Abstract: The present invention relates to a carbonaceous material having a pore volume determined by performing Grand Canonical Monte Carlo simulation on an adsorption-desorption isotherm of carbon dioxide of 0.05 cm3/g or more and 0.20 cm3/g or less, and a ratio of desorption amount to adsorption amount (desorption amount/adsorption amount) at a relative pressure of 0.01 in the adsorption-desorption isotherm of 1.05 or more.

Abstract: An object of the present invention is to provide a carbonaceous material suitable as an electrode material of an electrochemical device which is increased in capacity with not only suppression of an increase in irreversible capacity, but also securement of a high electrode density, as well as a method for producing the carbonaceous material The present invention relates to a carbonaceous material for an electrochemical device, having a specific surface area of 23 m2/g or less as measured according to a BET method and an aerated energy (AE) of 40 mJ or more and 210 mJ or less as measured with a powder rheometer.

Abstract: The present invention relates to a coconut shell-derived modified activated carbon having a BET specific surface area of 1400 to 2000 m2/g, a value of hydrogen content/carbon content of 0.0015 to 0.0055, and intra-skeletal oxygen of 0.9 mass % or less.

Abstract: The present invention relates to a carbonaceous material for an electrochemical device, having an average particle size D50 of 30 ?m or larger as measured by a laser scattering method, and a basic flowability energy BFE of 270 mJ to 1,100 mJ as measured using a powder flowability analyzer equipped with a measuring vessel of 50 mm in diameter and 160 mL in volume under the conditions of a blade tip speed of 100 mm/sec and a powder sample filling capacity of 120 mL and calculated by the following formula: BFE=T/(R tan ?)+F (wherein, R=48 mm, ?=5°, T represents a numerical value of the rotational torque measured by the analyzer, and F represents a numerical value of the normal stress measured by the analyzer).

Abstract: The present invention relates to a coconut shell-derived modified activated carbon having a BET specific surface area of 1400 to 2000 m2/g, a value of hydrogen content/carbon content of 0.0015 to 0.0055, and intra-skeletal oxygen of 0.9 mass % or less.