Abstract: Disclosed are a modified barium titanate foam ceramic/thermosetting resin composite material and a preparation method therefor. An organic additive is used as an auxiliary; deionized water is used as a solvent; nanometer barium titanate is used as a ceramic raw material; and same are mixed and ground so as to form a slurry. A pre-treated polymer sponge is impregnated in the slurry for slurry coating treatment and a barium titanate foam ceramic is obtained after drying and sintering. Then, through dopamine modification, micrometer/nanometer silver is in-situ deposited on a skeleton surface. A resin, which is in the molten state and is thermosettable, is immersed into pores of the modified barium titanate foam ceramic, and a modified barium titanate foam ceramic/thermosetting resin composite material is obtained after a thermosetting treatment.

Abstract: The invention discloses a carbon nanotube/polyetherimide/thermosetting resin dielectric composite and a preparation method therefor. 100 parts by weight of polyetherimide and 1-7 parts by weight of carbon nanotube are mixed uniformly in an Haake torque melt cavity to obtain a carbon nanotubes/polyetherimide composite; 20 parts of the carbon nanotube/polyetherimide composite are dissolved in 100-150 parts of dichloromethane, then the mixed solution is added in 100 parts of molten thermocurable thermosetting resin, mixing, and heat preserving, stirring are performed until a mixture is formed in a uniform state, and curing and post-treating are performed to obtain a carbon nanotube/thermosetting resin dielectric composite, wherein the substrate thereof has a typical reverse phase structure, while the carbon nanotubes are dispersed in a polyetherimide phase. The composite has a relatively low percolation threshold, a high dielectric constant and a low dielectric loss.

Abstract: Barium titanate foam ceramics and a preparation method thereof are disclosed. An organic binder, an organic rheological agent and an organic dispersing agent are used as auxiliaries; deionized water is used as a solvent; nanometer barium titanate is used as a ceramic raw material; and all of same are mixed and ground so as to form a slurry with a certain solid content. A pretreated polymer sponge is impregnated into the slurry for slurry coating treatment and then dried to obtain a barium titanatefoam ceramic blank with an ideal slurry coating and without blocking holes, and same is then sintered so as to obtain a barium titanate foam ceramic. The foam ceramic has a three-dimensional network skeleton structure, and the skeleton of the foam ceramic is composed of pure barium titanate ceramic of a single chemical composition.

Abstract: A method of preparing an organotin containing hyperbranched polysiloxane structure includes the following steps: (1) by weight, 0.5-1.5 portions of hyperbranched polysiloxane with reactive functional groups is dissolved in 50-100 portions of an alcohol solvent, to obtain a solution A; (2) by weight, 0.5-0.9 portions of a tin-based initiator and 50-100 portions of the alcohol solvent are mixed to obtain a solution B, wherein said tin-based initiator is selected from dihydroxy butyl tin chloride, butyl tin trichloride, and dibutyl tin dichloride; and (3) dropping the solution B into the solution A at the temperature of 0° C.-60° C., reacting for 3-6 h, filtering and drying to obtain the organotin containing hyperbranched polysiloxane structure.

Abstract: The invention discloses a carbon nanotube/polyetherimide/thermosetting resin dielectric composite and a preparation method therefor. 100 parts by weight of polyetherimide and 1-7 parts by weight of carbon nanotube are mixed uniformly in an Haake torque melt cavity to obtain a carbon nanotubes/polyetherimide composite; 20 parts of the carbon nanotube/polyetherimide composite are dissolved in 100-150 parts of dichloromethane, then the mixed solution is added in 100 parts of molten thermocurable thermosetting resin, mixing, and heat preserving, stirring are performed until a mixture is formed in a uniform state, and curing and post-treating are performed to obtain a carbon nanotube/thermosetting resin dielectric composite, wherein the substrate thereof has a typical reverse phase structure, while the carbon nanotubes are dispersed in a polyetherimide phase. The composite has a relatively low percolation threshold, a high dielectric constant and a low dielectric loss.

Abstract: A method of preparing an organotin containing hyperbranched polysiloxane structure includes the following steps: (1) by weight, 0.5-1.5 portions of hyperbranched polysiloxane with reactive functional groups is dissolved in 50-100 portions of an alcohol solvent, to obtain a solution A; (2) by weight, 0.5-0.9 portions of a tin-based initiator and 50-100 portions of the alcohol solvent are mixed to obtain a solution B, wherein said tin-based initiator is selected from dihydroxy butyl tin chloride, butyl tin trichloride, and dibutyl tin dichloride; and (3) dropping the solution B into the solution A at the temperature of 0° C.-60° C., reacting for 3-6 h, filtering and drying to obtain the organotin containing hyperbranched polysiloxane structure.