Abstract: The invention relates to a process for determining the degree of branching of modified polymers wherein the polymers are modified in the sense that their degree of branching after polymerization was increased once more, wherein the modified polymers are treated with a polar transformation mixture comprising a compound of general formula (I) R1—S—S—R1?? (I) wherein the Mooney viscosity (ML 1+4 at 100° C.) of the polymers is determined before and after the treatment with the polar transformation mixture and the degree of branching is determined.

Abstract: Vulcanizable polymer compositions based on backbone-functionalized polydienes having the general formula (I):

Abstract: The invention relates to neodymium-catalyzed polybutadienes (NdBR) comprising >95 wt % of cis-1,4 units and <1 wt % of 1,2-vinyl content, based on the neodymium-catalyzed polybutadiene, wherein the NdBR evinces a molar mass breakdown of not less than 25%.

Abstract: The invention relates to methods for achieving a step increase in the Mooney viscosity in production of high-molecular-weight polybutadiene having >95% by weight content of cis-1,4 units and <1% by weight 1,2-vinyl content, characterized in that 1) at least one monomer selected from butadiene and/or isoprene is polymerized at temperatures of from ?20° C. to 150° C. in the presence of at least one inert, organic solvent and in the presence of at least one catalyst based on neodymium carboxylate, 2) the polymerization is then terminated by addition of protic compounds and 3) then sulphur chlorides are added to the polymer, and prior to addition these sulphur chlorides are treated with a carboxylic acid, fatty acid and/or fatty acid ester.

Abstract: The Invention relates to neodymium-catalysed polybutadienes (NdBR) comprising >95 wt % of cis-1,4 units and <1 wt % of 1,2-vinyl content, based on the neodymium-catalysed polybutadiene, wherein the NdBR evinces a molar mass breakdown of not less than 25%.

Abstract: Vulcanizable polymer compositions based on backbone-functionalized polydienes having the general formula (I):

Abstract: The invention relates to neodymium-catalysed polybutadienes (NdBR) comprising >95 wt % of cis-1,4 units and <1 wt % of 1,2-vinyl content, based on the neodymium-catalysed polybutadiene, wherein the NdBR evinces a molar mass breakdown of not less than 25%.

Abstract: The invention relates to a process for determining the degree of branching of modified polymers wherein the polymers are modified in the sense that their degree of branching after polymerization was increased once more, wherein the modified polymers are treated with a polar transformation mixture comprising a compound of general formula (I) R1—S—S—R1?? (I) wherein the Mooney viscosity (ML 1+4 at 100° C.) of the polymers is determined before and after the treatment with the polar transformation mixture and the degree of branching is determined.

Abstract: The invention relates to methods for achieving a step increase in the Mooney viscosity in production of high-molecular-weight polybutadiene having >95% by weight content of cis-1,4 units and <1% by weight 1,2-vinyl content, characterized in that 1) at least one monomer selected from butadiene and/or isoprene is polymerized at temperatures of from ?20° C. to 150° C. in the presence of at least one inert, organic solvent and in the presence of at least one catalyst based on neodymium carboxylate, 2) the polymerization is then terminated by addition of protic compounds and 3) then sulphur chlorides are added to the polymer, and prior to addition these sulphur chlorides are treated with a carboxylic acid, fatty acid and/or fatty acid ester.

Abstract: The present invention relates to water and solvent-free polymers, in particular water and solvent-free synthetic rubber products like styrene butadiene rubber products and butadiene rubber products as well as a process for the production thereof. The invention further relates to a device suitable to accomplish said process.

Abstract: The present invention relates to water and solvent-free polymers, in particular water and solvent-free synthetic rubber products like styrene butadiene rubber products and butadiene rubber products as well as a process for the production thereof. The invention further relates to a device suitable to accomplish said process.