Abstract: A steel wire rod for a spring includes: C: 0.2 to 1.2%, Si: 1.0 to 3%, Mn: 0.1 to 2%, Cr: 3% or less (not inclusive of 0%), Al: 0.0002 to 0.005%, Ca: 0.0002 to 0.002%, Ti: 0.0003 to 0.010%, and balance: iron and unavoidable impurities. An average composition of oxide-based inclusions having a minor axis of 1 ?m or more which are present in a cross section satisfies CaO: 35% or less, Al2O3: 40% or less, SiO2: 30 to 95%, MgO: 8% or less, MnO: 5% or less, TiO2: 3 to 10%, and CaO+Al2O3+SiO2+MgO+MnO+TiO2?80%. The number of oxide-based inclusions having a minor axis of 2 ?m or more which are present in the cross section is more than 0.002 inclusions/mm2.

Abstract: This steel material for bearings includes prescribed components in the steel, the oxide inclusions in the steel that have a minor axis of 1 ?m or greater satisfying the following conditions (1) and (2). (1) The average composition contains specific respective amounts of CaO, Al2O3, SiO2, and TiO2, and CaO+Al2O3+SiO2+TiO2?60%. (2) The proportion of oxide inclusions in which TiN occurs at the interface of the oxide inclusions and the steel is 30% or more of the total of the oxide inclusions.

Abstract: Disclosed is a method for controlling a Ti concentration in a steel when manufacturing a silicon-deoxidized steel comprising 0.1 to 3% by mass of Si and 0.0001 to 0.005% by mass of Al by ladle refining of a molten steel, the method including the step of: adding an oxide including TiO2 to a slag in a ladle during the ladle refining, wherein the slag produced at end of the ladle refining satisfies formulas (1) to (7) below: 0.5?CaO/SiO2?1.8??(1) 4% by mass?Al2O3?20% by mass??(2) MgO?15% by mass??(3) 1.5% by mass?TiO2?10% by mass??(4) CaO+SiO2+Al2O3+MgO+TiO2?90% by mass??(5) 0.4?TiO2/MnO?5??(6) 1?TiO2/T.Fe?10??(7) where a compound represented by a chemical formula represents the content of the compound in percent by mass; and T.Fe represents the total concentration, in mass ratio, of Fe contained in Fe oxides in the slag.

Abstract: A steel wire rod for a spring includes: C: 0.2 to 1.2%, Si: 1.0 to 3%, Mn: 0.1 to 2%, Cr: 3% or less (not inclusive of 0%), Al: 0.0002 to 0.005%, Ca: 0.0002 to 0.002%, Ti: 0.0003 to 0.010%, and balance: iron and unavoidable impurities. An average composition of oxide-based inclusions having a minor axis of 1 ?m or more which are present in a cross section satisfies CaO: 35% or less, Al2O3: 40% or less, SiO2: 30 to 95%, MgO: 8% or less, MnO: 5% or less, TiO2: 3 to 10%, and CaO+Al2O3+SiO2+MgO+MnO+TiO2?80%. The number of oxide-based inclusions having a minor axis of 2 ?m or more which are present in the cross section is more than 0.002 inclusions/mm2.

Abstract: A bearing steel material which contains 0.8-1.1 mass % C, 0.15-0.8 mass % Si, 0.1-1.0 mass % Mn, 1.3-1.8 mass % Cr, up to 0.05 mass % P (0 mass % is excluded), up to 0.015 mass % S (0 mass % excluded), 0.0002-0.005 mass % Al, 0.0002-0.0020 mass % Ca, 0.0005-0.010 mass % Ti, up to 0.0080 mass % N (0 mass % is excluded), and up to 0.0025 mass % O (0 mass % is excluded). The steel material contains oxide inclusions which have an average composition that comprises, in terms of mass %, 20-50% CaO, 20-50% Al2O3, 20-70% SiO2, and 3-10% TiO2.

Abstract: A bearing steel material which contains 0.8-1.1 mass % C, 0.15-0.8 mass % Si, 0.1-1.0 mass % Mn, 1.3-1.8 mass % Cr, up to 0.05 mass % P (0 mass % is excluded), up to 0.015 mass % S (0 mass % excluded), 0.0002-0.005 mass % Al, 0.0002-0.0020 mass % Ca, 0.0005-0.010 mass % Ti, up to 0.0080 mass % N (0 mass % is excluded), and up to 0.0025 mass % O (0 mass % is excluded). The steel material contains oxide inclusions which have an average composition that comprises, in terms of mass %, 20-50% CaO, 20-50% Al2O3, 20-70% SiO2, and 3-10% TiO2.

Abstract: A bearing steel material which contains 0.8-1.1 mass % C, 0.15-0.8 mass % Si, 0.1-1.0 mass % Mn, 1.3-1.8 mass % Cr, up to 0.05 mass % P (0 mass % is excluded), up to 0.015 mass % S (0 mass % excluded), 0.0002-0.005 mass % Al, 0.0002-0.0020 mass % Ca, 0.0005-0.010 mass % Ti, up to 0.0080 mass % N (0 mass % is excluded), and up to 0.0025 mass % O (0 mass % is excluded). The steel material contains oxide inclusions which have an average composition that comprises, in terms of mass %, 20-50% CaO, 20-50% Al2O3, 20-70% SiO2, and 3-10% TiO2.