes controlling the pH of cooling water to be in a range of pH 5-9. Particular embodiments focus on Al—Zn—Si—Mg alloys that contain the following elements in % by weight: Zn: 2 to 19, Si: 0.01 to 2, Mg: 1 to 10, and Balance Al and unavoidable impurities.

Abstract: A steel strip that has a coating of an Al—Zn—Si alloy that contains 0.3-10 wt. % Mg and 0.005-0.2 wt. % V.

Abstract: Red rust staining of Al/Zn coated steel strip in “acid rain” or “polluted” environments can be minimised by forming the coating as an Al—Zn—Si—Mg alloy coating with an OT:SDAS ratio greater than a value of 0.5:1, where OT is the overlay thickness on a surface of the strip and SDAS is the measure of the secondary dendrite arm spacing for the Al-rich alpha phase dendrites in the coating. Red rust staining in “acid rain” or “polluted” environments and corrosion at cut edges in marine environments can be minimised in Al—Zn—Si—Mg alloy coatings on steel strip by selection of the composition (principally Mg and Si) and solidification control (principally by cooling rate) and forming Mg2Si phase particles of a particular morphology in interdendritic channels.

Abstract: A method of forming a coating of an Al—Zn—Si—Mg alloy on a steel strip to form an Al—Zn—Mg—Si coated steel strip is disclosed. The method includes the steps of dipping steel strip into a bath of molten Al—Zn—Si—Mg alloy and forming a coating of the alloy on exposed surfaces of the steel strip and cooling the coated strip with cooling water. The cooling step includes controlling the p H of cooling water to be in a range of pH 5-9. Particular embodiments focus on Al—Zn—Si—Mg alloys that contain the following elements in % by weight: Zn: 2 to 19, Si: 0.01 to 2, Mg: 1 to 10, and Balance Al and unavoidable impurities.

Abstract: Red rust staining of Al/Zn coated steel strip in “acid rain” or “polluted” environments can be minimised by forming the coating as an Al—Zn—Si—Mg alloy coating with an OT:SDAS ratio greater than a value of 0.5:1, where OT is the overlay thickness on a surface of the strip and SDAS is the measure of the secondary dendrite arm spacing for the Al-rich alpha phase dendrites in the coating. Red rust staining in “acid rain” or “polluted” environments and corrosion at cut edges in marine environments can be minimised in Al—Zn—Si—Mg alloy coatings on steel strip by selection of the composition (principally Mg and Si) and solidification control (principally by cooling rate) and forming Mg2Si phase particles of a particular morphology in interdendritic channels.

Abstract: A steel strip that has a coating of an Al—Zn—Si alloy that contains 0.3-10 wt. % Mg and 0.005-0.2 wt. % V.

Abstract: Red rust staining of Al/Zn coated steel strip in “acid rain” or “polluted” environments can be minimised by forming the coating as an Al—Zn—Si—Mg alloy coating with an OT:SDAS ratio greater than a value of 0.5:1, where OT is the overlay thickness on a surface of the strip and SDAS is the measure of the secondary dendrite arm spacing for the Al-rich alpha phase dendrites in the coating. Red rust staining in “acid rain” or “polluted” environments and corrosion at cut edges in marine environments can be minimised in Al—Zn—Si—Mg alloy coatings on steel strip by selection of the composition (principally Mg and Si) and solidification control (principally by cooling rate) and forming Mg2Si phase particles of a particular morphology in interdendritic channels.

Abstract: A method of forming a coating of an Al—Zn—Si—Mg alloy on a steel strip to form an Al—Zn—Mg—Si coated steel strip is disclosed. The method includes the steps of dipping steel strip into a bath of molten Al—Zn—Si—Mg alloy and forming a coating of the alloy on exposed surfaces of the steel strip and cooling the coated strip with cooling water. The cooling step includes controlling the pH of cooling water to be in a range of p H 5-9. Particular embodiments focus on Al—Zn—Si—Mg alloys that contain the following elements in % by weight: Zn: 30 to 60, Si: 0.3 to 3, Mg: 0.3 to 10, and Balance Al and unavoidable impurities.

Abstract: A steel strip that has a coating of an Al—Zn—Si alloy that contains 0.3-10 wt. % Mg and 0.005-0.2 wt. % V.

Abstract: A method of forming a coating of an Al—Zn—Si—Mg alloy on a steel strip to form an Al—Zn—Mg—Si coated steel strip is disclosed. The method includes the steps of dipping steel strip into a bath of molten Al—Zn—Si—Mg alloy and forming a coating of the alloy on exposed surfaces of the steel strip and cooling the coated strip with cooling water. The cooling step includes controlling the p H of cooling water to be in a range of pH 5-9. Particular embodiments focus on Al—Zn—Si—Mg alloys that contain the following elements in % by weight: Zn: 2 to 19, Si: 0.01 to 2, Mg: 1 to 10, and Balance Al and unavoidable impurities.

Abstract: A method of forming a coating of an Al—Zn—Si—Mg alloy on a steel strip to form an Al—Zn—Mg—Si coated steel strip is disclosed. The method includes the steps of dipping steel strip into a bath of molten Al—Zn—Si—Mg alloy and forming a coating of the alloy on exposed surfaces of the steel strip and cooling the coated strip with cooling water. The cooling step includes controlling the pH of cooling water to be in a range of p H 5-9. Particular embodiments focus on Al—Zn—Si—Mg alloys that contain the following elements in % by weight: Zn: 30 to 60, Si: 0.3 to 3, Mg: 0.3 to 10, and Balance Al and unavoidable impurities.

Abstract: A method of forming a coating of a metal alloy on a steel strip to form a metal alloy coated steel strip is disclosed. The method includes a hot dip coating step of dipping steel strip into a bath of molten metal alloy and forming a metal alloy coating on exposed surfaces of the steel strip. A native oxide layer as defined herein forming on the metal alloy coating of the metal alloy coated strip emerging from the metal coating bath. The method includes controlling the method downstream of the hot dip coating step and/or selecting the metal coating composition to maintain the native oxide layer at least substantially intact on the metal alloy coating during the downstream steps.

Abstract: A method of forming a coating of an Al—Zn—Si—Mg alloy on a steel strip to form an Al—Zn—Mg—Si coated steel strip is disclosed. The method includes the steps of dipping steel strip into a bath of molten Al—Zn—Si—Mg alloy and forming a coating of the alloy on exposed surfaces of the steel strip and cooling the coated strip with cooling water. The cooling step includes controlling the pH of cooling water to be in a range of pH 5-9. Particular embodiments focus on Al—Zn—Si—Mg alloys that contain the following elements in % by weight: Zn: 2 to 19, Si: 0.01 to 2, Mg: 1 to 10, and Balance Al and unavoidable impurities.

Abstract: A method of forming a coating of a metal alloy on a steel strip to form a metal alloy coated steel strip is disclosed. The method includes a hot dip coating step of dipping steel strip into a bath of molten metal alloy and forming a metal alloy coating on exposed surfaces of the steel strip. A native oxide layer as defined herein forming on the metal alloy coating of the metal alloy coated strip emerging from the metal coating bath. The method includes controlling the method downstream of the hot dip coating step and/or selecting the metal coating composition to maintain the native oxide layer at least substantially intact on the metal alloy coating during the downstream steps.

Abstract: A method of forming a coating of an Al—Zn—Si—Mg alloy on a steel strip to form an Al—Zn—Mg—Si coated steel strip is disclosed. The method includes the steps of dipping steel strip into a bath of molten Al—Zn—Si—Mg alloy and forming a coating of the alloy on exposed surfaces of the steel strip and cooling the coated strip with cooling water. The cooling step includes controlling the pH of cooling water to be in a range of p H 5-9. Particular embodiments focus on Al—Zn—Si—Mg alloys that contain the following elements in % by weight: Zn: 30 to 60, Si: 0.3 to 3, Mg: 0.3 to 10, and Balance Al and unavoidable impurities.

Abstract: A steel strip that has a coating of an Al—Zn—Si alloy that contains 0.3-10 wt. % Mg and 0.005-0.2 wt. % V.

Abstract: Red rust staining of Al/Zn coated steel strip in “acid rain” or “polluted” environments can be minimised by forming the coating as an Al—Zn—Si—Mg alloy coating with an OT:SDAS ratio greater than a value of 0.5:1, where OT is the overlay thickness on a surface of the strip and SDAS is the measure of the secondary dendrite arm spacing for the Al-rich alpha phase dendrites in the coating. Red rust staining in “acid rain” or “polluted” environments and corrosion at cut edges in marine environments can be minimised in Al—Zn—Si—Mg alloy coatings on steel strip by selection of the composition (principally Mg and Si) and solidification control (principally by cooling rate) and forming Mg2 Si phase particles of a particular morphology in interdendritic channels.