Abstract: Described herein is a scalable, economic, energy and time efficient method for the synthesis of a crystalline uniform nanoporous oxide material by utilizing colloidal particles in solution combustion synthesis. By removing colloids from nanocomposite via chemical etching crystalline uniform porous oxide is prepared with tailored porosity. The produced oxides have high specific surface area, high pore volume, uniform pore structure and high crystallinity. Properties of the oxide can be tuned by the concentration and size of colloids added, which affects the porous structure (mesopore diameter, pore wall thickness, surface area, and pore volume). In principle, this method can be applied to synthesize different high porosity crystalline metal oxides and nanocomposites.

Abstract: A versatile, highly scalable single step method is provided for depositing a metallic Pd film from low temperature combustion of an aqueous solution. By using only palladium nitrate and glycine as precursors, water as a solvent, mirror-bright dense Pd films with high crystallinity and good adhesion can be deposited at 250° C. on different substrates without subsequent annealing. The technique can be used to form a reusable catalytic flask as illustrated by the Suzuki-Miyaura cross-coupling reaction, where the Pd film uniformly covers the inner walls of the flask and eliminates the catalyst separation step.

Abstract: Described herein is a scalable, economic, energy and time efficient method for the synthesis of a crystalline uniform nanoporous oxide material by utilizing colloidal particles in solution combustion synthesis. By removing colloids from nanocomposite via chemical etching crystalline uniform porous oxide is prepared with tailored porosity. The produced oxides have high specific surface area, high pore volume, uniform pore structure and high crystallinity. Properties of the oxide can be tuned by the concentration and size of colloids added, which affects the porous structure (mesopore diameter, pore wall thickness, surface area, and pore volume). In principle, this method can be applied to synthesize different high porosity crystalline metal oxides and nanocomposites.