Abstract: This invention relates to the sphere of plasma electrolyte oxide coating of aluminium alloys. The method incorporates anode-cathode oxide coating in an alkaline electrolyte at a temperature of 15-50° C., using 50-60 Hz frequency alternating current. In the initial stage of the process oxide coating is carried on for 5-90 seconds at a current density of 160-180 A/dm2, then the current density is dropped to 3-30 A/dm2 and the process is continued in a regimen of spontaneous diminution of power demand without on-line adjustment of the regimen until the set coating thickness is achieved. The alkaline electrolyte used is an aqueous solution of alkaline metal hydroxide at 1-5 g/l, an alkaline metal silicate at 2-15 g/l, an alkaline metal pyrophosphate at 2-20 g/l and peroxide compounds at 2-7 g/l (in terms of H2O2—30%).