Abstract: The present invention relates to a method for manufacturing a non-planar product in glass-ceramic. Said method comprises the following steps: (i) in a conventional furnace (3), heating a sheet of precursor glass of said glass-ceramic, so that said sheet becomes formable while avoiding its ceramming; (ii) forming said heated sheet; (iii) cooling said formed sheet (2b); (iv) ceramming said formed, cooled sheet.

Abstract: The present invention relates to a method for manufacturing a non-planar product in glass-ceramic. Said method comprises the following steps: (i) in a conventional furnace (3), heating a sheet of precursor glass of said glass-ceramic, so that said sheet becomes formable while avoiding its ceramming; (ii) forming said heated sheet; (iii) cooling said formed sheet (2b); (iv) ceramming said formed, cooled sheet.

Abstract: A method of a drawing a glass ribbon from molten glass sheet via a downdraw process by creating a temperature drop across a thickness of the molten glass flowing over forming surfaces of a forming wedge. The forming wedge includes an electrically conductive material for heating the glass above the root.

Abstract: Disclosed are mono- or multi-component glass-ceramic articles (10; 20; 30; 40; 50; 60; 70; 80; 90) having at least one weld joint (100), as well as a method of manufacturing such articles (10; 20; 30; 40; 50; 60; 70; 80; 90), which includes the implementation of at least one welding. The present invention is based upon mastery of the welding of glass-ceramic precursor glasses.

Abstract: A monocrystalline alloy with a high resistance to creep having a nickel base matrix, with a density of the order of 8.5 and having a percentage, by weight, composition as follows: Co 5 to 8%--Cr 6.5 to 10%--Mo 0.5 to 2.5%--W 5 to 9%--Ta 6 to 9%--Al 4.5 to 5.8%--Ti 1 to 2%--Nb 0 to 1.5%--C, Zr, and B each less than 100 ppm--Ni remainder to 100%. Furthermore, the summation Ta+Mo+1/2 W lies between 11.5% and 13.5% by weight, the atomic sum Ti+Al+Ta+Nb lies between 15.5% and 17%, the atomic sum Ta+Nb+Mo+1/2 W lies between 4% and 5.5%, the atomic sum Ti+Al+Ta+Nb+Mo+1/2 W lies between 17.5% and 19% and the atomic sum Ti+Al lies between 12.8% and 14.5%.