Abstract: Method of manufacturing zirconium alloy tubular products containing (wt. %): niobium—0.9-1.7; iron—0.04-0.10; oxygen—0.03-0.10; silicon—less than 0.02, carbon—less than 0.02, and zirconium—as the base of the alloy. This includes an ingot melting by multiple vacuum arc remelting, mechanical processing of the ingot, heating, hot working of the ingot, subsequent mechanical processing for the production of tubular billets, heat treatment of the tubular billets, application of a protective coating and heating to a hot pressing temperature, hot pressing, removal of the protective coating, multi-stage cold radial forging, vacuum thermal treatment, multiple cold rolling runs with a total deformation degree of 50-80-% per run and a tubular coefficient of Q=1.0-2.7 with intermediate vacuum thermal treatment after each cold rolling operation, and final vacuum thermal treatment of the resulting tubular products carried out at the final size with subsequent final finishing operations.

Abstract: Method of manufacturing zirconium alloy tubular products containing (wt. %): niobium—0.9-1.7; iron—0.04-0.10; oxygen—0.03-0.10; silicon—less than 0.02, carbon—less than 0.02, and zirconium—as the base of the alloy. This includes an ingot melting by multiple vacuum arc remelting, mechanical processing of the ingot, heating, hot working of the ingot, subsequent mechanical processing for the production of tubular billets, heat treatment of the tubular billets, application of a protective coating and heating to a hot pressing temperature, hot pressing, removal of the protective coating, multi-stage cold radial forging, vacuum thermal treatment, multiple cold rolling runs with a total deformation degree of 50-80-% per run and a tubular coefficient of Q=1.0-2.7 with intermediate vacuum thermal treatment after each cold rolling operation, and final vacuum thermal treatment of the resulting tubular products carried out at the final size with subsequent final finishing operations.

Abstract: Manufacturing method for tubular products made of zirconium-based alloy includes melting an ingot by multiple vacuum arc remelting, mechanical processing of the ingot, heating, multi-stage hot forging of the ingot for production of a forged piece, subsequent mechanical processing of the forged piece for production of the a round-profile blank, manufacturing of tubular billets, their quenching and tempering, application of a protective coating, heating to a hot pressing temperature, hot pressing, removal of the protective coating, vacuum thermal treatment, multiple cold rolling steps in order to produce tubular products, with intermediate vacuum thermal treatment after each cold rolling, and a final vacuum thermal treatment being carried out at a final size with subsequent final finishing operations. The tubular products can be used as the structural components of a core in water-cooled nuclear reactors.

Abstract: Manufacturing method for zirconium alloy tubular products containing (% wt.): niobium—0.9-1.7; iron—0.10-0.20; oxygen—0.10-0.20; silicon—less than 0.02, carbon—less than 0.02, zirconium—the alloy base. The method includes melting an ingot by multiple vacuum arc remelting, mechanical processing of the ingot, heating, multi-stage hot forging for production of the forged piece, subsequent mechanical processing of the forged piece for production of tubular billets with vacuum thermal treatment, application of a protective coating, heating to a hot pressing temperature, hot pressing, removal of the protective coating, vacuum thermal treatment, multiple cold rolling steps with a total deformation degree of 58-74% per run and a tubular coefficient of Q=1.18-2.01, with intermediate vacuum thermal treatment in order to produce tubular products, and final vacuum thermal treatment being carried out at the final size with subsequent final finishing operations.