Abstract: The polyester resin of the present invention is a polyester resin obtained by using polyethylene terephthalate, a polyvalent carboxylic acid component, and a polyhydric alcohol component, wherein the polyester resin comprises 1 molar part or more in total of at least one type of structural unit selected from the group consisting of a structural unit derived from a tri- or higher valent carboxylic acid and a structural unit derived from a tri- or higher hydric alcohol, with respect to 100 molar parts of structural units derived from an acid component, and wherein a heat absorption is 0.1 to 10 J/g as measured with respect to the polyester resin heat-treated at 150° C. for 30 minutes.

Abstract: There are provided a polyester resin for toner which has a sufficiently low TVOC, can be produced with high productivity, and can produce toner having excellent durability; and toner containing the polyester resin for toner. The polyester resin for toner has a TVOC of 380 ppm or less and includes a component derived from ethylene glycol, a hydrocarbon group having 12 carbon atoms or more, and a titanium element.

Abstract: The invention relates to a polyester resin for toner to be used in the development of an electrostatic image or magnetic latent image in electrophotography, electrostatic recording, electrostatic printing, or the like, a method for producing a polyester resin for toner, and a toner, and an object of the invention is to provide, with excellent productivity and stability, a polyester resin for toner having excellent storage stability, hot offset resistance, and low temperature fixing property as toner while still considering the environmental protection and safety. A polyester resin for toner contains 40 mol % or more and 60 mol % or less of structural units derived from tri- or higher hydric carboxylic acids based on 100 mol % of structural units derived from all acid components, and has a metal content of 100 ppm or less.

Abstract: There are provided a polyester resin for toner which has a sufficiently low TVOC, can be produced with high productivity, and can produce toner having excellent durability; and toner containing the polyester resin for toner. The polyester resin for toner has a TVOC of 380 ppm or less and includes a component derived from ethylene glycol, a hydrocarbon group having 12 carbon atoms or more, and a titanium element.

Abstract: The present invention relates to a polyester resin with excellent solubility in generic solvents, especially with excellent solubility at a temperature of 0° C. or lower. According to the present invention, by using the polyester resin with excellent solubility in generic solvents, solubility at a lower temperature, especially the solubility at a temperature of 0° C. or lower, is enhanced, making it easier to prepare paints, coatings and the like. The polyester resin related to the present invention contains 0.05 to 0.5 mol of an isosorbide-derived structural unit and 0.015 to 0.4 mol of a trihydric or higher alcohol-derived structural unit relative to 1 mol of a polycarboxylic acid-derived structural unit.

Abstract: The invention relates to a polyester resin for toner to be used in the development of an electrostatic image or magnetic latent image in electrophotography, electrostatic recording, electrostatic printing, or the like, a method for producing a polyester resin for toner, and a toner, and an object of the invention is to provide, with excellent productivity and stability, a polyester resin for toner having excellent storage stability, hot offset resistance, and low temperature fixing property as toner while still considering the environmental protection and safety. A polyester resin for toner contains 40 mol % or more and 60 mol % or less of structural units derived from tri- or higher hydric carboxylic acids based on 100 mol % of structural units derived from all acid components, and has a metal content of 100 ppm or less.

Abstract: To provide a crosslinked polyester resin by using environmentally friendly and low-cost raw materials while reducing the content of a bisphenol A-derived component. [Subject Matter] [Solutions] To provide a polyester resin containing a trivalent or higher acid-derived component and a bisphenol A-alkylene oxide adduct-derived component. In such a polyester resin, the bisphenol A-alkylene oxide adduct-derived component is contained at 0.01˜0.35 mol relative to 1 mol of all the acid-derived components, and the ratio of acid value (mg KOH/g) to hydroxyl value (mg KOH/g) is set to be 1:3˜1:26.

Abstract: To provide a crosslinked polyester resin by using environmentally friendly and low-cost raw materials while reducing the content of a bisphenol A-derived component. [Subject Matter] [Solutions] To provide a polyester resin containing a trivalent or higher acid-derived component and a bisphenol A-alkylene oxide adduct-derived component. In such a polyester resin, the bisphenol A-alkylene oxide adduct-derived component is contained at 0.01˜0.35 mol relative to 1 mol of all the acid-derived components, and the ratio of acid value (mg KOH/g) to hydroxyl value (mg KOH/g) is set to be 1:3˜1:26.

Abstract: The present invention relates to a polyester resin with excellent solubility in generic solvents, especially with excellent solubility at a temperature of 0° C. or lower. According to the present invention, by using the polyester resin with excellent solubility in generic solvents, solubility at a lower temperature, especially the solubility at a temperature of 0° C. or lower, is enhanced, making it easier to prepare paints, coatings and the like. The polyester resin related to the present invention contains 0.05 to 0.5 mol of an isosorbide-derived structural unit and 0.015 to 0.4 mol of a trihydric or higher alcohol-derived structural unit relative to 1 mol of a polycarboxylic acid-derived structural unit.