Abstract: The present invention relates to a method for producing a chemically strengthened glass substrate, the method including the following steps (A) to (C): (A) preparing a chemically strengthened glass substrate A having a main surface and an end surface; (B) obtaining a glass substrate by polishing a surface of the chemically strengthened glass substrate A; and (C) performing ion exchange by bringing the glass substrate into contact with an inorganic salt composition including 90% by mass or more of KNO3 and 1.0% by mass or more and 6.0% by mass or less of NaNO3 to obtain a chemically strengthened glass substrate C.

Abstract: The present invention relates to a chemically strengthened glass, having a slope of a K2O concentration of ?1.9%/?m or more at a depth of 1 to 3 ?m and ?0.001%/?m or less at a depth of 5 to 10 ?m, in a K2O concentration profile having an abscissa representing the depth (?m) from a surface of the glass and an ordinate representing the K2O concentration (%) by mole percentage in terms of oxides.

Abstract: The present invention relates to a method for producing a chemically strengthened glass, the method including, performing a chemical strengthening treatment including the following steps (1) to (3) to a glass having a specific composition, (1) a step of bringing the glass into contact with an inorganic salt composition including 70 mass % or more of potassium nitrate to perform ion exchange; (2) a step of bringing the glass having been ion-exchanged in step (1) into contact with an inorganic salt composition including 50 mass % or more of sodium nitrate to perform ion exchange; and (3) a step of bringing the glass having been ion-exchanged in step (2) into contact with an inorganic salt composition including 70 mass % or more of potassium nitrate to perform ion exchange.

Abstract: The present invention relates to a method for producing a chemically strengthened glass, the method including, performing a chemical strengthening treatment including the following steps (1) to (3) to a glass having a specific composition, (1) a step of bringing the glass into contact with an inorganic salt composition including 70 mass % or more of potassium nitrate to perform ion exchange; (2) a step of bringing the glass having been ion-exchanged in step (1) into contact with an inorganic salt composition including 50 mass % or more of sodium nitrate to perform ion exchange; and (3) a step of bringing the glass having been ion-exchanged in step (2) into contact with an inorganic salt composition including 70 mass % or more of potassium nitrate to perform ion exchange.

Abstract: The present invention relates to a method for producing a chemically strengthened glass, the method including, performing a chemical strengthening treatment including the following steps (1) to (3) to a glass having a specific composition, (1) a step of bringing the glass into contact with an inorganic salt composition including 70 mass % or more of potassium nitrate to perform ion exchange; (2) a step of bringing the glass having been ion-exchanged in step (1) into contact with an inorganic salt composition including 50 mass % or more of sodium nitrate to perform ion exchange; and (3) a step of bringing the glass having been ion-exchanged in step (2) into contact with an inorganic salt composition including 70 mass % or more of potassium nitrate to perform ion exchange.