Abstract: A method for producing a polylactic acid resin composition, including the following steps (1) and (2): step (1): subjecting an organic crystal nucleating agent to a wet pulverization in the presence of a carboxylic acid ester having a weight-average molecular weight of from 150 to 600 and a viscosity at 23° C. of from 1 to 500 mP·s and/or a phosphoric ester having a weight-average molecular weight of from 150 to 600 and a viscosity at 23° C. of from 1 to 500 mPa·s to give a finely pulverized organic crystal nucleating agent composition; and step (2): melt-kneading a raw material for a polylactic acid resin composition comprising the finely pulverized organic crystal nucleating agent composition obtained in the step (1) and a polylactic acid resin.

Abstract: A composite material of the invention is a mixture of cellulose microfibers having a carboxyl group content of 0.1 to 3 mmol/g and a moldable polymeric material selected from the group consisting of a biomass-derived polymer and a petroleum-derived polymer. The biomass-derived polymer is preferably polylactic acid or pulp. The cellulose microfibers are preferably present in an amount of 0.01% to 60% by mass. Another composite material of the invention is a mixture of cellulose composite microfibers and a moldable resin, the cellulose composite microfibers being obtained by adsorbing a surfactant onto cellulose microfibers having a carboxyl group content of 0.1 to 3 mmol/g.

Abstract: The invention relates to a biodegradable resin composition containing a biodegradable resin, a plasticizer and a crystal nucleus agent, the plasticizer being a compound containing two or more ester groups in the molecule thereof, wherein at least one alcohol component constituting the ester contains an alkylene oxide having 2 to 3 carbon atoms, added in the average amount of 0.

Abstract: The present invention provides the method for producing a polylactic acid resin composition, including steps (1) and (2) step (1): adding the polycarbodiimide cross-linking agent to the polylactic acid resin to cross-link the polylactic acid resin; and step (2): mixing the cross-linked polylactic acid resin prepared in the step (1) with the uncross-linked polylactic acid resin.

Abstract: The invention relates to a biodegradable resin composition containing a biodegradable resin, a plasticizer and a crystal nucleus agent, the plasticizer being a compound containing two or more ester groups in the molecule thereof, wherein at least one alcohol component constituting the ester contains an alkylene oxide having 2 to 3 carbon atoms, added in the average amount of 0.

Abstract: The invention relates to a biodegradable resin composition containing a biodegradable resin, a plasticizer and a crystal nucleus agent, the plasticizer being a compound containing two or more ester groups in the molecule thereof, wherein at least one alcohol component constituting the ester contains an alkylene oxide having 2 to 3 carbon atoms, added in the average amount of 0.

Abstract: A method of manufacturing a polylactic acid resin injection molded article, having the step (1): a step of melt-kneading a polylactic acid resin composition containing a polylactic acid resin and a specified organic crystal nucleus agent, while contacting the composition with a supercritical fluid; and step (2): a step of filling the melted product obtained in step (1) in a die to mold with injection-molding. The manufacturing method of the present invention is used as an advantageous technique as compared with the technique of achieving satisfactory moldability by the addition of plasticizer in the field, for example, which requires a polylactic acid resin molded article having high rigidity.

Abstract: A method for producing a resin composition, including the steps of melt-kneading a raw material A containing a polylactic acid resin, a crystal nucleating agent, and a plasticizer containing an ester compound formed between a polycarboxylic acid having a hydrocarbon group having 1 to 7 carbon atoms and a mono-alcohol having a hydrocarbon group having 1 to 7 carbon atoms, to prepare a polylactic acid-containing melt-kneaded mixture having a relative crystallinity of 70% or more (step A); and further melt-kneading the polylactic acid-containing melt-kneaded mixture obtained by the step A and a raw material B containing a polypropylene resin and a compatibilizing agent (step B). The resin composition obtainable by the method of the present invention can be suitably used in various industrial applications, such as daily sundries, household electric appliance parts, and automobile parts.

Abstract: A biodegradable resin composition containing a biodegradable resin and a cellulose having a crystallinity of X (%), wherein the cellulose is obtained by a step including subjecting a cellulose-containing raw material to a pulverization treatment (A), wherein the cellulose-containing raw material contains a cellulose having a crystallinity of Y (%), and has a bulk density of from 100 to 500 kg/m3, and an average particle size of from 0.01 to 1.0 mm, and contains a cellulose in an amount of 20% by weight or more of a residue component obtained by removing water from the raw material, wherein X and Y satisfy the following formulas: 50?X?Y?5 (1) and 55?Y?99 (2). The biodegradable resin composition can be suitably used for various industrial applications, such as daily sundries, household electric appliance parts, and automobile parts.

Abstract: A biodegradable resin composition containing a biodegradable resin and a cellulose having a crystallinity of less than 50%; and a biodegradable resin molded article wherein the biodegradable resin composition as defined above is molded. The biodegradable resin composition can be suitably used for various industrial applications, such as daily sundries, household electric appliance parts, and automobile parts.

Abstract: The invention relates to a biodegradable resin composition containing a biodegradable resin, a plasticizer and a crystal nucleus agent, the plasticizer being a compound containing two or more ester groups in the molecule thereof, wherein at least one alcohol component constituting the ester contains an alkylene oxide having 2 to 3 carbon atoms, added in the average amount of 0.

Abstract: The present invention provides a polylactic acid resin composition, containing a polylactic acid resin and a metal hydrate surface-treated with at least one silane coupling agent selected from an amino-silane coupling agent, a mercapto-silane coupling agent and an isocyanate-silane coupling agent, wherein the content of an alkali metal component in the metal hydrate is not more than 0.2% by mass and a polylactic acid resin molded article produced by molding the polylactic acid resin composition.

Abstract: The present invention provides the method for producing a polylactic acid resin composition, including steps (1) and (2) step (1): adding the polycarbodiimide cross-linking agent to the polylactic acid resin to cross-link the polylactic acid resin; and step (2): mixing the cross-linked polylactic acid resin prepared in the step (1) with the uncross-linked polylactic acid resin.

Abstract: The invention relates to a biodegradable resin composition containing a biodegradable resin, a plasticizer and a crystal nucleus agent, the plasticizer being a compound containing two or more ester groups in the molecule thereof, wherein at least one alcohol component constituting the ester contains an alkylene oxide having 2 to 3 carbon atoms, added in the average amount of 0.

Abstract: The invention relates to a biodegradable resin composition containing a biodegradable resin, a plasticizer and a crystal nucleus agent, the plasticizer being a compound containing two or more ester groups in the molecule thereof, wherein at least one alcohol component constituting the ester contains an alkylene oxide having 2 to 3 carbon atoms, added in the average amount of 0.

Abstract: The invention relates to a biodegradable resin composition containing a biodegradable resin, a plasticizer and a crystal nucleus agent, the plasticizer being a compound containing two or more ester groups in the molecule thereof, wherein at least one alcohol component constituting the ester contains an alkylene oxide having 2 to 3 carbon atoms, added in the average amount of 0.

Abstract: A method of manufacturing a polylactic acid resin injection molded article, having the step (1): a step of melt-kneading a polylactic acid resin composition containing a polylactic acid resin and a specified organic crystal nucleus agent, while contacting the composition with a supercritical fluid; and step (2): a step of filling the melted product obtained in step (1) in a die to mold with injection-molding. The manufacturing method of the present invention is used as an advantageous technique as compared with the technique of achieving satisfactory moldability by the addition of plasticizer in the field, for example, which requires a polylactic acid resin molded article having high rigidity.

Abstract: The invention relates to a biodegradable resin composition containing a biodegradable resin, a plasticizer and a crystal nucleus agent, the plasticizer being a compound containing two or more ester groups in the molecule thereof, wherein at least one alcohol component constituting the ester contains an alkylene oxide having 2 to 3 carbon atoms, added in the average amount of 0.

Abstract: The present invention relates to a method of producing a biodegradable resin composition, which includes step (1) of mixing a biodegradable resin, a plasticizer, and a crystal nucleating agent with one another at the melting point (Tm) of the biodegradable resin or more, wherein the crystal nucleating agent is an aliphatic compound having, in its molecule, two or more of at least one group selected from an ester group, a hydroxyl group and an amide group, and step (2) of thermally treating the resulting biodegradable resin composition at a temperature of from the glass transition temperature (Tg) to less than Tm of the composition, as well as a biodegradable resin composition, which contains a biodegradable resin, a plasticizer, and the above crystal nucleating agent, and which satisfies the following conditions: the haze thereof with a thickness of 0.5 mm after thermal treatment at 60° C. for 36 or 60 hours is 20% or less; the storage elastic modulus (E?) at a temperature of 25° C.

Abstract: An additive to a polyester base synthetic resin containing a plasticizer that contains at least one compound selected from hydroxy aliphatic monocarboxylic acid ester and carboxylic acid amide is provided. In addition, a polyester base synthetic resin composition containing a polyester-base synthetic resin, a plasticizer, and at least one compound selected from hydroxy aliphatic monocarboxylic acid ester and carboxylic acid amide are also provided. Further, a plasticizer for biodegradable resins that can impart flexibility without disturbing the transparency of the biodegradable resins is provided. A biodegradable composition contains the plasticizer.