Abstract: A base steel sheet has a hot-dip galvanized layer formed on a surface thereof, in which, in a steel sheet structure in a range of ? thickness to ? thickness centered around ¼ thickness of a sheet thickness from a surface, a volume fraction of a retained austenite phase is 5% or less, and a total volume fraction of phases of bainite, bainitic ferrite, fresh martensite, and tempered martensite is 40% or more, an average effective crystal grain diameter is 5.0 ?m or less, a maximum effective crystal grain diameter is 20 ?m or less, and a decarburized layer with a thickness of 0.01 ?m to 10.0 ?m is formed on a surface layer portion, in which a density of oxides dispersed in the decarburized layer is 1.0×1012 to 1.0×1016 oxides/m2, and an average grain diameter of the oxides is 500 nm or less.

Abstract: The present invention provides a high-strength galvanized steel sheet with maximum tensile strength of 900 MPa or more. The high-strength galvanized steel sheet has an alloyed galvanized layer formed on a surface of a base steel sheet containing predetermined amounts of C, Si, Mn, P, S, Al, N, O with a balance being constituted of iron and inevitable impurities, in which in a structure of the base steel sheet, retained austenite is limited to 8% or less in volume fraction, kurtosis K* of the hardness distribution between 2% hardness and 98% hardness is ?0.30 or less, a ratio between Vickers hardness of surface layer of the base steel sheet and Vickers hardness of ¼ thickness of the base steel sheet is 0.35 to 0.70, and a content of iron in the alloyed galvanized layer is 8 to 12% in mass %.

Abstract: [Summary] The present invention provides a high-strength steel sheet excellent in impact resistance. The high-strength steel sheet contains predetermined contents of C, Si, Mn, P, S, Al, Ti, N, and O, with the balance being iron and inevitable impurities, and has a steel sheet structure in which, in a ? thickness to ? thickness region across ¼ of a sheet thickness, 1 to 8% retained austenite is contained in volume fraction, an average aspect ratio of the retained austenite is 2.0 or less, an amount of solid-solution Mn in the retained austenite is 1.1 times an average amount of Mn or more, and TiN grains having a 0.5 ?m average grain diameter or less are contained, and a density of AlN grains with a 1 ?m grain diameter or more is 1.0 pieces/mm2 or less, wherein a maximum tensile strength is 900 MPa or more.

Abstract: Provided are: a galvannealed steel sheet, reliably and sufficiently improved in the adhesiveness of a plated layer with a base steel sheet, as a galvannealed steel sheet, prepared by using a high-strength steel sheet as a base material; and a method for producing the galvannealed steel sheet. The galvannealed steel sheet wherein a galvannealed layer is formed on a base steel sheet including a high-strength steel having predetermined component composition; the average amount of Fe in the galvannealed layer is in a range of 8.0 to 12.0%; and the absolute value ?Fe of a difference between the amount of Fe in the vicinity of an interface with the base steel sheet (the amount of Fe in the vicinity of an internal side) and the amount of Fe in the vicinity of the external surface of the plated layer (the amount of Fe in the vicinity of an external side) in the plated layer is in a range of 0.0 to 3.0%.

Abstract: High strength steel sheet which secures tensile maximum strength 900 MPa or more high strength while having excellent shapeability, which high strength steel sheet which is excellent in shapeability characterized by having a predetermined composition of ingredients, by the steel sheet structure including a ferrite phase and martensite phase, by the ratio of Cu particles incoherent with the bcc iron being 15% or more with respect to the Cu particles as a whole, by a density of Cu particles in the ferrite phase being 1.0×1018/m3 or more, and by an average particle size of Cu particles in the ferrite phase being 2.0 nm or more.

Abstract: High strength steel sheet and high strength galvanized steel sheet which are excellent in shapeability which secure a tensile maximum strength 900 MPa or more high strength while obtaining excellent ductility and stretch flangeability, which sheets have predetermined compositions of ingredients, have steel sheet structures which contain volume fraction 1 to 20% of residual austenite phases, and which have martensite transformation points of the residual austenite phases of ?60° C. or less.

Abstract: This high-strength steel sheet includes by mass percentage: 0.05 to 0.4% of C; 0.1 to 2.5% of Si; 1.0 to 3.5% of Mn; 0.001 to 0.03% of P; 0.0001 to 0.01% of S; 0.001 to 2.5% of Al; 0.0001 to 0.01% of N; 0.0001 to 0.008% of O; and a remainder composed of iron and inevitable impurities, wherein a steel sheet structure contains by volume fraction 10 to 50% of a ferrite phase, 10 to 50% of a tempered martensite phase, and a remaining hard phase, wherein a 98% hardness is 1.5 or more times as high as a 2% hardness in a range from ? to ? of a thickness of the steel sheet, wherein a kurtosis K* of the hardness distribution between the 2% hardness and the 98% hardness is ?1.2 to ?0.4, and wherein an average crystal grain size in the steel sheet structure is 10 ?m or less.

Abstract: The invention is directed to providing, for application in automobiles, construction materials, household appliances and the like, high-strength sheets excellent in formability properties such as hole expansibility and ductility, and also in fatigue resistance, characterized in comprising, in specified contents expressed in mass %, C, Si, Mn, P, S, Al, N and O and a balance of iron and unavoidable impurities, and having a steel sheet structure composed mainly of ferrite and hard structures, a crystal orientation difference between some ferrite adjacent to hard structures and the hard structures of less than 9°, and a maximum tensile strength of 540 MPa or greater.

Abstract: High strength steel plate with an ultimate tensile strength of 900 MPa or more which is excellent in hydrogen embrittlement resistance characterized in that, in the structure of the steel plate, (a) by volume fraction, ferrite is present in 10 to 50%, bainitic ferrite and/or bainite in 10 to 60%, and tempered martensite in 10 to 50%, and (b) iron-based carbides which contain Si or Si and Al in 0.1% or more are present in 4×108 (particles/mm3) or more.

Abstract: The invention is directed to providing, for application in automobiles, construction materials, household appliances and the like, high-strength sheets excellent in formability properties such as hole expansibility and ductility, and also in fatigue resistance, characterized in comprising, in specified contents expressed in mass %, C, Si, Mn, P, S, Al, N and O and a balance of iron and unavoidable impurities, and having a steel sheet structure composed mainly of ferrite and hard structures, a crystal orientation difference between some ferrite adjacent to hard structures and the hard structures of less than 9°, and a maximum tensile strength of 540 MPa or greater.

Abstract: The invention is directed to providing, for application in automobiles, construction materials, household appliances and the like, high-strength sheets excellent in formability properties such as hole expansibility and ductility, and also in fatigue resistance, characterized in comprising, in specified contents expressed in mass %, C, Si, Mn, P, S, Al, N and O and a balance of iron and unavoidable impurities, and having a steel sheet structure composed mainly of ferrite and hard structures, a crystal orientation difference between some ferrite adjacent to hard structures and the hard structures of less than 9°, and a maximum tensile strength of 540 MPa or greater.

Abstract: The present invention provides a steel for steel sheets excellent in workability and showing significantly decreased formation of surface defects, and a method of deoxidizing molten steel for the steel for steel sheets which prevents nozzle clogging during continuous-casting the molten steel. That is, the steel for steel sheets excellent in workability, comprises, based on weight, 0.0001 to 0.0030% of C, up to 0.03% of Si, 0.05 to 0.30% of Mn, up to 0.015% of P, 0.001 to 0.015% of S, up to 0.008% of Al, 0.02 to 0.08% of Ti, 0.0005 to 0.0020% of Ca, 0.0005 to 0.01% of N, optionally containing at least one of 0.001 to 0.02 wt % of Nb and 0.0001 to 0.0010 wt % of B, and the balance of Fe and unavoidable impurities.