Abstract: The method is for producing porous calcium deficient hydroxyapatite granules and comprises the following steps: (a) subjecting granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH), the granules comprising interconnected pores with a minimum mean diameter of 3 microns, to a first incubation in an alkaline aqueous solution having a pH-value of less than 10 and containing PO43? ions; (b) subjecting the granules to a second incubation in an alkaline aqueous solution having a pH-value of more than 10 and optionally PO43? ions; (c) filtering and drying the obtained porous granules of calcium deficient hydroxyapatite; and wherein (d) the sum of the amounts of PO43? ions present in the first and second incubation is at least as large as the amount of SO42? ions of the granules used for step (a).

Abstract: The method is for producing porous calcium deficient hydroxyapatite granules and comprises the following steps: (a) subjecting granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH) to an incubation in an alkaline aqueous solution having a pH-value of less than 10 and containing PO43? ions; whereby the granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH) comprise interconnected pores with a minimum mean diameter of 3 microns; (b) washing with water the granules obtained after incubation of step a); (c) drying the obtained porous granules of calcium deficient hydroxyapatite; whereby (d) the amount-of PO43? ions present in the incubation of step a) is at least as large as the amount of SO42? ions of the granules used for step (a).

Abstract: The method is for producing porous calcium deficient hydroxyapatite granules and comprises the following steps: (a) subjecting granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH), the granules comprising interconnected pores with a minimum mean diameter of 3 microns, to a first incubation in an alkaline aqueous solution having a pH-value of less than 10 and containing PO43? ions; (b) subjecting the granules to a second incubation in an alkaline aqueous solution having a pH-value of more than 10 and optionally PO43? ions; (c) filtering and drying the obtained porous granules of calcium deficient hydroxyapatite; and wherein (d) the sum of the amounts of PO43? ions present in the first and second incubation is at least as large as the amount of SO42? ions of the granules used for step (a).

Abstract: The method is for producing porous calcium deficient hydroxyapatite granules and comprises the following steps: (a) subjecting granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH) to an incubation in an alkaline aqueous solution having a pH-value of less than 10 and containing PO43? ions; whereby the granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH) comprise interconnected pores with a minimum mean diameter of 3 microns; (b) washing with water the granules obtained after incubation of step a); (c) drying the obtained porous granules of calcium deficient hydroxyapatite; whereby (d) the amount-of P43? ions present in the incubation of step a) is at least as large as the amount of SO42? ions of the granules used for step (a).

Abstract: The method is for producing porous calcium deficient hydroxyapatite granules and comprises the following steps: (a) subjecting granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH) to an incubation in an alkaline aqueous solution having a pH-value of less than 10 and containing PO43? ions; whereby the granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH) comprise interconnected pores with a minimum mean diameter of 3 microns; (b) washing with water the granules obtained after incubation of step a); (c) drying the obtained porous granules of calcium deficient hydroxyapatite; whereby (d) the amount-of PO43? ions present in the incubation of step a) is at least as large as the amount of SO42? ions of the granules used for step (a).

Abstract: The method is for producing porous calcium deficient hydroxyapatite granules and comprises the following steps: (a) subjecting granules of calcium sulfate anhydrous (CSA), calcium sulfate dihydrate (CSD) or calcium sulfate hemihydrate (CSH), the granules comprising interconnected pores with a minimum mean diameter of 3 microns, to a first incubation in an alkaline aqueous solution having a pH-value of less than 10 and containing PO43? ions; (b) subjecting the granules to a second incubation in an alkaline aqueous solution having a pH-value of more than 10 and optionally PO43? ions; (c) filtering and drying the obtained porous granules of calcium deficient hydroxyapatite; and wherein (d) the sum of the amounts of PO43? ions present in the first and second incubation is at least as large as the amount of SO42? ions of the granules used for step (a).